Author(s)

Thiago B. Fideles^1*, Hugo M. Lisboa², Renata G. Araújo¹, Luciane C. Trindade¹, Ítalo M. F. Pinheiro¹, Marcus V. L. Fook¹

¹Laboratory of Biomaterials Evaluation and Development-CERTBIO, Materials Engineering Department, Campina Grande Federal University, Campina Grande, Brazil.
¹Laboratory of Biomaterials Evaluation and Development-CERTBIO, Materials Engineering Department, Campina Grande Federal University, Campina Grande, Brazil.
²Entro de Tecnologia e Recursos Naturais, Food Engineering Department, Campina Grande Federal University, Campina Grande, Brazil.

Development of novel biomaterials and its practical application have been the subject of much research in the field of scaffolds for tissue engineering, providing the success of producing scaffolds biomaterials that facilitate tissue growth and provide structure support for cells. The design and production of scaffolds for tissue engineering is yet unable to completely reproduce the native tissue properties. Preferably, scaffolds would be made of biodegradable polymers whose properties are more similar to the ECM. Chitosan, which is the copolymer of D-glucosamine and N-acetyl-D-glucosamine, is an excellent material due to its versatile properties and is one of the widely studied polymers for tissue engineering application. The objective of the present work was to characterize mechanical and morphological chitosan scaffolds pro- duced by a particle aggregation method. Chitosan scaffolds were prepared throughout two steps: using the ionotropic gelation for macrosphere production and aggregation to produce the scaffolds. The chitosan scaffolds were characterized by Scanning Electron Microscopy (SEM) and Compression Tests. Through SEM results, was observed a three-dimensional structure, with 55% porosity and interconnectivity among pores. The pores were inhomogeneous and varied in the range of 40-262 μm. The mechanical characterization by compression tests showed a very elastic and easily conformable structure, since the stress required to deform the scaffold is lower. The cytotoxicity results proved that the produced has no toxicity effects and cell viability values were enclose in 80%.

Chitosan, Scaffolds, Aggregation Method, Biomedical Application

Fideles, T. , Lisboa, H. , Araújo, R. , Trindade, L. , Pinheiro, Í. and Fook, M. (2017) Mechanical and Morphological Characterization of Chitosan Scaffolds Produced by Particle Aggregation Method. Open Access Library Journal, 4, 1-12. doi: 10.4236/oalib.1104021.