Von Fraunhofer, J.A. and Suchatlampong, C. (1975) The Surface Characteristics of Denture Base Polymers. Journal of Dentistry, 3, 105-109.
http://dx.doi.org/10.1016/0300-5712(75)90060-3

has been cited by the following article:

  • TITLE: Evaluation the Vickers Hardness of Denture Base Materials

    AUTHORS: Zeynep Yesil Duymus, Alper Ozdogan, Hamza Ulu, Ozlem Ozbayram

    KEYWORDS: Hardness, Denture Bases, Polyamide

    JOURNAL NAME: Open Journal of Stomatology, Vol.6 No.4, April 21, 2016

    ABSTRACT: The aim of this study was to evaluate the Vickers Hardness of four different denture base materials. Four different denture base materials were used in this study: Heat-cured pink acrylic resin, self-cured acrylic resin, heat-cured clear acrylic resin and polyamide denture base materials. To-tally 80 disc shaped samples which 2 mm thickness and 40 mm diameter were prepared. The samples were stored in distilled water after polished. Then, Vickers Hardness test was performed with TMTeck HV-1000B (200 gram at 15 second). The statistically analysis of obtained data was performed with use one-way analysis of variance test. The results showed that the highest Vickers Hardness value (18.57 HV) was identified in heat-cured (pink) acrylic resin, the lowest Vickers Hardness value (9.62 HV) was identified in polyamide denture base materials. The result of one-way analysis of variance test showed that there were statistically very highly significant differences between four denture base materials of Vickers Hardness (p