C. U. Melo, E. Kamseu and C. Djangang, “Effect of Fluxes on the Fired Properties between 950℃ - 1050℃ of Some Cameroonian Clays,” Tiles & Bricks International, Vol. 19, No. 6, 2003, pp. 57-69.

has been cited by the following article:

• TITLE: Industrial Potentiality of Alluvial Clays Deposits from Cameroon: Influence of Lateritic Clayey Admixture for Fired Bricks Production

  AUTHORS: Aubin Nzeugang Nzeukou, Véronique Kabeyene Kamgang, Robert Eko Medjo, Uphie Chinje Melo, André Njoya, Patrick Ninla Lemougna, Nathalie Fagel

  KEYWORDS: Alluvial Clay Deposit; Characterization; Lateritic Clay Admixture; Brick; Cameroon

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.1 No.5, September 13, 2013

  ABSTRACT: The cartography and characterization of an alluvial clay deposit from Ebebda (Central region of Cameroon) were carried out in order to assess its suitability for the production of fired clay bricks. The clayey area investigated is ~ 50,000 m2 with an average thickness of the exploitable layer of 2.2 m, suggesting a deposit of about ~2.2 × 105 tonnes of clay. Mineralogy, physico-chemical and thermal analyses as well as firing properties were performed on representative clay samples. Kaolinite and quartz are the major minerals associated to illite. Upon heating to 900℃ - 1200℃, the linear shrinkage varies from 1.5% to 15%, the water absorption from 1.5% to 24% and the bending strength from 2 to 12 MPa. The admixture of lateritic clays (widely available) at 50%, 60%, 70% and 80% allow to decrease the shrinkage and bending strength, and to increase the water absorption. Overall, properties were satisfying the requirement for fired brick with 70% of laterite in the mixture.