Induction of Anthracnose Disease Resistance on Chili Fruit by Treatment of Oligochitosan—Nanosilica Hybrid Material

Abstract Full-Text HTML XML Download Download as PDF (Size:1042KB) PP. 1105-1113
DOI: 10.4236/as.2017.810080    683 Downloads   1,180 Views   Citations

ABSTRACT

Oligochitosan (OC) with molecular weight Mw of 5000 g/mol was prepared by gamma Co-60 ray irradiation of chitosan solution. Nanosilica (nSiO2) with the size of 10 - 30 nm was synthesized by calcination of acid treated rice husk. The mixture of 1% OC - 1% nSiO2 was prepared by dispersion of nSiO2 in OC solution. The morphology of nSiO2 in the mixture of OC-nSiO2 was measured from images of transmission electron microscopy (TEM). The effect of foliar application of the mixture of OC-nSiO2 on the induction of resistance against anthracnose disease caused by Colletotrichum gloeosporioides fungus on chili fruits was investigated. Results indicated that foliar application of OC-nSiO2 with the concentration of 60 mg/l - 60 mg/l was found to be as the optimal treatment that reduced the disease severity on chili fruits to 22.2% compared with 90.0% of the control. Thus, OC-nSiO2 hybrid material could be considered as an effective biotic elicitor to prevent anthracnose disease infection for chili fruits. Furthermore, the prepared OC-nSiO2 hybrid material can also be used as an environmentally friendly agrochemical product for sustainable development of agriculture.

1. Introduction

Chitosan and oligochitosan (OC) have attracted considerable interest due to their many unique biological activities such as antioxidant activity [1] , antimicrobial activity [2] , plant growth promotion such as rice [3] , coffee [4] , soybean [5] , ... In addition, chitosan and OC also have elicitation effect to induce disease resistance in plants such as grapevine [6] , potato [7] , ... Moreover, OC was supposed as a plant vaccine that is similar to general animal vaccine [8] . The excessive use of chemical fertilizer and pesticide in agriculture may lead to adverse effects in food products and in the environment. Therefore, the recent trend in agriculture has been focused on organic and vertical farming not only addressing the rising concern for environmental issues but also accommodating the demands of food of increasing world population [9] . Organic farming is considered as a viable alternative in comparison to chemical-based agriculture [10] . Nanotechnology opens up a wide applicability in various fields like medicine, pharmaceutics, electronics and agriculture. Nanomaterials hold great promise of improved plant disease resistance, controlled release of agro-chemicals, enhanced plant growth, etc. [11] . According to [12] , nanomaterials can be used as a magical tool for enhancing growth and improvement of agricultural production. Recently, the synergistic effect of a mixture of chitosan-silica induced resistance in tomato against bacterial wilt caused by Ralstonia solanacearum was reported for the first time [13] . Chili fruit is widely consumed mainly as a spice for food ingredients. World production of chilies in 2009 was estimated to be about 3 million tones [14] . The top-ten chili producing countries were India, China, Ethiopia, Myanmar, Mexico, Vietnam, Peru, Pakistan, Ghana and Bangladesh, and accounted for more than 85% of the world chili production in 2007 [15] . Anthracnose disease has been a real threat to chili (Capsicum spp.) production in the tropics and subtropics worldwide. Anthracnose is caused by a complex of Colletotrichum species, typically Colletotrichum capsici, Colletotrichum acutatum, and Colletotrichum gloeosporioides having been reported as significant pathogens in many countries including China, India, Brazil, Thailand and Vietnam, etc. [16] . Therefore, protection of chili fruits from infection of anthracnose disease is in high demand. Up to now, there are rare reports in the literature on the reduction of anthracnose disease on chili fruits using OC-nSiO2 hybrid materials.

To contribute to the development of organic farming, in the present study, OC was prepared by gamma Co-60 irradiation degradation of chitosan in solution and nSiO2 was prepared from rice husk. The effect of foliar application of OC-nSiO2 mixture on the induction of resistance against anthracnose disease caused by Colletotrichum gloeosporioides fungus on chili fruits was investigated.

