Structural Analysis of Magnesium-Aluminium Hydrotalcites Modified with Iron III Obtained by Hydroxide Precipitation Method ()
1. Introduction
One of the most versatile adsorbent material groups is the synthetic hydrotalcite anionic clays due their wide applications as adsorbents and catalyst support materials, named Layered Double Hydroxide (LDH) [1] [2] [3] . Hydrotalcites have a structure similar to the brucite Mg(OH)2, where the Mg2+ cations are bonded to the six OH− anions, forming an octahedral arrangement. Each OH− anions, in turn, are coordinated to two Mg2+ of vicinal octahedral centers, which results in an poly-octahedral structure similar to sheet with infinite two-dimension. The sheets cannot be directly assembled on one another in order to get a three-dimensional structure because all of the sheet surfaces are positively charged due the terminal protons. Nevertheless, in aqueous media, water and mineral anions, like the carbonate, are able to form an intricate arrangement of hydrogen bonds in order to connect the sheets through the interlayer species and give rise to LDH structure [4] [5] [6] .
However, the typical hydrotalcite structures possess some of the Mg2+ cation replaced by trivalent cation, like Al3+ one, which causes a charge unbalancing among the mixed cation centers and terminal OH− groups, leading to the formation of highly positively charged sheets. Thus, to stabilize this type of hydrotalcite LDH structure, a proportional amount of interlayer anions is required to compensate the positive charge in the layer. There is a wide variety of LDH structure, because the interlayer species can be adjusted in order to compensate the amount of trivalent cations. Hence, the compositions can be controlled by the general formula
[7] [8] [9] .
The carbonated magnesium-aluminium hydrotalcite is the typical anionic clay easily prepared in the laboratory. Avery stable structure can be obtained carrying the Mg/Al ratio between 4 and 2, which means, according to the general formula, a x value of 0.2 and 0.33, respectively. The most of hydrotalcite compositions are solid solutions not well established and is very usual the same compositions present significant fluctuations in their physical properties. The most of LDH hydrotalcites possess structural memory against the dehydration process, because the cross-linked hydroxyl group and interlayer carbonate anion remains intact in dehydrated structure. On the other hand, the dehydroxylation process occurs only above 350˚C and leads to the formation of disordered structure with interstitial cations. However, depending of the hydrotalcite composition, part of the LDH structure can remain intact even the dehydroxylation process [10] [11] [12] [13] .
Extra modifications can be carried out by insertion of other trivalent cations, such as Mn(III), Cr(III), and Fe(III) in total or partial substitutions to the aluminium ones [14] - [20] . However, the changing in divalent cation site is more difficult, because the magnesium plays an important role in structural memory of LDH phases [21] [22] [23] . By considering the hydrotalcites compositions with magnesium content adjusted between 67 and 80 mol%, the structure memory becomes high and the LDH phase resists to the dehydration process and even to the dehydroxylation around 350˚C. Only when the carbonate interlayer specie starts go out in temperatures close to 500˚C, is that occurs a pronounced migration of magnesium from octahedral to tetrahedral sites, which leads to structure collapse [24] [25] [26] . The Fe3+ cation possesses lower ionic radii mismatch with Mg2+ than the Al3+ one [27] and the differences among the ionic radii are also responsible by structure strains and by the mechanism of compression-expansion process, which lead to significant changes in surface area and porosity [28] [29] [30] .
The most simple and versatile methodology to synthesize hydrotalcite powder samples is the co-precipitation method based on the addition of inorganic metallic salt solutions on the alkaline precipitant solution. Structural morphology depends on the pH of aging after precipitation. For carbonated magnesium-aluminium hydrotalcites, the pH range must set between 10 and 11 and the aging step is carried out under vigorous stirring until from 3 to 18 hours at 60˚C. It is necessary a filtration step of the aged precipitate followed by washing with distilled water until the complete soluble sodium salts and final drying at 100˚C [31] . The Fe3+ and Al3+ cations have very similar physical-chemical characteristics concerning the pH of precipitation, which makes the synthesis procedure of carbonated magnesium-aluminium-iron hydrotalcites very similar to the typical magnesium-aluminium hydrotalcites [32] .
In this work, we aim to prepare three compositions of carbonated magnesium-aluminium-iron hydrotalcites through the co-precipitation method at pH 11 in order to investigate the influence of iron (III) co-substitution on the structural and morphologic stabilities along the increasing in the temperature of thermal treatment.
