Punching and Local Damages of Fiber and FRP Reinforced Concrete under Low-Velocity Impact Load ()
1. Introduction
The addition of fiber reinforcement is one of the most effective methods for enhancing the performance of concrete [1] [2] [3] . Conventional fiber reinforced concrete has been developed since the 1960s. In recent years, the development and application of high performance fiber reinforced cementitious composites (HPFRCC) are increasing due to their high ductility and energy absorption characteristics [4] [5] [6] [7] . However, it is difficult to obtain the required properties of the FRCC by simply adding fiber to the concrete matrix. In particular, to overcome the main weaknesses of conventional concrete (low tensile strength and ductility), higher volume fraction of fibers and smaller size of aggregates are applied to fiber-reinforced composites during mixing process. In addition, as shown in Figure 1, more than two types of fibers are used simultaneously to control micro cracks and macro cracks. This requires complex compounding processes, which can lead to entanglement or lack of uniform distribution of fibers in the matrices.
Many researchers are paying attention to fiber reinforced polymers (FRP) for the reinforcement of construction structures because of their significant advantages over high strain rates [8] [9] [10] [11] . However, the actual FRP products are skill-dependent, and the quality may not be uniform. Apart from cost, the most essential problem in the FRP system is the “bond” between the FRP and concrete. The ACI 440 assumes only two failure modes for design calculations: compressive failure of the concrete and failure of the FRP strengthening system [12] [13] . Typical failure modes of FRP-plates or sheet reinforced RC beams are classified as FRP rupture, crushing of compressive concrete, shear failure, concrete cover separation, plate-end interfacial debonding, intermediate flexural crack-induced interfacial debonding, and intermediate flexural shear crack-induced interfacial debonding [14] . Also, almost all failure modes show a brittle manner. Therefore, in this study, two-way punching tests were carried out
Figure 1. Effects on fibers on cracking.
to evaluate the performances of FRP strengthened and steel and synthetic fiber reinforced concrete specimens for impact and static loads.
2. Experimental Programs
2.1. Test Variables
The test variables in this study are summarized in Table 1. Three concrete matrices (normal concrete (NC), steel fiber reinforced concrete (SFRC), and hybrid PVA fiber reinforced cementitious composite (FRCC), were used to fabricate the test specimens. Table 2 shows the mix proportions of the concrete matrix. Ordinary Portland cement was used for a 40 MPa design strength NC. For the NC’s mixture, 50% water to cement ratio (W/C) was applied. Aggregates were crushed gravels with a maximum size of 20 mm, and sea sand. In order to achieve workability, a liquid type polycarboxylate super-plasticizer was injected. A 0.75% volume fraction of long steel fiber (30 mm end hooked) was applied into the normal concrete mixture for the steel fiber reinforced concrete (SFRC).
Table 3 presents the mix proportions of PVA FRCC [6] [7] [15] [16] . In the PVA FRCC mixture, there is no coarse aggregate, but 100 to 120 mm silica sand only used for an aggregate. Properties of steel and PVA fiber are summarized in Table 4 and shapes of fiber are shown in Figure 2. The total volume of fraction of the PVA fiber is 2%. In actual mixtures, two different PVA fibers were used, simultaneously, and a ratio of two fibers was selected from compressive and flexural strength tests [6] [7] [16] . From the mechanical tests, as summarized in Table 5, 1.6% and 0.4% for short (REC15) and long (RF4000) selected, respectively.
Table 1. Variables of material test.
Table 2. Mix proportions of NC and SFRC.
a)high range water reducing admixture to cement ratio. b)volume fraction of steel fiber on SFRC.
Table 3. Mix proportions of PVA FRCC.
a)hydroxypropyl methylcelluose to cement ratio. b)total volume fraction of PVA fibers.
Table 5. Mechanical properties of PVA FRCCs [16] .
fcu = compressive strength; f1,crack = flexural strength at first crack; fr = flexural strength; fsp = splitting tensile strength; TJSCE = toughness of JSCE method; FJSCE = equivalent flexural strength of JSCE method.
Figure 2. Shapes of steel and PVA fiber.
Note that, in the mixture of Kim et al. [16] , the W/C was 40%, however, in this study, the W/C was modified to 50% in order to match the compressive strength of NC and SFRC.