2. Materials and Methods

2.1. Preparation of Oligochitosan by γ-Irradiation

Chitosan from shrimp shell with a degree of deacetylation (DDA%) of ~91.4%; the weight average molecular weight (Mw) of 44.5 × 103 g/mol was supplied by a factory in Vietnam. OC with Mw of 5000 g/mol was prepared by gamma Co-60 ray irradiation degradation method as described in our previous paper [17] with some modifications. Briefly, chitosan (40 g) was dissolved in 800 ml of 2% (w/v) lactic acid solution, then 15 ml of hydrogen peroxide (30% H2O2) and 185 ml water were added to prepare 1 liter of 4% (w/v) chitosan solution containing 0.5% H2O2. Then, the prepared chitosan solution was irradiated at ambient condition on gamma SVST Co-60/B irradiator at the VINAGAMMA Center with a dose of 21 kGy.

2.2. Preparation of Nanosilica from Rice Husk

nSiO2 with particles size of 10 - 30 nm was prepared from rice husk as described in our previous paper [18] . Briefly, raw rice husk was first rinsed with water to remove dusts, soluble substances, and other contaminants. It was then dried at 60˚C in forced air oven (Yamato, DNF 410, Japan). 50 g of the dried rice husk was then treated with 500 ml of 0.5 N HCl at ambient temperature for 2 h by magnetic stirring. Then, it was decanted and thoroughly washed with distilled water until the rinse became free from acid. The treated-rice husk was subsequently dried in forced air oven until to dry and ground into fine powder. Finally, the rice husk powder was incinerated at 700˚C for 2 h inside a programmable furnace (Nabertherm GmbH, Germany) to obtain nSiO2.

2.3. Preparation of Oligochitosan-Nanosilica Hybrid Material

10 g of nSiO2 were mixed with 77 ml of NaOH 1M solution by string for 60 min. Then 250 ml of 4% OC solution and distilled water slowly added to prepare 1 liter of 1% OC-1% nSiO2. The mixture was then stirred for 4 h at room temperature. To increase the adsorption ability of OC on nSiO2, pH of the mixture was adjusted to ~7.5 [19] . The particle size of nSiO2 from rice husk and nSiO2 in the OC-nSiO2 hybrid material was measured using transmission electron microscopy (TEM) images [18] .

2.4. Preparation of Colletotrichum gloeosporioides Fungal Suspension

The C. gloeosporioides fungal strain was obtained from Microbial Laboratory of the Research and Development Center for Hi-Tech Agriculture. An inoculum of C. gloeosporioides was prepared by cultivating fungal colonies in Petri dishes on potato dextrose agar (PDA) medium at 30˚C for ten days. Then, the fungal spores were harvested by flooding Petri dishes with sterile distilled water. The obtained suspension of fungal spores was then adjusted to 104 spores/ml with distilled water [20] .

2.5. Experimental Design

The 60 - 65 day-old-chili plants (Capsicum frutescens L.) with young green fruits were used for the study. The experiment was conducted in the greenhouse of Hi-Tech Agriculture Center, Cu Chi, Ho Chi Minh City, at 30˚C ± 2˚C and RH of 60% ± 2%. The experimental treatments were arranged in a randomized complete block design with five treatments namely: control (water), 20 - 20, 40 - 40, 60 - 60 and 80 mg/l - 80 mg/l of OC-nSiO2. Particularly, 1 liter of 1% OC - 1% nSiO2 was diluted with water up to the volume of 500, 250, 167, and 125 liters for preparation of foliar spaying solution of 20 - 20, 40 - 40, 60 - 60 and 80 mg/l - 80 mg/l of OC-nSiO2, respectively. Each treatment consisted of three replications with 10 plants/replication.

2.6. Foliar Application of OC-nSiO2 on Chili Plants and Fungal Inoculation on Chili Fruits

The chili plants were sprayed three times with a duration of one time per week. After 24 h of the third spaying, the chili fruits were caused lesions as follows: 50 fruits/chili plant were randomly selected to create lesion by using a needle with a diameter of 0.6 mm to pierce through the fruits. Then, the injury fruits were inoculated with C. gloeosporioides fungus by spaying fungal spore suspension of 104 spores/ml.

2.7. Assessment of Disease Severity

After 7 days of fungal inoculation, the disease severity (DS) was then recorded and calculated as follows [21] :

DS (%) = 100 ´ (number of infected fruits)/(total number of inoculated fruits)

All data were statistically analyzed by analysis of variance (ANOVA) according to the experimental design and Least Significant Difference (LSD) at 5% probability level was utilized to compare the different means.

3. Results

3.1. Morphology of nSiO2

TEM images of nSiO2 and nSiO2 in the mixture of 1% OC - 1% nSiO2 were presented in Figure 1. The size of nSiO2 synthesized from rice husk was of 10 - 30 nm in

(a) (b)

Figure 1. TEM images of nSiO2 (a) and nSiO2 in mixture of 1% OC - 1% nSiO2 (b).