2. Materials and Methods
2.1. Sample Synthesis
The hydrotalcite samples were obtained by co-precipitation method at pH 11, according to the formula
, with y set as 0, 0.05, and 0.10, which were named as HTF00, HTF05, and HTD10 sample, respectively. Firstly, it was prepared the cation aqueous solutions by dissolution of hexahydrate Mg(NO3)2∙6H2O, aluminium III nitrate nonahydrate Al(NO3)3∙9H2O, and iron III nitrate nonahydrate Fe(NO3)3∙9H2O in distilled water. The stoichiometric calculations were carried out in order to get cation molar sum (Mg2+ + Al3+ + Fe3+) equal to 1.0 mol∙L−1. In sequence, it was prepared the anion precipitant aqueous solutions by dissolution in distilled water of sodium hydroxide (NaOH) and sodium carbonate (Na2CO3).
Both solutions were slowly poured on the third flask kept under vigorous stirring at room temperature. For precipitate aging process, each precipitate suspension batch was heated at 60˚C for 6 hours under moderate stirring and finally filtered and washed with distilled water until neutral pH for supernatant solution. The washed precipitate samples were dried at 100˚C for 24 hours and slightly crushed in a porcelain mortar in order to get the powders desagglomeration. In sequence, each dried precipitate samples was divided in three parts and lead to thermal treatment at different temperatures (100˚C, 200˚C and 500˚C) for 4 hours. The thermal treatment at 100˚C for 4 hours for samples already dried at 100˚C for 24 hours aims to normalize the powder processing among all of the samples. The appearance and powder colors for all of the samples as a function of iron (III) content and of temperature of thermal treatment can be seen on Figure 1.
2.2. Characterization Techniques
Each dried precipitate samples was analyzed by simultaneous (TG/DTA) technique by using a Netszch Thermische Analyse (TASC 414/2 controller), alpha-alumina standard, Pt 10 thermocouple, synthetic air flux of 30 cm3∙min−1 and heating rate of 10˚C∙min−1. All of the thermally treated samples were lead to X-ray diffraction technique using D5005Siemens equipment, with K-alpha Cu radiation in 2-theta range from 20˚ to 80˚. All of the phases were identify by comparing the patterns with the JCPDS data bank [33] . The main functional groups and its variations were analyzed by FTIR spectrophotometer with Nexus 650 Thermo Nicoletequipped with photo-acoustic detector for solid samples. The nitrogen adsorption-desorption isotherm at 77 K was carried out using ASAP 2010 Micromeritics equipment. The pore size distribution in the mesopore-macropore range was calculated by BJH model [34] and the specific area by BET one [35] .
Figure 1. Powder colors for carbonated magnesium-aluminium hydrotalcites varying as a function of iron (III) content and of temperature of thermal treatment.
3. Results and Discussion
Thermal properties of the dry precipitates for each composition investigated by simultaneous TGA/DTA analysis are shown in Figure 2. There are three curves (TGA, DTG and DTA) for each sample, which is identified by a different color. It is possible to observe the four weight losses, which are notably changed as a function of iron content. The dehydration and dehydroxylation processes have more evidenced endothermic behavior due the narrower temperature range for these steps. However, the other two processes also endothermic behavior, but is broader due the kinetic component influence. The first weight loss starts at room temperature due the water vapor dragging by the airflow of analysis. That residual drying occurring up to 100˚C for all of the samples seems not to be dependent on the iron (III) content, but probably is a function of differences in the inter-particle morphology. The weight losses for the first process are shown in first column of the Table 1.
In sequence, the dehydration of interlayer spaces starts to occur above 100˚C and extends up to 260˚C for HTF00 sample. The final temperature of the dehy-
Figure 2. Thermal analyses (TG/DTA) for carbonated magnesium-aluminium-iron hydrotalcite precipitate samples dried at 100˚C for 24 hours.
Table 1. Weight losses and DTG peaks for the thermal events observed TG/DTG curves of carbonated magnesium-aluminium-iron hydrotalcite dried precipitates.
dration process is displaced to lower temperatures for HTF05 and HTF10 samples, as shown in DTG curves, followed by a similar changing in the maximum of weight loss (DTG peak), as shown in the second column of the Table 1. The relation between water loss and the iron content in the samples seems to be inversely proportional, which it is coherent because the calculated y values, according to the general formula
, were 0.7 for all of the samples.
The third thermal event is the layer dehydroxylation process through the water loss originated from the condensation of hydroxyl groups, which originate metallic oxide mixture in material thermally treated above that temperature range [36] [37] . In spite of the weight loss not to be noticed dependence with iron (III) content among the samples, the final temperature and the DTG peak for that process are displaced to lower temperatures, as shown in the third column of the Table 1. Theoretical value for weight loss in dehydroxylation step is between 29%, for HTF00 sample and 27%, for HTF10 one.
