Corrosion Behaviour of Modified HVOF Sprayed WC Based Cermet Coatings on Stainless Steel

DOI: 10.4236/jmmce.2011.1011076   PDF   HTML     6,895 Downloads   8,796 Views   Citations


WC based cermet coatings have been considered as alternative replacements to the more traditional hard chrome plating for improved surface properties of aircraft landing gear. While these coatings are used in engineering applications requiring superior hardness and improved wear resistance, little is known about the corrosion resistance. In this study, three WC based composite coatings were deposited onto ferritic stainless steel substrates using high velocity oxy fuel (HVOF) technology. Salt spray testing and potentiodynamic scanning studies in a saline environment were conducted on the coatings. Characterisation of the coating structure, composition and morphology, was carried out, prior to and after corrosion testing, using optical microscopy, scanning electron microscopy and EDX elemental analysis. The results showed that poor corrosion performance was exhibited by all three coatings. This was attributed to the high levels of porosity and the presence of micro-cracks within the coatings, resulting in attack of the substrate directly by the saline environment and possible galvanic coupling effects between the substrate and the coating. Dissolution and / or erosion of specific phases within the coating, resulting in the formation of micro-channels and increased number / size of voids may have accelerated corrosion of the system.

Share and Cite:

L. Ward, B. Hinton, D. Gerrard and K. Short, "Corrosion Behaviour of Modified HVOF Sprayed WC Based Cermet Coatings on Stainless Steel," Journal of Minerals and Materials Characterization and Engineering, Vol. 10 No. 11, 2011, pp. 989-1005. doi: 10.4236/jmmce.2011.1011076.

Conflicts of Interest

The authors declare no conflicts of interest.


[1] Nascimento, M. P., Souza, R.C., Miguel, I.M, Pigatin, W. L. and Voorwald, H. J. , 2001, “Effects of Tungsten Carbide Thermal Spray Coating by HP/HVOF and Hard Chromium Electroplating on AISI 4340 High Strength Steel”, Surface and Coatings Technology, Vol. 138, pp. 113-124.
[2] Natishan, P. M., Lawrence, S. H., Foster, R. L. and Sartwell, B. D., 2002, “Atmospheric Corrosion Study of Electrodeposited Hard Chromium and High-Velocity Oxygen-Fuel Thermal Spray Coatings”, Corrosion, Vol. 58, Ed. 2, pp. 119-123.
[3] Sartwell, B. D., 2000, “HVOF Thermal Spray Coatings Replace Hard Chrome: (High- Velocity Oxygen-Fuel)”, Advanced Materials and Processes, Vol. 156, Ed. 2, pp. 25-28.
[4] Perry, J. M., Neville A. and Hodgkiess, T., 2002, “A Comparison of the Corrosion Behaviour of WC-Co-Cr and WC-Co HVOF Thermally Sprayed Coatings by In Situ Atomic Force Microscopy (AFM)”, Journal of Thermal Spray Technology, Vol. 11, Ed. 4, pp. 536-541.
[5] Saenger, R., Martin, D. and Gabrielli, C., 2005, “Electrochemical Characterisation of Plasma Sprayed WC-Co Coatings by Impedance Techniques”, Surface and Coatings Technology, Vol. 194, pp. 335-343.
[6] Godoy, C., Lima, M. M., Castro, M. M. R. and Avelar–Batista, J. C., 2004, “Structural Changes in High Velocity Oxy – Fuel Thermally Sprayed WC-Co Coatings for Improved Corrosion Resistance”, Surface and Coatings Technology, Vol. 188-189, pp. 1-6.
[7] Lekatou, A., Regoutas, E. and Karantzalis, A. E., 2008, “Corrosion Behaviour of Cermet Based Coatings with a Bond Coat in 0.5 M H2SO4”, Corrosion Science, Vol. 50, pp. 3389-3400.
[8] Lekatou, A., Grois, D. and Grimanelis, D., 2008, “Corrosion Properties of HVOF Cermet Coatings with Bond Coats in an Aqueous Chloride Environment), Thin Solid Films, Vol. 516, pp. 5700-5705.
[9] Aw, P.K., Tan, A. L. K., Tan, T. P. and Qiu, J., 2008, “Corrosion Resistance of Tungsten Carbide Based Cermet Coatings Deposited by the High Velocity Oxy Fuel Spray Process”, Thin Solid Films, Vol. 516, pp. 5710-5715
[10] Kalish, H. S., 2009, Corrosion of Cemented Carbides, ASM Handbooks on-line, Vol. 13B, Corrosion, <>.
[11] Espallargas, N., Berget, J., Guilemany J. M., Benedetti, A. V. and Suegama, P. H., 2008, “Cr3 C2–NiCr and WC–Ni Thermal Spray Coatings as Alternatives to Hard Chromium for Erosion–Corrosion Resistance”, Surface & Coatings Technology, Vol. 202, pp. 1405–1417.
[12] Liu, Z., Cabrero, J., Niang, S. and Al-Taha, Z. Y, 2007, “Improving Corrosion and Wear Performance of HVOF-Sprayed Inconel 625 and WC-Inconel 625 Coatings by High Power Diode Laser Treatments”, Surface & Coatings Technology, Vol. 201, pp. 7149– 7158.
[13] Zhang, S. H., Yoon, J. H., Li, M. X., Cho, T. Y., Joo, Y. K. and Cho, J.Y., 2010, “Influence of CO2 Laser Heat Treatment on Surface Properties, Electrochemical and Tribological Performance of HVOF Sprayed WC–24%Cr3C2–6%Ni Coating”, Materials Chemistry and Physics, Vol. 119, pp. 458–464.
[14] Cho, J. E., Hwang, S. Y. and Kim, K.Y., 2006, “Corrosion Behaviour of Thermal Sprayed WC Cermet Coatings Having Various Metallic Binders in Strong Acidic Environments, Surface and Coatings Technology, Vol. 200, pp. 2653-2662.
[15] Koon, A. P., Hee, T. B., Taylor, M. , Western M. and Yip, J., 1999, Hard Chrome Replacements by HVOF Sprayed Coatings, SIMTech Technical Report (Pt/99/002/ST), Surface Technology Group, Process Technology Division.
[16] ASTM Committee, 1997, Standard Practice for Operating Salt Spray (Fog) Apparatus, ASTM Standard Designation: B117 – 97, ASTM, United States.
[17] Stokes, J., 2008, The Theory and Application of the HVOF Thermal Spray Process, Dublin City University, ISBN 1-87232-753-2, ISSN 1649-8232 <>.
[18] Warsono, R., 2004, Development of HVOF Sprayed Tungsten Carbide Nickel Coatings Deposited on Stainless Steel Substrates for Corrosion Protection in the Aerospace Environment, Internal Report, RMIT University, Melbourne.
[19] Celik E., Ozdemir, I., Avci, E. and Tsunekawa, Y., 2005, “Corrosion Behaviour of Plasma Sprayed Coatings”, Surface and Coatings Technology, Vol. 193 pp. 297-302.
[20] Jones, D.A., 1992, Principles and Prevention of Corrosion, Maxwell Macmillan International Publishing Group, Sydney.

comments powered by Disqus

Copyright © 2020 by authors and Scientific Research Publishing Inc.

Creative Commons License

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.