1. Introduction
Pure metals and alloys react chemically/electrochemically with corrosive medium to form a stable compound in which the loss of metal occurs. The compound so formed due to this loss of metal is a corrosion product commonly known as rust. Corrosion is defined as the destruction, degradation or deterioration of material due to reaction between the material and the environment [1] .
Many factors need to be considered when selecting engineering materials, but for chemical process plant the overriding consideration is usually the ability to resist corrosion [1] . Some metals and alloys are known for their resistance to corrosion but in extreme conditions, they corrode.
The chemical process plants used in textile and food processing plant make use of Al-Cu-Mg alloy where the use of mild steel would cause contamination [2] . Acid and alkalis are used for cleaning and descaling of this part of the plant. In addition to these cleaning and descaling process, these chemicals corrode the alloy thereby reducing the performance and the life span of the engineering materials.
In order to combat this constant and continuous problem, which is often difficult to eliminate completely, the use of inhibitor is one of the best options deployed for protecting metals and alloys against corrosion over the years. Considerable efforts have been made to find suitable corrosion inhibitor in various corrosive media. The known hazardous effects of most synthetic process have urged researchers to look beyond inhibitors that could not offer sustainable environment, especially in view of Cr (VI) being banned and labelled as a carcinogen. Corrosion control of metals is of technical, environmental and aesthetical importance. This has prompted the search for green inhibitor.
The adsorption of the inhibitors unto the metal/alloy surfaces retards the cathodic or anodic electrochemical processes that accompany corrosion of the metal/alloy [3] [4] . Studies have shown that the efficiency of inhibition is related to the amount of adsorbed inhibitor on the metal surface [5] . The inhibitor after adsorption may form a surface film that acts as a physical barrier restricting the diffusion of ions/molecules to or from the metal/ alloy surface and may prevent the metal atoms from participating in either the anodic or cathodic reactions of corrosion [6] [7] .
In the search for more environmentally friendly and readily available inhibitors, researchers have reported the use of local plants such as Vernonia amygdalina [8] and neem leaf [9] . The use of plant extracts as organic inhibitors for the corrosion of metals/alloys, has gained very wide interest among researchers in recent time [10] [11] .
Green corrosion inhibitors are biodegradable and do not contain heavy metals or other toxic compounds. The use of naturally occurring plant extracts as inhibitors is particularly interesting and economical because they are cheap, non-toxic, ecologically friendly and poses little or no threat to the environment [3] [12] . Therefore, while reducing corrosion rate in metals, green inhibitors take care of environmental pollution constituted by earlier suggested inhibitors. In addition to being environmentally friendly and ecologically acceptable, plant products are inexpensive, readily available and renewable. Hence, green inhibitors show real promise. Sida acuta is a species of flowering plant in the family, Malvaceae and it is a weed that frequently dominates pastures [13] . The plant is native to Mexico and Central America but has spread throughout the tropics and subtropics [14] . Its use for curing of fever is the most cited. The administration may be by oral route for example in the case of fever or by external application of the paste directly on the skin for skin diseases or snake bites [15] .
The aim of this research work is to investigate the effect of Sida acuta plant extracts as corrosion inhibitor for Al-Cu-Mg alloy in acidic medium.
2. Materials and Method
2.1. Materials
The materials used for the experiment include: Al-Cu-Mg alloy (Al—95.5%, Cu—4.0, Mg—0.5%) Sida acuta plant extract, concentrated HCl, distilled water, detergents and alcohol.
2.2. Equipment
The equipment used in the research work included 250 mL beakers, 250 mL conical flask, 1000 mL, 500 mL beaker, measuring cylinder, hack saw, metal file, emery cloth, clamp, vernier calliper, digital weighing balance, laboratory oven, brush, retort stands, threads, water bath, hand gloves.
2.3. Method
2.3.1. Extraction of Sida acuta Plant Extract
The leaves and stem of Sida acuta were collected, rinsed with distilled water and allowed to dry. The plant was grinded and then weighed with weighing balance. 500 mL of distilled water was added to 150 g of the blended plant and mixed. The resulting mixture was sieved to obtain the extract.
2.3.2. Experimental Procedure
After casting, the aluminium alloy was cut and machined to corrosion coupons (cylindrical shape) of dimension 1.5 × 1 cm. The corrosion test was based on weight loss methods. Twenty five coupons were produced for different concentration of inhibitor (10%, 20%, 30% and 40%) in the 0.5 M HCl solution and reference medium which was 0.5 M HCl solution without inhibitor. The coupons were polished and degreased in absolute ethanol, dried, weighed and stored in desiccators. The weight loss of each coupon was determined at 2 days interval for 10 days. Then the rate of corrosion, inhibition efficiency and degree of surface coverage were determined. The experiment was conducted at room temperature in the range of 26˚C - 30˚C.