Thus, part of hydroxyl groups are eliminated previously at lower temperature in overlapping with the dehydration process, once the final decarbonation step is also lower than theoretical values. If was considering the theoretical calculations for carbon dioxide loss are close to 13% then a similar overlapping with dehydroxylation step is very probable. Nevertheless, the iron (III) co-substitution seems to retain more amounts of interlayer carbonate anions than no co-substituted one. The final residue is very similar to the theoretical calculations.
In Figure 3 are shown the X-ray diffraction patterns for three samples of carbonated magnesium-aluminium-iron hydrotalcites thermally treated at 100˚C, 200˚C and 500˚C for 4 hours. The peak set for all of the samples thermally treat-
(a) (b) (c)
Figure 3. X-ray diffraction patterns for carbonated magnesium-aluminium-iron hydro-talcite precipitate samples thermally treated at different temperatures for 4 hours: (a) drying at 100˚C; (b) dehydration at 200˚C; and (c) dehydroxylation at 500˚C.
ed at 100˚C and 200˚C is very similar to the R-3m rhombohedral LDH structure and matches with JCPDS card 89 - 461 [33] . Taking in account the (006) peak position at 22.8˚ (2-theta), it is possible to observe a continuous decreasing along the increasing of iron (III) content and that event occurs for low-temperature thermally treated samples (100˚C and 200˚C). No odd peak in relation to the hydrotalcite single phases was found in X-ray diffraction patterns for these samples. On the other hand, the peak intensities become higher when the temperature of thermal treatment increases from 100 (Figure 3(a)) to 200˚C (Figure 3(b)) for all of the compositions. At 500˚C (Figure 3(c)), the LDH structure undergoes partial decomposition, giving origin to some amounts of secondary periclase MgO phase (JCPDS card 45 - 946). Nevertheless, the intensity for the (006) peak is considerable higher when compared to the other samples thermally treated at 500˚C, which permits to concludes the LDH structure for HTF05 sample is more stable than the one for other samples.
These results obtained from X-ray diffraction technique seems to be satisfactorily coherent with FTIR spectrometry ones, as shown in Figure 4. The bands signaled as 1, 2, 3, 6 and 8 are originated from different energetic modes of O-H groups, while the band signaled as 5 is associated to liquid water bending and the bands signaled as 4 and 7 are related to carbon-oxygen bonds in carbon dioxide and carbonate anions. Details for different modes are available on the text inside the figures.
After the dehydration process between 100 (Figure 4(a)) and 200˚C (Figure 4(b)), it is possible to observe the proportional decreasing in the intensity of the band 3, associated to the O-H symmetric stretch of water. In addition, there is the proportional increasing in the intensity of the band 6, associated to the -OH bending vibration. These aspects means the interlayer residual species are rear
(a) (b) (c)
Figure 4. FTIR spectra for carbonated magnesium-aluminium-iron hydrotalcite precipitate samples thermally treated at different temperatures for 4 hours: (a) drying at 100˚C; (b) dehydration at 200˚C; and (c) dehydroxylation at 500˚C.
ranged during the dehydration, which lead to better ordering of LDH structure, according to X-ray diffraction data. After the dehydroxylation process at 500˚C (Figure 4(c)), all of the bands originated from different energetic modes of O-H groups undergo the proportional decreasing in their intensities. It is possible to observe the intensities of the bands 4 and 7 are also proportionally reduced, meaning the part of carbon dioxide and carbonate amounts go out during the dehydroxylation process.
That evidence is coherent with lower value for decarbonation than theoretical calculations, as previously discussed about the thermal analysis data. Besides these changes, a new band associated to the M-O-M lattice vibration mode (band 9) raises for all of the samples, but that event is more noticed for HTF00 and HTF10 samples, due more amount of secondary periclase MgO phase.
