The influence of solvent and the rate of addition of water on the characteristics of alumina-zirconia powders obtained by sol-gel method were investigated. The Al₂O₃-ZrO₂ powders (1:1 molar ratio) were prepared using aluminum tri-sec-butoxide and zirconium n-propoxide as precursors. Ethanol (EtOH), isopropanol (iPrOH) and isobutanol (iBuOH) were used as solvents. The Al₂O₃-ZrO₂ powders were characterized by nitrogen physisorption (S_BET), Fourier transformed infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscopy (SEM). Prepared oxides calcined at 700℃ showed high specific surface area (200 - 240 m2/g). Obtained results suggest that the homogeneity of the mixed oxides is favored by using a water addition rate of 0.06 and 0.10 mL/min with ethanol as solvent.

Alumina-Zirconia; Mixed Oxides; Sol Gel Method; Effect of Solvent; Water Addition Rate

J. Angel, A. Aguilera, I. Galindo, M. Martínez and T. Viveros, "Synthesis and Characterization of Alumina-Zirconia Powders Obtained by Sol-Gel Method: Effect of Solvent and Water Addition Rate," Materials Sciences and Applications, Vol. 3 No. 9, 2012, pp. 650-657. doi: 10.4236/msa.2012.39095.