Trifuntional Oligoetherols and Polyurethane Foams with Carbazole Ring
AUTHORS:
Renata Lubczak
KEYWORDS:
Oligomers; Ring-Opening Polymerization; Polyurethanes; Thermal Properties
JOURNAL NAME:
Open Journal of Organic Polymer Materials,
Vol.2 No.1,
January
29,
2012
ABSTRACT: The method of synthesis of trifuntional oligoetherols with carbazole ring from 9-(2,3-epoxypropyl)carbazole and die- thanolamine and oxiranes like ethylene and propylene oxide was presented. Structure and some physicochemical prope- rties of the products were described. The oligoetherols were demonstrated as good substrates for synthesis of polyure- thane foams of enhanced thermal resistance. It has been found that the obtained foams are rigid at room temperature and their apparent density was 34 kg/m3- 44 kg/m3. The water uptake was low, maximum to 10.5 mass%. Dynamic thermal analysis of this foams showed that 5% mass loss starts at 200?C - 220?C, while temperature of 50% mass loss was 340?C - 370?C. Concomitantly the increase of compression strength was observed.
Related Articles:
-
Elseddik Abdelkader, Steven W. Buckner
-
Boaz Galdino de Oliveira, Regiane Araújo
-
Casimir Komenan
-
E. A. Salakhova, D. B. Tagiyev, K. F. Ibrahimova, P. E. Kalantarova
-
Maha S. M. Shehata