Pico, D., Wilms, C., Seide, G., Gries, T., Kleinholz, R. and Tiesler, H. (2012) “Glass Fibers” Ullmann’s Encyclopedia of Industrial Chemistry. Fibers, 12. Wiley-VCH Verlag GmbH & Co. KGaA.

has been cited by the following article:

• TITLE: Wood Particle-Recycled Glass Fiber Hybrid Composites

  AUTHORS: Kayode E. Oluwabunmi, Lee M. Smith, Sheldon Q. Shi

  KEYWORDS: Particleboard, Recycled Glass Fibers, Water Absorption, Thickness Swelling

  JOURNAL NAME: Open Journal of Composite Materials, Vol.7 No.5, October 27, 2017

  ABSTRACT: This study was done with the aim of assessing the feasibility of mechanically recycled glass fiber particleboards made from (loblolly pine and longleaf pine) wood particles with epoxy as binder. The modulus of rupture (MOR) and modulus of elasticity (MOE) were evaluated as indicators of mechanical performance. The water absorption rate and thickness swelling rate were also analyzed to investigate the physical performance of the board. An increase of over 80% in MOE values was obtained for the boards with 10 wt%glass fiber inclusion. For the MOR values, there was an increase of over 84.4% in both densities and glass fiber inclusions of all the board densities. However, there was a decrease in MOE when 30 wt% glass fibers wereincorporated into boards with density of 500kg/m3and 700kg/m3. A r-squared value of 0.869 supported the obtained resultthat the correlation between water absorption rate and thickness swelling rate was a function of the density of the composites.