Figure 1(a) and the size of nSiO2 in the OC-nSiO2 mixture in Figure 1(b) was observed to be rather smaller to that of original nSiO2.

The schematic interaction of OC with nSiO2 was illustrated in Figure 2. When nSiO2 was mixed with OC solution, the bonding of −Si-O-C−, −Si-O-H2N−, and −Si-OH occurred in the mixture of OC-nSiO2.

3.2. Anthracnose Disease Severity on Chili Fruits

Photographs of chili plants in greenhouse and symptom of anthracnose disease with concave lesion stains in slightly brown color on chili fruits caused by C. gloeosporioides fungus were presented in Figure 3.

The disease severity of chili fruits treated with OC-nSiO2 with different concentration and inoculated with C. gloeosporioides fungal spores was presented in Table 1.

Figure 2. Schematic illustration of interactions between OC and nSiO2.

(a) (b)

Figure 3. Photographs of chili plants in greenhouse (a) and symptom of anthracnose disease on chili fruit caused by C. gloeosporioides fungus (b).

Table 1. Disease severity of chili fruits inoculated with C. gloeosporioides fungal spores.

Different letters in the same column indicate significant differences at P ≤ 0.05.

4. Discussion

The greatest challenge in the application of OC for plant protection lies in the development of efficient methods for large-scale production of OC [22] . For this aspect, the production of OC by gamma Co-60 irradiation method can be favorably applied on large-scale [17] [23] .

TEM image in Figure 1(b) indicated that the nSiO2 morphology was almost maintained as the original nSiO2. However, some small parts were aggregated that may be presumed due to the interaction of nSiO2 with OC. Also, nSiO2 may be changed to Si(OH)4 in slightly basic medium pH ~7.5 [19] . As our observation, OC solution, unlike chitosan, is not precipitated in neutral and/or slightly basic medium. As can be observed in Figure 2 that the bonding of -Si-O-C-, -Si-O-H2N-, and -Si-OH between OC and nSiO2 was formed [21] and owing to these bonds, the colloidal mixture of OC-nSiO2 was in good stability during storage. Accordingly, the bonding of chitosan and nSiO2 in the mixture of chitosan-nSiO2 [24] was almost the same as in the mixture of OC-nSiO2.

Results in Table 1 indicated that foliar application of OC-nSiO2 induced significantly anthracnose disease resistance caused by C. gloeosporioides fungus on chili fruits. Among four treatments with different concentration of OC-nSiO2, the treatment with a concentration of 60 mg/l - 60 mg/l was found to act the highest effect in reduction of anthracnose disease on chili fruits. In particular, the disease severity of the treatment of 60 mg/l - 60 mg/l OC-nSiO2 was reduced to 22.2% compared to 90.0% of the control (water). It was reported that the bacterial wilt incidence on tomato plants was also significantly reduced by the treatment with chitosan-silicon mixture [13] . In particular, the bacterial wilt incidence was of ~20% for tomato plants treated with chitosan-silicon compared to ~80% of the control (without chitosan and silicon, inoculation with R. solanacearum). Recently, foliar application of OC-nSiO2 with a concentration of 50 mg/l - 50 mg/l increased soybean seed yield of 17% compared to control (water) [23] . Thus, it can be expected that foliar application of OC-nSiO2 is not only to induce disease infection resistance but also to increase chili fruit yield. Further study on the effect of OC-nSiO2 treatment on the enhancement of chili fruit yield should be carried out. Moreover, the nanomaterials, owing to their increased contact surface area, might have toxic effects that are not apparent in the bulk materials especially in the open agricultural ecosystem [24] . Therefore, the selection of nanomaterial for application in the field may be critically desirable as materials, which are non-toxic, biocompatible and biodegradable [25] . In this issue, it was reported that different form of synthetic amorphous silica has been used in a wide variety of industrial and consumer applications including food, cosmetics and pharmaceutical products for many decades, and no environmental or health risks have been associated with these materials including nSiO2 [26] . Therefore, the as-prepared OC-nSiO2 hybrid material can be considered as a safe product to human health and environment.

5. Conclusion

The method of gamma Co-60 ray irradiation degradation of chitosan in solution to prepare oligochitosan can be favorably applied on large scale. Nanosilica, a value-added product was appropriately synthesized from rice husk, an abundant agriculture waste. Foliar application of OC-nSiO2 on chili plant resulted in significant induction of anthracnose disease resistance caused by C. gloeosporioides fungus on chili fruits. Thus, the OC-nSiO2 hybrid material originated from natural resources can be potentially used to replace hazardous agrochemicals for sustainable agricultural production.

