Z. Guo, J. Xiong, M. Yang, J. Wang, L. Sun, Y. Wu, J. Chen and S. Xiong, “Microstructure and Properties of Ti(C,N)-Mo2C-Fe Cermets,” International Journal of Refractory Metals & Hard Materials, Vol. 27, No. 4, 2009, pp. 781-783.

has been cited by the following article:

• TITLE: Facile Synthesis and Thermal Stability of Nanocrystalline Molybdenum Carbide

  AUTHORS: Youjian Chen, Hong Zhang, Jinfeng Zhang, Jianhua Ma, Hongnan Ye, Gaojin Qian, Yi Ye, Shuang Zhong

  KEYWORDS: Molybdenum Carbide, Chemical Synthesis, X-Ray Diffraction, Thermogravimetric Analysis

  JOURNAL NAME: Materials Sciences and Applications, Vol.2 No.9, September 20, 2011

  ABSTRACT: Nanocrystalline molybdenum carbide (Mo2C) was prepared via one simple route by the reaction of metallic magnesium powders with molybdenum trioxide and potassium acetate in an autoclave at the condition of 600℃ and 4 h. X-ray powder diffraction (XRD) pattern indicated that the product was hexagonal α-Mo2C, and the cell constant was a = 3.0091 Å, c = 4.7368 Å. Scanning electron microscopy (SEM) image showed that the sample consisted of particles with an average size of about 100 nm in diameter. The product was also studied by the thermogravimetric analysis (TGA). It had good thermal stability and oxidation resistance below 450℃ in air.