M. El Omari, E. Hafidi, M. El Omari, A. Abaouz, A. Yacoubi, J.M. Reau, J. Senegas, “Short-range order and diffusion processes in the Na1?xBixF1+2x anion-excess solid solution,” Mater. Let., vol. 53, pp. 138–144, March 2002.

has been cited by the following article:

• TITLE: Ion Mobility in the Fluorite Solid Solutions 50PbF2–30BiF3–20K(Na)F According to 19F, 23Na NMR Data

  AUTHORS: V.Ya. Kavun, A.B. Slobodyuk, I.A. Telin, R.M. Yaroshenko, I.G. Maslennikova, V.K. Goncharuk, V.I. Kharchenko

  KEYWORDS: Solid Solutions 50PbF2–30BiF3–20K(Na)F; Ion Mobility; Ionic Conductivity; 19F, 23Na NMR spectra; functional materials

  JOURNAL NAME: Advances in Materials Physics and Chemistry, Vol.2 No.4B, January 15, 2013

  ABSTRACT: Ion mobility in solid solutions of the fluorite structure 50Pb2–30BiF3–20KF (I) and 50Pb2–30BiF3–20NaF (II) was studied by NMR method. Analysis of 19F, 23Na NMR spectra made it possible to reveal the character of ion motions in the fluoride and sodium sublattices with temperature variation, to determine the types and temperature ranges in which they took place. It was found that the dominant form of ionic mobility in the samples I and II above 380 K was the diffusion of fluoride and sodium ions. According to preliminary results of electro-physical studies, the conductivity reached values of ~ 2×10–2 – 10–3 S/cm above 500 K. The solid solutions I and II can be recommended as a basis for use in the development of new functional materials.