Scherban, A.P. and Datsenko O.A. (2013) Analysis of Phase Diagrams of Binary Metal Systems in the Field at Low Concentration of Components. Journal of V. N. Karazin Kharkiv National University, 60, 95-99.

has been cited by the following article:

• TITLE: Construction of Solidus Lines of Binary Metal Systems Having a Low Solubility of Components in the Solid Phase

  AUTHORS: A. P. Shcherban, O. A. Datsenko, G. P. Kovtun

  KEYWORDS: Binary Metal System, Cadmium, Zinc, Tellurium, Phase Diagram, Solidus Line, Eutectic Transformation, Retrograde Solubility

  JOURNAL NAME: Open Journal of Metal, Vol.4 No.3, September 23, 2014

  ABSTRACT: The paper presents the calculation results on the construction of solidus lines of phase diagrams for some binary metal systems based on cadmium, zinc and tellurium. The investigations have been carried out using the phase equilibrium thermodynamics and known liquidus lines. By the calculation method the solidus lines of phase diagrams of the Cd-Na, Cd-Tl, Te-Ga, Te-As, Te-Cu and Zn-Sn systems were constructed in the temperature range from the base component melting point to the eutectic transformation temperature. In the Cd-Tl, Te-As, Te-Cu and Zn-Sn systems a retrograde solubility of the second component in the solid phase was observed. The temperature and maximum solubility values at the retrograde behavior of solidus lines, as well as, the limiting solubility values of components at eutectic transformation in the systems based on Cd, Zn and Te were determined.