I. S. El-Mahallawi, K. Eigenfield, F. Kouta, A. Hussein, T. S. Mahmoud, R. M. Ragaie, A. Y. Shash and W. Abou-Al-Hassan, “Synthesis and Characterization of New Cast A356/(Al2O3)P Metal Matrix Nano-Composites,” ASME, Proceeding of the 2nd Multifunctional Nanocomposites & Nanomaterials, Interna-tional Conference & Exhibition, Organized by the American University in Cairo—AUC, in Collaboration with Cairo Uni-versity, Sharm El Sheikh, Egypt, 11-13 January 2008.

has been cited by the following article:

• TITLE: On the Electrical and Thermal Conductivities of Cast A356/Al2O3 Metal Matrix Nanocomposites

  AUTHORS: El-Sayed Youssef El-Kady, Tamer Samir Mahmoud, Ali Abdel-Aziz Ali

  KEYWORDS: Nanocomposites, Thermal Conductivity, Electrical Conductivity, Aluminum Alloys

  JOURNAL NAME: Materials Sciences and Applications, Vol.2 No.9, September 20, 2011

  ABSTRACT: To assess the effect of the dispersion of Al2O3 nanoparticles into A356 Al alloy on both the electrical and thermal conductivities, A356/Al2O3 metal matrix nanocomposites (MMNCs) were fabricated using a combination of rheocasting and squeeze casting techniques. Two different sizes of Al2O3 nanoparticles were dispersed into the A356 Al alloy, typically, 60 and 200 nm with volume fractions up to 5 vol%. The effect of the nanoparticles size and volume fraction on the electrical and thermal conductivities was evaluated. The results revealed that the A356 monolithic alloy exhibited better electrical and thermal conductivities than the MMNCs. Increasing the nanoparticles size and/or the volume fraction reduces both the thermal and electrical conductivities of the MMNCs. The maximum reduction percent in the thermal and electrical conductivities, according to the A356 monolithic alloy, were about 47% and 38%, respectively. Such percentages were exhibited by A356/Al2O3MMNCs containing 5 vol% of nanoparticles having 60 and 200 nm, respectively.