Li, X., Yang, Q., Hua, H., Chen, L., He, X., Hu, C. and Xi, Y. (2015) CdS/CdSe Core/Shell Nanowall Arrays for High Sensitive Photoelectrochemical Sensors. Journal of Alloys and Compounds, 630, 94-99.
https://doi.org/10.1016/j.jallcom.2015.01.020

has been cited by the following article:

• TITLE: A Novel Thermochemical Method for Fabrication and Theoretical Explanation of High Luminescent Mn-Doped CdS Nanoparticles

  AUTHORS: Mostafa Darvishi, Alireza Nikfarjam

  KEYWORDS: Mn:CdS Nanoparticle, Quantom Dot, Thermochemical Growth, Photoluminescence, UV-Vis Spectroscopy

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.6 No.3, March 19, 2018

  ABSTRACT: In this paper, fabrication and characterization of bare and doped CdS nanoparticles as well as investigating the luminescence properties of these particles as an important II-VI semiconductor are presented. A novel Thermochemical method was used for synthesis of these quantum dots. Thiols were used as the capping agent to prevent further growth during fabrication process. The application of TGA as a capping agent instead of TG was studied as a novel idea in this paper and was used practically in the synthesis of semiconductor nanoparticles. Using this process resulted in particles with sizes between 3 - 7 nm. Several samples were synthesized and characterized under various Mn ions doping ratio from 1:10 to 1:180, different temperatures from 40℃ to 96℃ and different pH values from 6 to 10. Synthesis of CdS nanoparticles with high Mn ions concentration resulted in luminescence decrement, while luminescence of nanoparticles was increased by decreasing Mn/Cd doping ratio until Mn:Cd = 1:180. The best fabrication temperature was obtained at 96℃ and the highest luminescence was observed at the pH value of 9. A theoretical explanation for the behavior of fabricated high luminescent quantum dots is presented based on the principles of quantum mechanics.