Determination of Some Physical and Mechanical Properties of the Wood-Based Panels Modified by Acrylic Textile Fiber ()
1. Introduction
Forest and other natural assets have been used in producing the items that are needed from time immemorial. While use of natural wood material decreased gradually, the use and production of wood-based panels increased by expanding. Wood-based panels developed in order to provide dimensional stability and to obtain large-size sheet [1] . These panels are produced for protection against moisture and vermin as supplemented with natural or synthetic substances, as are produced in the form of wood chips mixed with various ingredients (fiber cement board).
Animal wool, cotton and synthetic fibers are the basic material of textile production. The main features of these items include durability, length, flexibility, moisture absorption, resistance to heat and light, and being easily washable [2] .
Acrylic fiber is a synthetic fiber that closely resembles wool in its character [3] . According to the definition of the ISO (International Standards Organization) and BISFA (International Synthetic Fiber Standardization Office), fibers which contain a minimum of 85% acrylonitrile in their chemical structure are called “Acrylic Fibers”.
Acrylic fibers are soft and light fibers having light and warm tactile feeling to the human skin [4] . They are widely used, making the most of their characteristics, for knitted products such as sweater and jersey; bedding textiles such as blankets and Pile sheets; and carpets for home-uses. In addition, rag animals and western wigs are the products making use of acrylic fibers
Some important properties of acrylic fibers are: 1―Lighter than wool fibers, and fabric hand with bulkiness; 2―Superior in warm retention, light and warm; 3―Superior in elastic recovery, and resistant to crease; 4― Excellent in color development and can be dyed in desired color; 5―Little affected by sunlight; 6―Resistant to chemicals and cannot be attacked by molds and insects; 7―Thermoplastic [5] .
Acrylic fiber is composed of acrylonitrile and a co monomer. The co monomer is added to improve dyeability and the textile processability of the acrylic fiber. It can be used 100% alone, or in blends with other natural and synthetic fibers [6] -[8] .
Today, the cost, excellence and availability of raw materials are of principal importance. Due to environmental concerns, a very large number of companies are currently developing manufacturing processes using alternative materials for their crop and in search of new markets for the sub-products of their first-line production. Textile industry is an example of the reality that the industry is living these days. The textile industry has taken an increasing interest in developing a system for recycling waste fiber which results from the process of manufacturing product such as textile fabrics and fibers, non-woven fabrics etc. However, because of the lack of effective recycling technique, most of these wastes are currently destroyed by fire or buried underground [9] .
The results showed that laminate produced using epoxy and reinforced with carbon fiber had the highest technological properties [10] .
Bending strength and flexibility were increased on the composite material (gluelam) with glass fiber reinforced [11] .
In the experiments, heat conductivity constant was determined according to ASTM C 1113-90 Hot Wire Method standards [12] . The least conductivity of temperature was detected on MDF coated by melamine impregnated decorative paper and the most conductivity of temperature was detected on HDF covered by high pressured laminate [13] .
At the University of Minnesota and some Institutions in a Corporation “Mineral Bonded Composite Panel Research Initiatives and Projects” at the name of research done in the similar timber modification is known that [14] .
The main purpose of this study is to prepare a series of modified panels by mixing the wood chips (beech (Fagus sylvatica L.) and Scotch pine (Pinus sylvestris L.)) and acrylic fibers. These components are collected from the wood-working workshop and textile manufactories as industrial waste materials. It is planned to obtain four types of modified panel by changing the ratio of wood chips and acrylic fibers. Another aim of this study is to investigate some physical and mechanical properties of the modified panels and to compare the values with the industrially produced panels.
2. Material and Method
In this research wood based panels were produced from a mixture of wood chips and textile waste of acrylic fibers. Urea formaldehyde glue was used to hold the components together. Certain physical and mechanical properties of the panels were determined and the features were compared to the industrially produced particleboard.
