Y.-F. Lin, H.-W. Chang, S.-Y. Lu and C. W. Liu, “Preparation, Characterization, and Electrophysical Properties of Nanostructured BiPO4 and Bi2Se3 Derived from a Structurally Characterized, Single-Source Precursor Bi[Se2P(OiPr)2]3,” Journal of Physical Chemistry C, Vol. 111, 2007, p. 18538.

has been cited by the following article:

• TITLE: Temperature Dependence of Current-Voltage Characteristics in Individual Sb2Se3 Nanowire

  AUTHORS: Kien-Wen Sun, Ting-Yuan Fan

  KEYWORDS: Nanowire, Dielectrophoresis, E-Beam Lithography

  JOURNAL NAME: Materials Sciences and Applications, Vol.1 No.1, April 28, 2010

  ABSTRACT: We demonstrated techniques toward nanoscale thermometries by using a hydrothermally prepared single Sb2Se3 nanowire. Suitable electrodes were fabricated to make electrical contact with a nanowire on a silicon substrate by combining techniques of dielectrophoresis, electron beam (e-beam) lithography, and focused ion beam (FIB). Measurements of temperature-dependent electrical resistivity were carried out from room temperature up to 525 K. The current-voltage characteristics showed linear and symmetric behavior through the entire temperature range, which indicated that the contacts are ohmic. The resistance of the single Sb2Se3 nanowire decreased with increasing temperature. However, a larger thermal activation energy of ~ 4.2 eV was found near a temperature above 420 K. We speculate that the reduction of resistance at a higher temperature was due to the breakdown of grain boundary barriers.