For the measurement of flexural tensile strength, 100 × 100 × 400 mm prismatic specimens were fabricated and square specimens of 50 × 350 × 350 mm were prepared for punching test. The cast specimens were stored in water at 20˚C ± 3˚C for two weeks. Fourteen days after casting, the FRPs were adhered and then cured for 14 more days at 50% ± 5% relative humidity and at a temperature of 20˚C ± 3˚C. The unidirectional E-glass and high strength carbon fiber sheets were attached with epoxy resin along the shapes of punching test specimens, with a crossing at right angles of ±45 and 0/90 degrees. Glass fiber reinforced polymer (GFRP) was only used with the normal concrete, while the carbon fiber reinforced polymer (CFRP) was used with the three matrices. The mechanical properties of fiber sheets and resins are summarized in Table 6.
2.2. Quasi-static Loading Test
The restraint conditions of punching tests are illustrated in Figure 3, the two-way punching tests were carried out with 300 mm clear spans, and quasi-static and impact loads were applied at the center of the specimens. The quasi-static loading with displacement control at a load rate of 0.01 mm/s and gradually applied using a 2700 kN capacity universal testing machine (UTM). The deflections of the center of specimens were measured with linear variable differential transformer (LVDT) [17] [18] .
2.3. Low-velocity Impact Loading Test
The low-velocity impact tests were carried out with a drop weight test machine that has a maximum capacity of about 800 Joules, as shown in Figure 3. The impact load and velocity were measured with the load cell in the tup and attached speedometer, respectively. When a tup passes through the hole, the speedometer measures the impact velocity, and then the computer calculates the impact energy, and displacement, etc. In this test, a 33.62 kgf weight was dropped along a 0.7 m clear height, and then struck the center of the specimens. Impact velocities of weight were increased by the addition of air pressure for the tests of retrofitted concrete specimens. In the test for not reinforced specimens (NC), the average impact velocity was 4.92 m/sec. For the reinforced specimens (SFRC, PVA FRCC, and FRP retrofitted specimens), as additional air pressure applied, the impact velocities were 5.91 to 5.93 m/sec.
Table 6. Properties of FRP materials.
Figure 3. Test set-up of two-way punching and details of drop-weight impact testing machine.
3. Test Results and Discussions
3.1. Basic Mechanical Properties of Concrete
Tests for mechanical properties of concrete such as compressive and flexural tensile strength were carried out according to ASTM C39 and C1609. The material properties of each matrix are summarized in Table 7 and typical load-deflection curves of matrices are illustrated in Figure 4. Compressive strengths of three mixtures were about 50 MPa, similarly, however, flexural tensile strengths of SFRC and PVA FRCC were 1.4 and 2.1 times larger than flexural strength of the NC, respectively. Also, in the curve of PVA FRCC, there is a strain hardening prior to the peak load, and after the peak, the PVA FRCC shows more rapid strain softening than the SFRC’s case.
3.2. Punching Test Results
The test results of two-way static punching tests are summarized in Table 8. Figure 5 also show the representative relationships between static loads and deflections of the two-way punching tests. As shown in Figure 5, the ultimate strength of FRP reinforced two-way NC specimens increased by 2.65 to 3.03 times greater than the plain NC series (NC-N) under quasi-static loadings, and the deflections of center at the maximum loads increased by 3.8 to 4.7 times. For the orientation of fibers, the ultimate loads and deflections of center of the 0/90 series were slightly higher than the ±45 series. The loads of SFRC-N specimens gradually increased, and the specimens reinforced with CFRP showed strain softening after the maximum loads.
In the case of the PVA FRCC, both the non-retrofitted specimens and reinforced specimens with CFRP after maximum loads showed strain softening. However, the peak loads of the CFRP retrofitted PVA FRCC series is not greater than that of the plain PVA FRCC specimens. The FRP retrofitted NC specimens
Figure 4. Typical load-deflection relationships of concrete.
Table 7. Mechanical properties of concrete.
Table 8. Test results of two-way static punching.
and plain SFRC specimens showed complex failure patterns of splitting and punching. In addition, in the failure cases of the splitting of concrete matrices, the deboning of FRPs were more serious. However, all the PVA FRCC series had typical punching failure as shown in Figure 5.
In the PVA FRCC series, the P-N specimens showed 4 times larger dissipated energy than for the energy of the N-N specimens. However, the CFRP retrofitted PVA FRCC specimens had similar capacities to the CFRP retrofitted SFRC elements. Also, identically to the SFRC’s cases, retrofitted specimens showed a plateau at the first blow and nonlinearity of time-deflection curve, and almost failed by one blow (Figure 6 & Figure 7) (Table 9).