Acknowledgements

This research is funded by Vietnam National Foundation for Science and Technology Development (NAFOSTED) under grant number “106-NN.03-2015.84”.

Conflicts of Interest

The authors declare no conflicts of interest.

Cite this paper

Dzung, P. , Hung, L. , Ngoc, L. , Hiet, H. , Le, B. , Thang, N. , Phu, D. , Duy, N. and Hien, N. (2017) Induction of Anthracnose Disease Resistance on Chili Fruit by Treatment of Oligochitosan—Nanosilica Hybrid Material. Agricultural Sciences, 8, 1105-1113. doi: 10.4236/as.2017.810080.

References

[1] Kim, K.W. and Thomas, R.L. (2007) Antioxidative Activity of Chitosans with Varying Molecular Weights. Food Chemistry, 101, 308-313.
https://doi.org/10.1016/j.foodchem.2006.01.038
[2] Zheng, L.Y. and Zhu, J.F. (2003) Study on Antimicrobial Activity of Chitosan with Different Molecular Weights. Carbohydrate Polymers, 54, 527-530.
https://doi.org/10.1016/j.carbpol.2003.07.009
[3] Chamnanmanoontham, N., Pongprayoon, W., Pichayangkura, R., Roytrakul, S. and Chadchawan, S. (2015) Chitosan Enhances Rice Seedling Growth via Gene Expression Network between Nucleus and Chloroplast. Plant Growth Regulation, 75, 101-114.
https://doi.org/10.1007/s10725-014-9935-7
[4] Dzung, N.A., Khanh, V.T.P. and Dzung, T.T. (2011) Research on Impact of Chitosan Oligomers on Biophysical Characteristics, Growth, Development and Drought Resistance of Coffee. Carbohydrate Polymers, 84, 751-755.
https://doi.org/10.1016/j.carbpol.2010.07.066
[5] Luan, L.Q., Nagasawa, N., Tamada, M. and Nakanishi, T.M. (2006) Enhancement of Plant Growth Activity of Irradiated Chitosan by Molecular Weight Fractionation. Radioisotopes, 55, 21-27.
https://doi.org/10.3769/radioisotopes.55.21
[6] Aziz, A., Trotel-Aziz, P., Dhuicq, L., Jeandet, P., Couderchet, M., et al. (2006) Chitosan Oligomers and Copper Sulfate Induce Grapevine Defense Reactions and Resistance to Gray Mold and Downy Mildew. Phytopathology, 96, 1188-1194.
https://doi.org/10.1094/PHYTO-96-1188
[7] Vasyukova, N.I., Zinov’eva, S.V., Il’inskaya, L.I., Perekhod, E.A., Chalenko, G.I., et al. (2001) Modulation of Plant Resistance to Diseases by Water-Soluble Chitosan. Applied Biochemistry and Microbiology, 37, 103-109.
https://doi.org/10.1023/A:1002865029994
[8] Yin, H., Zhao, X. and Du, Y. (2010) Oligochitosan: A Plant Disease Vaccine: A Review. Carbohydrate Polymers, 82, 1-8.
https://doi.org/10.1016/j.carbpol.2010.03.066
[9] Garg, A. and Balodi, R. (2014) Recent Trends in Agriculture: Vertical Farming and Organic Farming. Advances in Plants and Agriculture Research, 1, Article ID: 00023.
https://doi.org/10.15406/apar.2014.01.00023
[10] Stockdale, E.A., Lampkin, N.H., Hovi, M., Keatinge, R., Lennartsson, E.K.M., et al. (2001) Agronomic and Environmental Implications of Organic Farming Systems. Advances in Agronomy, 70, 263-327.
https://doi.org/10.1016/S0065-2113(01)70007-7
[11] Huang, S., Wang, L., Liu, L., Hou, Y. and Li, L. (2015) Nanotechnology in Agriculture, Livestock, and Aquaculture in China. A Review. Agronomy for Sustainable Development, 35, 369-400.
https://doi.org/10.1007/s13593-014-0274-x
[12] Taha, R.A. (2016) Nanotechnology and Its Application in Agriculture. Advances in Plants and Agriculture Research, 3, Article ID: 00089.
https://doi.org/10.15406/apar.2016.03.00089
[13] Kiirika, L.M., Stahl, F. and Wydra, K. (2013) Phenotypic and Molecular Characterization of Resistance Induction by Single and Combined Application of Chitosan and Silicon in Tomato against Ralstonia solanacearum. Physiological and Molecular Plant Pathology, 81, 1-12.
