I. S. El-Mahallawi, K. Eigen-field, F. Kouta, A. Hussein, T. S. Mahmoud, R. M. Ra-gaie, A. Y. Shash and W. Abou-Al-Hassan, “Synthesis and Characterization of New Cast A356/(Al2O3)P Metal Matrix Nano-Composites,” ASME, In the proceeding of the 2nd Multifunctional Nano- composites & Nanomateri-als, International Conference & Exhibition, Cario, Janu-ary 2008.

has been cited by the following article:

• TITLE: Elevated Temperatures Tensile Characteristics of Cast A356/Al2O3 Nanocomposites Fabricated Using a Combination of Rheocasting and Squeeze Casting Techniques

  AUTHORS: El-Sayed Youssef El-Kady, Tamer Samir Mahmoud, Mohamed Abdel-Aziz Sayed

  KEYWORDS: Nanocomposites, Mechanical Properties, Rhecocasting, Squeeze Casting, Aluminum Alloys

  JOURNAL NAME: Materials Sciences and Applications, Vol.2 No.5, May 5, 2011

  ABSTRACT: In the present investigation, the tensile properties of A356/Al2O3 nanocomposites at both ambient and elevated temperatures were studied. The A356/Al2O3 nanocomposites were fabricated using a combination between the rheocasting and squeeze casting techniques. The A356 matrix alloy was reinforced with Al2O3 nanoparticulates having average sizes of 60 nm and 200 nm with different volume fractions up to 5 vol%. The results revealed that the A356/Al2O3 nanocomposites exhibited better mechanical properties than the A356 monolithic alloy. Such improvement in the mechanical properties was observed at both room and elevated temperatures up to 300°C. Increasing the volume fraction and/or reducing the size of Al2O3 nanoparticulates increase both the tensile and yield strengths of the nanocomposites.