The isotherms of nitrogen adsorption-desorption at 77 K for all of the samples are shown in Figure 5. The type IV isotherm is characteristic of the natural anionic clays, which is generally associated with capillary condensation in mesopores [38] [39] [40] . The isotherms observed for the synthetic carbonated magnesium-aluminium-iron hydrotalcite samples prepared in this work seems to be very similar with the natural clay ones, mainly for high volume adsorbed at relative pressures, which is characteristic of external surface area and macropore contributions. Nevertheless, there is a considerable volume absorbed at relative pressures between 0.7 and 0.9, which is characteristic of the mesopores. No considerable volume adsorbed uptake is observed for any samples, what means the hydrotalcite samples do not have micropores or small mesopores. The dehydrated HTF00 sample presents higher volume absorbed than dried one, as can be observed by comparing the Figure 5(a) and Figure 5(b), but during the dehy-
(a) (b) (c)
Figure 5. Nitrogen adsorption-desorption isotherms at 77 K for carbonated magnesium- aluminium-iron hydrotalcite precipitate samples thermally treated at different temperatures for 4 hours: (a) drying at 100˚C; (b) dehydration at 200˚C; and (c) dehydroxylation at 500˚C.
droxylation at 500˚C, the volume adsorbed turns to decrease (Figure 5(c)). These volume adsorbed variation at high relative pressures seems to be inverse for iron (III) co-substituted samples, once the dehydration tends to decrease the volume adsorbed, while the dehydroxylation one, leads to increase of them.
The morphologic behavior observed through the nitrogen adsorption-desorption at 77 K, can be better understand on the Figure 6, which shows a strict correlation between BET specific area and volume adsorbed variations for all of the samples. At low temperatures of thermal treatment (100˚C and 200˚C), the adsorptive characteristics are better for no co-substituted sample, presenting surface area close 160 - 165 m2/g. However, at 500˚C, the iron (III) co-substi- tuted samples present also similar surface area. The dehydration process for iron (III) co-substituted samples seems to be morphological harmful, due to particle sintering during the dehydration. As consequence, the sintered powders are disrupted by the water vapor evolution at 500˚C, leading to increasing in specific area again.
In Figure 7 are observed the BJH pore size distribution in mesopore (2 to 50 nm) and macropore (>50 nm) regions. The higher incremental pore volumes are very broad for all of the samples and tend to localize in mesopore-macropore boundary (at 50 nm). For HTF00 and HTF05 samples, the incremental pore volumes does not changes during the dehydration process, as can be observed comparing the Figure 7(a) and Figure 7(b), but for the dehydroxylation process at 500˚C (Figure 7(c)), the HTF05 sample turns the more porous sample among all of the others. On the other hand, the HTF10 sample presents a continuous decreasing in incremental pore volume in the mesopore region, reaching to present practically no mesoporosity at 500˚C.
Figure 6. Evolution of BET surface area for carbonated magnesium-aluminium-iron hydrotalcite precipitate samples along the temperature of thermal treatement for 4 hours.
(a) (b) (c)
Figure 7. BJH pore size distribution patterns for carbonated magnesium-aluminium-iron hydrotalcite precipitate samples thermally treated at different temperatures for 4 hours: (a) drying at 100˚C; (b) dehydration at 200˚C; and (c) dehydroxylation at 500˚C.
These results about the porosity of thermally treated samples seem to be strongly associated with the remaining rhombohedral LDH hydrotalcite phase after the dehydroxylation at 500˚C. In fact, the X-ray diffraction patterns are very coherent with proposition. On the other hand, there is no substantial decreasing for the incremental pore volume associated to large macropores (>100 nm), what makes the HTF10 sample moderately stable only against the particle sintering during the dehydroxylation process. Thus, is very probable the periclase phase becomes more macroporous when it is resulted from the hydrotalcite co-substituted with 10 mol% of iron (III).
4. Conclusion
From obtained results, it can be concluded the carbonated magnesium-alumi- nium-iron hydrotalcite presents full inherent structural and morphological properties of anionic clay adsorbent materials, including the rhombohedral phase with satisfactory crystallinity, structural stability against the dehydration process, high surface areas, and large porosity with pore size predominant in mesopore-macropore boundary region. It was possible to observe the iron (III) co-substituted samples provide better surface area after dehydroxylation process. However, by considering the pore size distribution and the structural stability for thermally treated LDH rhombohedral phase, the insertion of 5 mol% of iron (III) seems to be the best composition. For lower temperatures of thermal treatment, the no co-substituted sample has still the best set of structural and morphological characteristics, taking in account the adsorbent applications. However, the lower temperatures for dehydration and dehydroxylation process for the samples co-substituted with 5 mol% of iron (III) can be associated to the lowering of chemisorption heats in interlayer spaces. Under the point view of reversible process, that composition can be better applicable as reusable adsorbent material due the facilities for desorption steps, so that is a good suggestion for future works.
Acknowledgements
The authors thank the Brazilian foundations FUNDECT-MS, CNPq, CAPES and FINEP for financial supports.