Lai, Q., Zhu, S., Luo, X., Zou, M. and Huang, S. (2012) Ultraviolet-Visible Spectroscopy of Graphene Oxides. AIP Advances, 2, Article ID: 032146.
has been cited by the following article:
TITLE: Graphene Oxide/Multilayer-Graphene Synthesized from Electrochemically Exfoliated Graphite and Its Influence on Mechanical Behavior of Polyurethane Composites
AUTHORS: L. M. Flores-Vélez, O. Domínguez
KEYWORDS: Electrochemical Exfoliation, Graphene Oxide, Nanocomposites, Polyurethane
JOURNAL NAME: Materials Sciences and Applications, Vol.9 No.7, June 12, 2018
ABSTRACT: Graphene Oxide/Multilayer-Graphene (GO-MG) flakes were obtained using an electrochemically exfoliated graphite (GR) electrode from secondary steel-making industry performed in a two-electrode system using tungsten as the counter electrode and GR as the working electrode. The exfoliated GO-MG flakes were processed and incorporated in an elastomeric polyurethane (PU) matrix. The mechanical properties of the PU/GO-MG composites were evaluated and compared with equivalent composites made of PU/GR powder. From experimental data analysis it was concluded that GO-MG flakes were approximately composed of 67 wt% GO and 33 wt% MG. The number of layers in the graphene flakes was estimated to be between 2 and 5 sheets. PU showed a breaking stress of 570 kPa, while the PU/20wt% GR attained a maximum stress of 750 kPa as compared to PU/10wt% GO-MF composite exhibiting a breaking stress of 1060 kPa.