Figure 5. Load-deflection relationships of two-way punching impact tests and punching failure of PVA FRCC specimens under static load.
Figure 6. Time-deflection relationships of two-way punching impact test.
Table 9. Test results of two-way impact punching.
Figure 7. Load-deflection relationships of two-way punching impact tests.
Figure 8 shows representative failure patterns of the two-way specimens under impact loadings. The retrofitted specimens with FRPs or long steel fiber exhibited complex failure modes of splitting and punching. The NC specimens split with irregular fragments; however, the SFRC failed with radially splitting pieces. The FRP retrofitted SFRC showed apparent punching failures and FRPs were debonded and ruptured locally. In PVA FRCC, FRP was relatively well adhered after penetration.
3.3. Comparison of Penetration Depth
Kennedy (1976) [19] suggested that seven phenomena for the impact effect on concrete, as described in Figure 9. 1) Penetration: tunneling into the target by the projectile (the length of the tunnel is called the penetration depth); 2) Cone cracking and plugging: formation of a cone-like crack under the projectile and the possible subsequent punching-shear plug; 3) Spalling: ejection of target material from the proximal face of the target; 4) Radial cracking: global cracks radiating from the impact point and appearing on either the proximal or distal face of the concrete slab or both, when cracks develop through the target thickness; 5) Scabbing: ejection of fragments from the distal face of the target; 6) Perforation: complete passage of the projectile through the target with or without a residual velocity; and, 7) Overall structural responses and failures: global bending, shear and membrane responses as well as their induced failures throughout the target.
In this study, the penetration depths were assessed, and various empirical formulas of penetration depth due to missile impact are shown in appendix.
Figure 8. Representative failure patterns of two-way specimens on impact punching loads.
Figure 9. Missile impact effects and local damage on concrete [19] [20] [21] .
The modified Petry, ACE, modified NDRC, and BRL formulae are from the tests for a lightweight and high-velocity rigid missile, whereas the Kar, Hughes, Haldar-Hamieh, and Adeli-Amin formulae are based on experiments for heavy and low-velocity impact. Formulae for perforation and scabbing [21] [22] , are not considered in this study.
Table 10 is a comparison of penetration depth for experiments and empirical
Table 10. Comparison of penetration depth.
formulae. The given conditions are: the weight and tup are steel (hence, E = 2.00 × 109 Pa), the mass of the projectile is 33.62 kg, the diameter of the projectile is 25 mm, and the aggregate diameter is 20 mm. The compressive and tensile strength used are the values of Table 9. Also, the measured projectile impacting velocities are 4.912, 5.923, and 5.944 m/s for NC, SFRC, and PVA FRCC, respectively. Except the modified Petry [19] [23] [24] and Hughes formulae [25] , all other formulae use the compressive strength of concrete, while only the Hughes formula uses the tensile strength of concrete. Therefore, with the exception of the Hughes formula, all other formulae that governed by the missile velocity predict similar values for plain and fiber reinforced concrete, or higher penetration depth in fiber reinforced concrete than in the NC.
As can be seen in Table 10, the Hughes formula is well predicted for the fiber reinforced concretes. For the NC specimen, since the tensile strength is much higher than typical values, i.e. the prediction equations for modulus of rupture of concrete (
in this test), the Hughes formula seems to show an underestimated value. However, as shown in Figure 10, since the NC specimens were split under impact loading, displacements of the end of the tup can be overestimated. Therefore, for the plain concrete, the missile effects should be adequately assessed by specimens of large dimensions. The solid lines in Figure 10 show tendencies of the Hughes formula for V0 = 4.9 and 5.9 m/s, also lozenge shaped dots means the average perforation depth of each matrix.
Figure 10. Comparison of penetration depth between experiment and Hughes formula.
4. Concluding Remarks
Punching tests were performed in order to observe the behaviors of fiber reinforced polymer (FRP) strengthened and fiber reinforced concrete specimens for quasi-static and low-velocity impact loads by using the universal testing machine (UTM) and drop weight testing machine. The following is an outline of concluding remarks for the material tests:
1) Two-way square specimens were fabricated with normal concrete (NC), steel fiber reinforced concrete (SFRC), and hybrid PVA fiber reinforced cementitious composite (PVA FRCC). For the hybrid PVA FRCC, two different types of fiber were used, and the FRPs were attached along the shapes of the specimens at ±45 and 0/90 degrees.