https://doi.org/10.1016/j.pmpp.2012.11.002
[14] Tiwari, R.K. (n.d.) Post Harvest Profile of Chili.
http://agmarknet.gov.in/Others/preface-chhilli.pdf
[15] Huq, A.S.M.A. and Arshad, F.M. (2010) Technical Efficiency of Chili Production. American Journal of Applied Sciences, 7, 185-190.
https://doi.org/10.3844/ajassp.2010.185.190
[16] Mahasuk, P., Khumpeng, N., Wasee, S., Taylor, P.W.J. and Mongkolporn, O. (2009) Inheritance of Resistance to Anthracnose (Colletotricum casici) at Seedling and Fruiting Stages in Chili Pepper (Capsicum spp.). Plant Breeding, 128, 701-706.
https://doi.org/10.1111/j.1439-0523.2008.01615.x
[17] Duy, N.N., Phu, D.V., Anh, N.T. and Hien, N.Q. (2011) Synergistic Degradation to Prepare Oligochitosan by γ-Irradiation of Chitosan Solution in the Presence of Hydrogen Peroxide. Radiation Physics and Chemistry, 80, 848-853.
https://doi.org/10.1016/j.radphyschem.2011.03.012
[18] Dzung, P.D, Ngoc, L.S., Thuy, N.N., Truc, L.T.M., Le, B.V., et al. (2016) Effect of Nanosilica from Rice Husk on the Growth Enhancement of Chili Plant (Casicum frutescens L.). Journal of Science and Technology, 54, 607-613.
[19] Tiraferri A., Maroni, P., Rodríguez, D.C. and Borkovec, M. (2014) Mechanism of Chitosan Adsorption on Silica from Aqueous Solutions. Langmuir, 30, 4980-4988.
https://doi.org/10.1021/la500680g
[20] Somapala, K.S., Weerahewa, H.L.D. and Thrikawala, S. (2016) Enhanced Resistance against Anthracnose Disease in Chili Pepper (Capsicum annuum L.) by Soil Application of Potassium. International Journal of Agriculture, Forestry and Plantation, 2, 35-39.
http://digital.lib.ou.ac.lk/docs/bitstream/701300122/1227/1/KLIAFP2_39.pdf
[21] Ahmad, A. and Ashraf, Y. (2016) In Vitro and In Vivo Management of Alternaria Leaf Spot of Brassica campestris L. Journal of Plant Pathology & Microbiology, 7, Article ID: 1000365.
https://doi.org/10.4172/2157-7471.1000365
[22] Das, S.N., Madhuprakash, J., Sarma, P.V.S.R.N., Purushotham, P., Suma, K., et al. (2015) Biotechnological Approaches for Field Applications of Chitooligosaccharides (COS) to Induce Innate Immunity in Plants. Critical Reviews in Biotechnology, 35, 29-43.
https://doi.org/10.4172/2157-7471.1000365
[23] Phu, D.V., Du, B.D., Tuan, L.N.A., Tam, H.V. and Hien, N.Q. (2017) Preparation and Foliar Application of Oligochitosan-Nanosilica on the Enhancement of Soybean Seed Yield. International Journal of Environment, Agriculture and Biotechnology, 2, 421-428.
https://doi.org/10.22161/ijeab/2.1.53
[24] Sumarni, W., Iswari, R.S., Marwoto, P. and Rahayu, E.F. (2016) Physical Characteristics of Chitosan-Silica Composite of Rice Husk Ash. IOP Conference Series: Materials Science and Engineering, 107, Article ID: 012039.
https://doi.org/10.1088/1757-899X/107/1/012039
[25] Ghormade, V., Deshpande, M.V. and Paknikar, K.M. (2011) Perspective for Nano-Biotechnology Enabled Protection and Nutrition of Plants. Biotechnology Advances, 29, 792-803.
https://doi.org/10.1016/j.biotechadv.2011.06.007
[26] Fruijtier-Pölloth, C. (2012) The Toxicological Mode of Action and the Safety of Synthetic Amorphous Silica-A Nanostructured Material. Toxicology, 294, 61-79.
https://doi.org/10.1016/j.tox.2012.02.001

  
comments powered by Disqus

Copyright © 2018 by authors and Scientific Research Publishing Inc.

Creative Commons License

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.