Corrosion Inhibition of Mild Steel in Hydrochloric Acid by Tannins Rom Rhizophora Racemosa
Makanjuola Oki, Ebitei Charles, Collins Alaka, Tambari Kayode Oki
DOI: 10.4236/msa.2011.26079   PDF    HTML     9,228 Downloads   17,944 Views   Citations


Studies on the corrosion behaviour of mild steel electrodes in inhibited hydrochloric acid are described. Conventional weight loss measurements show that a maximum concentration of 140 ppm of tannin from Rhizophora racemosa is required to achieve 72% corrosion inhibition. Similar concentration of tannin: H3PO4 in ratio 1:1 gave 61% inhibition efficiency, whereas efficiency obtained for phosphoric acid as inhibitor in the same environment was 55%. Corrosion rates obtained over six hours of exposure in 1M HCl solution at inhibitor concentrations of 140 ppm are 2 mA/cm2, 2.4 mA/cm2, 2.6 mA/cm2 and 6 mA/cm2 for tannin, tannin/H3PO4 and H3PO4-inhibited and uninhibited specimens respectively. Natural atmospheric exposure studies revealed that specimens treated in H3PO4 resisted corrosion for three weeks, while tannin treated specimens suffered corrosion attack after one week of exposure tests.

Share and Cite:

Oki, M. , Charles, E. , Alaka, C. and Oki, T. (2011) Corrosion Inhibition of Mild Steel in Hydrochloric Acid by Tannins Rom Rhizophora Racemosa. Materials Sciences and Applications, 2, 592-595. doi: 10.4236/msa.2011.26079.

Conflicts of Interest

The authors declare no conflicts of interest.


[1] Gen-Ichiro Nonaka, “The isolation and structure elucidation of tannins,” Pure and Applied Chemistry, Vol. 6, No. 3, 1989, pp 357-360.
[2] A Veawab, P Totinwachwuthikul and A Chakma, “Investigation of low-toxic corrosion inhibitors for carbon dioxide separation process using aqueous MEA solvent,” Industrial & Engineering Chemistry Research, Vol. 40, 2001, pp. 4771-4777.
[3] B Raja and MG Sethuraman,”Inhibitive effect of black pepper extract on the sulphuric acid corrosion of mild steel,” Materials Letter, Vol. 62, 2008, pp. 113-116.
[4] A Bouyanzer, B Hammouti and L Majidi,, “Pennyroyal oil from Menthapulegium as corrosion inhibitor for steel in 1 M HCl,” Material Letters, vol. 60, 2006, pp. 2840- 2843.
[5] PC Okafor, EE Ebenso and UJ Ekpe, “?zadirachta indica extracts as corrosion inhibitor for mild steel in acid medium,” International Journal Electrochemical Science, Vol. 5, 2010, pp. 978-984.
[6] LR Chaulhan and G Gunasekaran, “Corrosion inhibition of mild steel by plant extract in dilute HCl Medium,” Corrosion Science, Vol. 49, 2007, pp. 1143-1161.
[7] Y. Abed, B. Hammouti, F. Touhami, A. Aouniti, S. Kertit, A. Mansri, and K. Elkacemi, “Poly (4-vinylpyrindine) (P4VP) as Corrosion Inhibitors of Armco Iron in Molar Sulphuric Acid Solution”,Bull. Electrochemistry, Vol. 17, 2001, pp. 105-108.
[8] EE Oguzie, “Studies on the inhibitive effects of Occimum viridis extracts on the acid corrosion ofmild steel, Material Chem. & Physics, Vol. 99, 2006, pp. 441-445.
[9] G Gunasekaran and LR Chaulhan,”Ecofiendly inhibitors for the inhibition of mild steel in phosphoric acid medium Electrochimica Acta, Vol. 49, 2004, pp. 4387- 4395.
[10] M. Abdallah, E. E. Helal, and A. S. Fouda, “Amino- Pyrimidine Derivatives as Inhibitors for Corrosion of 1018 Carbon Steel in Nitric Acid Solution”, Corrosion Science, Vol. 48, 2006, pp. 639-643.
[11] L S Moiseeva and Yu. Yu. Tur, “The role of combined corrosion inhibitor contact time in neutral aqueous media” Chemical and Petroleum Engineering, Vol. 59, No. 5-6, 2003, pp. 298-302.
[12] CM Ojinnaka, Tanner’s guide to Nigerian Plants, Leather Research Institute of Nigeria, 1988.
[13] E Chaieb, A Bouyanzer, B Hammouti and M Berrabh, “Limonene as green inhibitor for steel corrosion in HCl solutions,” Acta Phys. Chim. Sin, Vol. 25, No 7, 2009, pp. 254-258.
[14] U Rammelt, S Kohler and G Reinhard, “EIS characterization of the inhibition of mild steel corrosion with carboxylates in neutral aqueous solution” Electrochimica Acta, Vol. 53, No 23, 2008, pp. 6968-6972.
[15] E Bardal, Corrosion and Protection, Springer Verlag London Ltd., 2004.
[16] I Langmuir, “The adsorption of gases on plane surfaces of glass, mica and platinum” J. AmericanChemical Society, Vol. 39, 1947, pp. 1848-1856.
[17] A N Frumkin, “Electrocapillary curve of higher aliphatic acids and the state equation of the surface layer, “Z. Physical Chemistry, Vol. 116, 1925, pp. 466-470.

Copyright © 2024 by authors and Scientific Research Publishing Inc.

Creative Commons License

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.