Patel, N.H., Deshpande, M.P. and Chaki, S.H. (2015) Study on Structural, Magnetic Properties of Undoped and Ni Doped CdS Nanoparticles. Materials Science in Semiconductor Processing, 31, 272-280.
https://doi.org/10.1016/j.mssp.2014.11.039

has been cited by the following article:

• TITLE: Synthesis and Characterization of Metal-Doped (Ni, Co, Ce, Sb) CdS Catalysts and Their Use in Methylene Blue Degradation under Visible Light Irradiation

  AUTHORS: Irem Firtina Ertis, Ismail Boz

  KEYWORDS: Chalcogenides, Chemical Synthesis, Optical Properties, Photocatalytic Reaction

  JOURNAL NAME: Modern Research in Catalysis, Vol.6 No.1, December 9, 2016

  ABSTRACT: Metal doped CdS nanoparticles were synthesized by a simple chemical precipitation route with different metals. The obtained nanoparticles were characterized by XRD and UV-vis reflectance spectroscopy. The results indicated that metal-doped CdS catalysts were successfully obtained with cubic structure and 4.0 - 4.5 nm crystallite size. The band gap energies of metal-doped CdS catalysts were estimated using UV-visible reflectance spectra to be about the range of 2.25 - 2.55 eV. Methylene blue was degraded by using metal doped CdS nanoparticles under a 400 W medium-pressure mercury lamp of visible light irradiation (λ > 420 nm). Higher degradation efficiency was achieved by adding metals to the photocatalyst compared with the single CdS catalyst. In this case, the degradation efficiency of Co-CdS catalyst after 4h irradiation time was about 87%.