Huang, Y., Zhao, B., Lin, S. and Sun, Y. (2017) Optimization of Thermoelectric Properties in Layered Bi2Sr2Co2Oy via High-Magnetic-Field Sintering. Journal of Alloys and Compounds, 705, 745-748.
https://doi.org/10.1016/j.jallcom.2017.02.104

has been cited by the following article:

• TITLE: Thermoelectric Properties of Misfit Layered Bismuth-Based Rhodium Oxides, (Bi,Pb)2Sr2Rh2Oy

  AUTHORS: Takuya Watanabe, Hiroshi Irie

  KEYWORDS: Electroceramics, Layered Rhodium Oxide, Misfit Layer Structure, Thermoe-lectric Material, Harman Method

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.6 No.7, July 9, 2018

  ABSTRACT: Rhodium oxides, including a misfitlayered structure with alternate stacking of a rock salttype layer and a hexagonal RhO2 layer, are expected to have good thermoelectric properties. Among them, the thermoelectric properties (electrical conductivity (σ), Seebeck coefficient (S), Figure of merit (ZT) and calculated thermal conductivity (κ) by S, σ, ZT, and absolute temperature (T)) of bismuth-based rhodium oxides ((Bi1-x,Pbx) 2Sr2Rh2Oy, x = 0 and 0.02, hereafter BSR and BPSR, respectively) were investigated. In comparison with Bi2Sr2Co2Oy (BSC) at 700°C, S and κ enhanced (increased S, 110 (BSR) and 105 μV K-1 (BPSR) from 85 μV K-1 (BSC) and decreased κ, 0.32 (BSR) and 0.50 W m-1 K-1 (BPSR) from 1.75 W m-1 K-1 (BSC)), whereas σ decreased (15 (BSR) and 31 S cm-1 (BPSR) from 70 S cm-1 (BSC)). BPSR reached the highest ZT value of 0.067 at 700°C, compared to those of 0.056 (BSR) and 0.027 (BSC).