2) The maximum load of FRP reinforced NC specimens increased by 2.65 to 3.03 times greater than the plain NC series under quasi-static loadings, and the deflections of center at the maximum loads increased by 3.8 to 4.7 times. The ultimate loads of the SFRC-N series increased by 38% more than the N-N series, and for the PVA FRCC, the carbon fiber reinforced polymer (CFRP) strengthening improves 62% of the peak load. The loads of SFRC-N specimens gradually increased, but the specimens reinforced with CFRP showed strain softening after the maximum loads. Both the non-retrofitted specimens and reinforced PVA FRCC specimens with CFRP after maximum loads exhibited strain softening.
3) The FRP reinforced NC, SFRC, and PVA FRCC specimens showed twice the amount of enhanced dissipated energy (total energy) under impact loadings than the non-retrofitted specimens. In the low-velocity impact test of the two-way NC specimens strengthened by FRPs, the ultimate impact loads increased by 1.33 times, and the total dissipated energy increased by 4 to 5 times greater than the plain NC series. For the two-way specimens, the total energy increased by 217% between the non-retrofitted SFRC and NC specimens. The total dissipated energy of the CFRP retrofitted SFRC was twice greater than that of the plain SFRC series. In the PVA FRCC series, the P-N specimens showed 4 times greater dissipated energy than for the energy of the N-N specimens. However, the CFRP retrofitted PVA FRCC specimens had similar capacities to the CFRP retrofitted SFRC elements.
4) For the penetration of two-way specimens with steel fiber, the Hughes formula considering the tensile strength of concrete was a better predictor than other empirical formulae. However, for plain concrete, specimens need to be of larger size to avoid splitting failure. In addition, penetration depth due to missile impact may be much different due to the tensile strength of fiber reinforced concrete, so it should be improved through various experiments.
Appendix: Empirical Formulae for Penetration Depth
Modified Petry formula [19] [23] [24]
(1)
where, k = 6.36 × 10−4 for massive plain concrete;
= 3.39 × 10−4 for normal reinforced concrete; and
= 2.26 × 10−4 for specially reinforced concrete in modification Petry I.
Ballistic Research Laboratory (BRL) formula [19] [26] [27] [28]
(2)
Army corps of engineers (ACE) formula [19] [29] [30]
(3)
Modified NDRC formula [19] [31] [32]
(4a)
(4b)
(4c)
Ammann and Whitney formula [19]
(5)
Whiffen formula [33]
(6)
where,
, and about ±15% prediction accuracy, the corresponding ranges of application are 5.52 <
< 68.95 MPa, 0.136 < M < 9979.2 kg, 12.7 < d < 965.2 mm, and 0 < V0 < 11.27.8 m/s.
Kar formula [28] [34]
(7a)
(7b)
(7c)
where, E, Es = elastic moduli of the projectile and steel, respectively. If the projectile is steel, formula is identical to the modified NDRC formula.
UKAEA formula [35]
(8a)
(8b)
(8b)
(8c)
Within 25 <
< 300 m/s, 22 <
< 44 MPa, and 500 < M/d3 < 200,000 kg/m3, the prediction accuracy is ±20% for x/d > 0.75, and +100% to −50% for x/d < 0.75.
Haldar-Hamieh formula [36] [37]
(9a)
(9b)
(9b)
(9c)
Adeli-Amin formula [27]
(10a)
(10b)
Hughes formula [25]
(11a)
(11b)
(11c)
Healey and Weissman formula [28]
(12a)
(12b)
(12c)
IRS formula [38]
For penetration
(13a)
For total protection of the penetration, perforation, and scabbing, the minimum wall thickness is
(13b)
CRIEPI formula [39]
(14)
Notation
= aggregate diameter (m)
= diameter of the projectile (m)
= unconfined compressive strength of concrete (Pa)
= tensile strength of concrete (Pa)
= thickness of the concrete target
= 0.2 m
= mass of the projectile (kg)
= projectile nose shape coefficient (1.0, 0.12, 1.26, and 1.39 for flat, blunt, spherical and very sharp noses, respectively)
= nose shape factor (0.72, 0.84, 1.0, and 1.14 for flat, hemispherical, blunt, and very sharp noses, respectively)
= projectile impacting velocity (m/s), and
= penetration depth (m).