2.3.3. Determination of Corrosion Rate (MPY) and Percentage Protection (%)
The weight loss was determined by finding the difference between initial and final weight of coupon after 2 days (because there would have been a tangible weight loss within the period) of immersion from the relationship(s) [16] .
(1)
where W—weight loss, Wo—initial weight, Wf—final weight.
The standard expression for measurement of corrosion rate in mils per year (MPY) was used which is given as follows [14] [17] .
(2)
where MPY—mils per year, W—weight loss in g, D—density of the materials in g/cc, T—time of exposure in hours, A—area in in2.
The inhibition efficiency was determined using the relationship [3] [7] :
(3)
where W and Wo are the corrosion rates with and without inhibitor respectively.
Adsorption consideration.
The percentage protection at each concentration of inhibitor was evaluated using the equation [18] .
(4)
where Wb and Wi are the weight loss in corrodent without and with inhibitor respectively.
3. Results and Discussion
3.1. Results
To determine the effect of length of exposure on weight loss, corrosion rate, inhibitor efficiency and percentage protection, coupons were retrieved at different exposure times for analysis. Readings were taken at room temperature using different percentage volume of Sida acuta extract. Figure 1 shows the variation of the weight loss with time of exposure for the reference and four different inhibitor concentrations in the 0.5 M HCl solution. Figure 2 is the corrosion rates variation with time of exposure for different inhibitor concentrations in the hydrochloric acid solution. Figure 3 shows the variation of inhibitor efficiency with exposure time at various inhibitor concentration, while Figure 4 shows the percentage protection with inhibitor concentration for different time of exposure.
3.2. Discussion
Coupons were pulled from the medium at four-exposure time. All the acidic solutions with Sida acuta extract
Figure 1. Weight loss of alloy in acidic medium against exposure time at different % v/v Sida acuta extract.
Figure 2. Corrosion rate of alloy in acidic medium against exposure time.
Figure 3. Variation of inhibitor efficiency with time.
were found to inhibit corrosion. After 3rd day the solution with 10% Sida acuta extract gave the highest weight loss of 0.68 g followed by the solution containing 20% v/v Sida acuta extract (weight loss of 0.5 g) down to solution with 40% of the extract with weight loss of 0.38 g. Under the same condition, the blank coupon (coupon in the medium without inhibitor) gave 1.17 g weight loss. Comparing the inhibited and blank coupon results at this exposure days; 0.49 g, 0.67 g, 0.69 g, and 0.79 g of the coupon was saved from corrosion in the acidic solution containing; 10%, 20%, 30% and 40% v/v Sida acuta extract respectively. The weight loss increases with time of exposure. On the third day, solution with 40% extract gave the lowest weight loss but highest weight loss on the tenth day. In contrast, coupon in solution containing 10% extract gave the highest weight loss on the
Figure 4. Effect of % v/v Sida acuta extract on surface coverage in acidic medium.
third day but the least weight loss on the tenth day. This shows that to have better inhibition in acidic medium at long exposure time such as ten days, it is recommended that the percentage volume inhibitor should be 10%, but at a shorter time of three days, 40% v/v of the extract is advisable to be used.
Figure 2 shows that corrosion rate decreases with exposure time in the presence of the extract. Comparing with the medium without inhibitor, there is a good indication that the rate of penetration of the corrodent is reduced. The significant decrease in corrosion rate of medium with inhibitor can be attributed to the adsorption of molecule of the inhibitor on the alloy surface, since this inhibitor molecule acts as physical barrier to restrict the diffusion of ions to and from the alloy and then prevent the alloy atoms (ions) from participating in further anodic or cathodic reactions, hence resulting in decrease in the corrosion rate [13] . The plant extract molecule can adsorb on the alloy surface and block the active sites on the surface, thereby reducing the corrosion rate in the medium.
From the plot of inhibition efficiency against exposure time (Figure 3), it can be seen that 10% inhibitor concentration has the highest protection efficiency and this increase with time of exposure, from 37.42% at third day to 75.2% at the seventh day and 93.63% at the tenth day. This shows that the inhibitor acts best within ten days at 10% inhibitor concentration.
The percentage protection is presented in Figure 4. In each of the solution, the highest percentage protection was on tenth day with 10% v/v of the extract, an indication for better protection at longer exposure time.
4. Conclusions
The results presented in this work show that Sida acuta extract inhibits corrosion of Al-Cu-Mg alloy in HCl medium at room temperature. The choice of HCl with the inhibitor for pickling of metals and cleaning scales will be one of the best choices when compared to other mineral acids since some other mineral acids like HF-HNO3 mixture results in the disadvantage of nitrous gas emission and nitrate effluent, which pollute the environment.
Therefore, in textile and food industries where processing plants make use of Al-Cu-Mg in the machine parts, the process of cleaning, pickling and descaling can be done using HCl with Sida acuta as the inhibitor. This will be more economical and efficient, and play a vital role in reducing corrosion rate.