2.1. Materials
2.1.1. Acrylic Fibers
Characteristics of acrylic have many appealing properties. Acrylic’s high performance makes it one of the fastest growing fibers in the outdoor, performance apparel categories. This fiber draws moisture away from the skin and quickly transports it to the surface making the wearer more comfortable. Other characteristics of acrylic include: quick drying time, excellent color fastness, UV resistance, soft hand luxurious touch & drape warmth in thermal constructions easy care bulk without extra weight resistance to weathering durability resilience shape retention stain resistance wrinkle resistance and resistance to shrinking, fading, aging, chemicals, oils, moths, mildew, and fungus. Uses of Acrylic not only have many appealing characteristics and advantages, but many apparel, home furnishings, and industrial end uses as well. This fiber accounted for 5 percent of the fiber produced in the United States in 1990 with only three companies producing it at the time [15] .
Some basic properties of acrylic fibers were presented in Table 1.
2.1.2. Coarse and Fine Wood Chips
Coarse wood chips in roughing planning machines (Moulder) and the fine wood chips in band saw machines on a separate collection system have been booked during processing application workshops beech wood and pine wood at the Gazi University Faculty of Technology Wood Products Industrial Division. Coarse and fine wood chips collected and purified from impurities in amounts necessary for each panel in Table 1 have been classified in accordance with the principles. This is classified in separate containers to air dry shavings to balance the degree of humidity (12%) were kept in the room until the air conditioning. The length of coarse chips 3 - 4 mm and a thickness of at least 1 mm ; the lengths of fine chips 1 - 2 mm, thickness as less than 0.5mm were measured.
2.2. Preparation of the Modified Panels
Four types of modified panels (Eltapan-I, Eltapan-II, Eltapan-III, Eltapan-IV) were produced by mixing acrylic waste materials and fine-coarse wood chips fiber in different proportions (Table 2).
In preparing textile fiber panels (fiber + wood panel representing the “Eltapan” has been called) joined textile fiber and wood chips mixture of 25% urea formaldehyde glue and hardener (glue resin: Kaurit and hardener: Ammonium sulphate, Germany).
Textile fibers which can be distributed homogeneously were cut in 10 mm long. Draft panels have produced from basic materials of a homogeneous mixture of obtained wood chips-glue-textile fiber. The mixture pressed 2.5 N/mm2 pressure and temperature conditions of 90˚C for 45 min (OTT brands, hot press, Germany). Basic materials content and ratios of panels in Table 2, the images of the photographs in Figure 1 and production phases in Figure 2 are given.
Table 1. Some basic properties of acrylic fibers [16] .
Table 2. The amounts (%) of the components used to prepare the panels.
Figure 1. Preparation of mixture of the panel and pressing.
The Extruded panels were conditioned at temperature of 20˚C ± 2˚C and relative humidity of 65% ± 5% for providing equilibrium moisture content of 12%.
The standard sizes for the test to be applied in pre-cut test samples in airtight plastic containers were stored until testing phase.
2.3. Test Method
Tests were applied by 4 tons capacity of Universal Testing Device at 800 kp stage according to ASTM-D143-83 [17] standards at the laboratory of Technology Faculty in Gazi University. Rate of progress of the experimental device was set to receive 2 mm distance in a minute. Maximum forces were recorded (N). In this study, applied tests are given to samples that are produced from modified panels (Eltapan I, Eltapan II, Eltapan III and Eltapan IV) and industrial chipboard obtained and application based on the standards in Table 3.
2.4. Evaluation of Data
In order to determine the effects, contents of textile fiber and wood chips mixture amounts % were performed.
3. Results
3.1. Density
The average density values of modified panels and industrial chipboard which were determined according to ASTM D1037-12 [18] and presented in Table 4.
According to Table 4, while the density of Eltapan-IV (from the modified panels) is higher than the industrial chipboard, other panels are lower.
3.2. Water Absorption and Thickness Swelling
Average values of water absorption and thickness swelling of the samples were determined according to ASTM D1037-12 [18] and presented in Figure 3.
As seen in Table 5, while swellings in water of all panels in the first 20 hours change rapidly, change in swellings percentages after from 20th hour are lesser. At the end of 55th hour, while the highest swelling is determined in ELTAP II, the lowest swelling is determined in ELTAP III.
3.3. Thermal Conductivity
The coefficient of thermal conductivity is expressed as the quantity of heat that passes through a unit cube of the substance in a given unit of time when the difference in temperature of the two faces is 1˚. Here, the heat conductivity coefficient (l) is expressed as kcal/hr·m·˚C [10] .
The average value of thermal conductivity coefficient of modified panels and industrial chipboard which were
Table 3. The experimental investigation of panel properties and their standards.
