Montero, X., Galetz, M. and Schütze, M. (2011) A Single Step Process to Form In-Situ an Alumina Foam/Aluminide TBC System for Alloys in Extreme Environments at High Temperatures. Surf. Coating. Technol., 206, 1586-1594. http://dx.doi.org/10.1016/j.surfcoat.2011.05.052

has been cited by the following article:

• TITLE: Rheological Behaviour, Synthesis and Performance of Smart Thermal Barrier Coating Systems Based on Hollow Alumina

  AUTHORS: F. Pedraza, B. Rannou, G. Boissonnet, B. Bouchaud, Z. Maache-Rezzoug

  KEYWORDS: Slurry, Viscosity, Wetting, Thermal Barrier Coating, Thermal Conductivity, Oxidation

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.3 No.12, December 17, 2015

  ABSTRACT: The stability of three water-based slurries containing different loads of Al microparticles was measured by laser scattering. The slurries displayed a Newtonian behaviour and the evolution of viscosity over nine days was found to be constant. Ground surfaces of nickel were also wetted similarly irrespective of the Al content in the slurries (30, 40 or 50 wt%) thereby demonstrating that the 1/10 PVA/H2O water based slurries are adequate for spraying. After deposition and annealing of the as-sprayed coatings, a thermal barrier coating system was formed with a top coat of hollow alumina spheres, an intermediate thermally grown oxide and a bottom aluminized bond coat. The coating system is shown to display very low thermal conductivity and remarkable oxidation resistance at high temperatures.