TITLE:
The Larger Grain and (111)-Orientation Planes of Poly-Ge Thin Film Grown on SiO2 Substrate by Al-Induced Crystallization
AUTHORS:
Shaoguang Dong, Junhuo Zhuang, Yaguang Zeng
KEYWORDS:
Al-Induced Crystallization, Poly-Ge Thin Film, Diffusion Control Interlayer, Lower Annealing Temperature
JOURNAL NAME:
Journal of Materials Science and Chemical Engineering,
Vol.6 No.2,
February
13,
2018
ABSTRACT: Al-induced crystallization yields the larger grain and (111)-orientation planes of poly-Ge thin film grown on SiO2 substrate, the (111)-orientation planes of poly-Ge thin film grown on SiO2 substrate are very important for the superior performance electronics and solar cells. We discussed the 50 nm thickness poly-Ge thin film grown on SiO2 substrate by Alinduced crystallization focusing on the lower annealing temperature and the diffusion control interlayer between Ge and Al thin film. The (111)-orientation planes ratio of poly-Ge thin film achieve as high as 90% by merging the lower annealing temperature (325℃) and the GeOx diffusion control interlayer. Moreover, we find the lack of defects on poly-Ge thin film surface and the larger average grains size of poly-Ge thin film over 12 μm were demonstrated by electron backscatter diffraction measurement. Our results turn on the feasibility of fabricating electronic and optical device with poly-Ge thin film grown on SiO2 substrate.