Table 4. The average density values of the modified panel and industrial chipboard.
Table 5. The average values for thermal conductivity coefficient and temperature changes of test panels.
Figure 3. Average values of thickness swelling of the panels depend on time.
determined according to the ASTM-C 1113 [12] in Table 5 were given.
As seen in Table 5, all the modified panels have a lower thermal conductivity according to the industrial chipboard.
3.4. Bending Strength
The average of bending strength of modified panels and industrial chipboard which were determined according to the ASTM D1037-12 in Table 6 were given.
As seen in Table 6, all the modified panels have a lower bending strength according to industrial chipboard.
4. Conclusions and Recommendations
All of the average values of swelling, density, thermal conductivity coefficient and bending strength of modified panels and industrial chipboard which were determined according to the ASTM D1037-12 [18] and ASTM-C 1113 [12] were given in Table 7.
The density values of modified panels and industrial chipboard were measured, the highest value (0.68 g/cm3) in industrial chipboard and (0.65 g/cm3) in ELTAP IV, and the lowest value (0.56 g/cm3) in ELTAP II was determined. Overall ranking from low to high:
Eltapan II > Eltapan I > ELTAPAN III > INDUSTRIAL PARTICLEBOARD > Eltapan IV
Eltapan-IV, the cause of the density being high in content of 50% coarse beech wood chips is taking place. Eltapan-II, the cause of the density being low in content of 50% fine wood chips (beech and pine) is taking place.
The thickness swell of the modified panels % ratios as measured. 100% of the maximum swollen thickness as well ELTAP II, 35.5% for the lowest thickness as swelling ratio was also determined ELTAP III. Overall ranking from low to high:
Eltapan III > Eltapan IV > ELTAPAN I > INDUSTRIAL PARTICLEBOARD > Eltapan II
ELTAPAN II contained in the swelling ratio of the thickness of thin beech wood chips panel said that upgrade. Micro fibrils of fine beech wood chips, the inner of the panel and therefore the water absorption of ELTAP II increase [13] .
Swelling ratios of the thickness and density in the modified panels and industrial chipboard panels are shown in the graph of Figure 4.
Thermal conductivity coefficients of the modified panels and industrial chipboard were measured. The highest thermal conductivity coefficient 0.1451 kcal/hr∙m∙˚C as well as ELTAP IV, the lowest thermal conductivity coefficient 0.1233 kcal/hr∙m∙˚C was also determined as an ELTAP II. Overall ranking from low to high:
Table 6. The average values of panels bending strength.
Table 7. All of the average values of technical specification of modified panels and industrial particleboard.
Eltapan II > Eltapan I > ELTAPAN III > Eltapan IV > INDUSTRIAL PARTICLEBOARD
The thermal conductivity coefficient (0.1233 kcal/hr∙m·˚C) of Eltapan II was low, that it comprises a low density and content of 50% fine wood chips components.
Thermal conductivity coefficients and density in the modified panels and industrial chipboard panels are shown in the graph of Figure 5.
Bending strength of the modified panels and industrial chipboard was determined. The highest bending strength 14.910 N/mm2 on the Eltapan IV (industrial chipboard: 27.7 N/mm2), while the lowest bending strength values were calculated 5.160 N/mm2 on the Eltapan III. Overall ranking from low to high:
Figure 4. Swelling ratios of the thickness and density in the modified panels and industrial chipboard panels.
Figure 5. Thermal conductivity coefficients and density in the modified panels and industrial chipboard panels.
Figure 6. Bending strength and density in the modified panels and industrial chipboard panels.
Eltapan III > Eltapan II > Eltapan I > ELTAPAN IV > INDUSTRIAL PARTICLEBOARD
Bending strength on the Eltapan IV was higher (from modified panels). The reason for this, the Eltapan IV is the content of 50% coarse beech wood chips and high density (0.65 g/cm3). Bending strength and density in the modified panels and industrial chipboard panels are shown in the graph of Figure 6.
The optimum properties of the ELTAP IV of modified panels recommended for general use. The IV ELTAP of modified panels has of maximum bending strength, in water swelling value is half of industrial chipboards and thermal conductivity is also low. Eltapan II is the most suitable for the isolation use