Ribeiro, C.,Sencadas, V., Caparros, C., Ribelles, J.L.G. and Lanceros-Méndez, S. (2012) Fabrication of Poly(Lactic Acid)-Poly(Ethylene Oxide) Electrospun Membranes with Controlled Micro to Nanofiber Sizes. Journal of Nanoscience and Nacotechnology, 12, 6746-6753.
http://dx.doi.org/10.1166/jnn.2012.4544

has been cited by the following article:

• TITLE: Morphology and Thermal Properties of Core-Shell PVA/PLA Ultrafine Fibers Produced by Coaxial Electrospinning

  AUTHORS: Raquel P. Gonçalves, Flavia F. F. da Silva, Paulo H. S. Picciani, Marcos L. Dias

  KEYWORDS: Core-Shell Fibers, Electrospinning, Poly(Lactic Acid), Poly(Vinyl Alcohol)

  JOURNAL NAME: Materials Sciences and Applications, Vol.6 No.2, February 15, 2015

  ABSTRACT: Coaxial electrospinning process was used to produce biodegradable membranes made of coreshell fibers of a poly(lactic acid) (PLA) shell and a poly(vinyl alcohol) (PVA) core. Scanning electron microscopy analyses of these structures showed that the PLA shell can present certain porosity depending on the process condition. FTIR-ATR and contact angle measurements also suggested imprisonment of the PVA core within the PLA shell. This type of structure was also confirmed by means of transmissions electron microscopy. The morphology of these fibers was dependent on the flow rate of both core and shell solutions, and homogeneous and smooth surface was only attained when the flow rate of the external PLA solution was 4 times the flow rate of the internal PVA solution. The increase in the PLA solution flow rate increases the diameter of the core-shell fiber which reaches up to 1.7 μm. Nevertheless, fibers with smaller average diameter could also be produced (200 nm). These core-shell fibers presented improved hydrophilicity as compared with monolithic PLA fibers.