Veluchamy, A., Doh, C.H., Kim, D.H., Lee, J.H., Lee, D.J., Ha, K.H., Shin, H.M., Jin, B.S., Kim, H.S., Moon, S.I. and Park, C.W. (2009) Improvement of Cycle Behavior of SiO/C Anode Composite by Thermochemically Generated Li4SiO4 Inert Phase for Lithium Batteries. Journal of Power Sources, 188, 574-577.
http://dx.doi.org/10.1016/j.jpowsour.2008.11.137

has been cited by the following article:

• TITLE: Synthesis of SiOx Nano-Powders Using a Microwave Plasma Torch at Atmospheric Pressure

  AUTHORS: Dong Hun Shin, Yun Seok Choi, Dong Jin Ku, Yong Cheol Hong, Bong Ju Lee

  KEYWORDS: Silicon Oxide, Secondly Battery, Microwave Plasma Torch, Volumetric Charge Capacity, Oxidation Value

  JOURNAL NAME: Soft Nanoscience Letters, Vol.6 No.2, April 29, 2016

  ABSTRACT: The silicon oxide nano-powders (SiOx-NPs) were obtained in an atmospheric microwave plasma torch using a gas-phase silicon tetrachloride (SiCl4) with N2 and H2. The gas-phase SiCl4 was injected with H2 gas into the microwave plasma torch generated by N2 and air swirl gas, and then the dark brown powders were deposited on the inner wall of a quartz tube. The sample was analyzed by an X-ray photoelectron spectroscopy (XPS), a scanning electron microscope (SEM), an energy dispersive spectrometer (EDS), and an X-ray diffraction (XRD). The average size and oxidation x values of synthesized SiOx-NPs were approximately 230 nm and 0.91, respectively. Furthermore, the volumetric charge capacity is 1127 mAh/g and has 89.2% retention after 100 cycles.