Y.-Y. Liang , L. H. Lin and X.-G. Zhang, “Solid State Synthesis of Hydrous Ruthenium Oxide for Supercapacitors,” Journal of Power Sources, Vol. 173, No. 1, 2007, pp. 599-605. doi:10.1016/j.jpowsour.2007.08.010

has been cited by the following article:

• TITLE: Poorly Crystalline Ru0.4Sn0.6O2 Nanocomposites Coated on Ti Substrate with High Pseudocapacitance for Electrochemical Supercapacitors

  AUTHORS: Yanqun Shao, Zhonghua Yi, Fenghua Lu, Fenyong Deng, Beibei Li

  KEYWORDS: Specific Capacitance; Supercapacitor; RuO2-SnO2; Electrode; Thermal Decomposition

  JOURNAL NAME: Advances in Chemical Engineering and Science, Vol.2 No.1, December 31, 2011

  ABSTRACT: Poorly crystalline Ru0.4Sn0.6O2 solid solution with size about 2 nm coated on Ti substrate was prepared by thermal decomposition at 260°C. The electrodes were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) for structural and morphological studies. The Capacitance properties of the electrodes were tested by cyclic voltammetry and charge-discharge tests. The results show that the electrodes have mud-cracks structure with cracks 0.2 μm in width. The electrode has stable electrochemical capacitor properties with a maximum specific capacitance of 648 F/g within a scan potential window –0.1 - 1.0 V in 0.5 M H2SO4 electrolyte solution.