• TITLE: Study of the Conversion of Postconsumer Polystyrene on CeO2/HZSM-5 Type Materials

  AUTHORS: Mirna Oliveira Sant’Ana, Anne Michelle Garrido Pedrosa, Marcelo José Barros de Souza

  KEYWORDS: HZSM-5 Zeolite, Cerium Oxide, Polystyrene, Pyrolysis

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.12 No.4, April 19, 2024

  ABSTRACT: The catalytic conversion of polystyrene (PS) was studied in the presence of the materials type HZSM-5, CeO2, 10% CeO2/HZSM-5 and 20% CeO2/HZSM-5, which were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and nitrogen adsorption at 77K. The catalytic tests were performed via thermogravimetric analysis (TG) at heating rates of 5, 10 and 20˚C min−1 in a temperature range from 30˚C to 900˚C. For the tests, a ratio of 30% by mass of each catalytic material mixed with PS was used and the activation energy of the degradation process was determined by the Vyazovkin method. The obtained results showed that the addition of the catalyst to the PS in general reduced its degradation temperature. The 10% CeO2/HZSM-5 catalyst showed greater efficiency, as it resulted in lower activation energy for PS degradation. Thus, the combination of CeO2 with HZSM-5 resulted in materials with potential for application in the catalytic degradation of polystyrene and the results indicate that the production of a composite material can be a good strategy to generate an increase in catalytic activity and a decrease in energy process activation.