Synthesis, structures, and properties of two new binuclear complexes based on carboxyl-substituted nitronyl nitroxide: [M2(NITpBA)4(H2O)2] (M = Zn and Cu)

Abstract

Two new binuclear complexes, [M2(μ-NITpBA)4(H2O)2] (M = Zn 1 and Cu 2) [where NIpBA = 2-(4-carboxyl-phenyl)-4,4,5,5-tetramethyl-4,5-dihydro-1H-imidazol-1-oxyl-3-oxide], were stylized and characterized. Magnetic susceptibility measurements revealed antiferromagnetic exchange interactions in two complexes.

Share and Cite:

Chen, J. , Zhang, Y. , Huang, K. , Huang, Q. and Wang, J. (2013) Synthesis, structures, and properties of two new binuclear complexes based on carboxyl-substituted nitronyl nitroxide: [M2(NITpBA)4(H2O)2] (M = Zn and Cu). Open Journal of Inorganic Chemistry, 3, 35-41. doi: 10.4236/ojic.2013.32005.

Two new binuclear complexes, [M2(μ-NITpBA)4(H2O)2] (M = Zn 1 and Cu 2) [where NIpBA = 2-(4-carboxyl-phenyl)-4,4,5,5-tetramethyl-4,5- dihydro-1H-imidazol-1-oxyl-3-oxide], were stylized and characterized. Magnetic susceptibility measurements revealed antiferromagnetic exchange interactions in the two complexes.

1. INTRODUCTION

The past decade has triggered fast-growing interests in nitronyl nitroxide radicals (NITR) as building blocks in the engineering of molecular-based magnet. The reasons are mainly that they are the most stable paramagnetic ligands, even in combination with metal ions where they can also act as bridging ligands [1]. Carboxylate bridges mediate exchange interactions between coordinated metal centres [2,3]. Metal complexes with bridging carboxylates as well as stable organic radical ligands are of considerable interest to the field of molecular magnetism [4]. In an effort to bring together the two areas of research, carboxyl-substituted nitronyl nitroxide, as an important anionic ligand, was deemed favorable for the realization in reactions with metal ions. To the best of our knowledge, to prepare transition metal complexes with nitronyl nitroxide-substituted carboxylate ligands, many investigations on the scope have been recently performed, but the related reports are very scarce [5,6]. The only structurally characterized transition metal compounds are 1D-chain systems in which two nitronyl nitroxides NITpBA are coordinated with two metal centers via one NO-group and a monodentate carboxylate group [7,8]. Miller’s group even reported on copper (II) compounds with NITpBA assumed to be in a bidentatebridging mode, but did not provide structural information on the related radical-metal compounds [9]. Rentschle’s group examined the reaction of NITpBAH with different metal salts, bases, and terminal capping coligands following with various methods but could not isolate any dimeric compounds. Ligand exchange reaction of NITpBAH with copper (II) acetate hydrate, however, leads to the desired system. Recrystallization from hot dimethylsulfoxide/methanol (2:1) leads to formation of small green-blue crystals Cu2(μ-NITpBA)4/H2O/dmso [10].

With the purpose of obtaining materials with unusual molecular high nuclearity spin clusters, we were interested in the preparation of carboxylate-bridged metal complexes with pendant organic radical substituents. In this paper, we present the simple synthesis and properties of two new metal–radical binuclear complexes [M2(μ- NITpBA)4(H2O)2] (M = Zn 1 and Cu 2).

2. EXPERIMENTAL

2.1. General

All reagents used in the synthesis were of analytical grade without further purification. 2-(4-carboxyl-phenyl)- 4,4,5,5-tetramethyl-4,5-dihydro-1H-imidazol-1-oxyl-3-oxide was prepared by the literature method [11]. Elemental analyses (C, H, and N) were carried out with a Perkin Elmer 240 C elemental analyzer. IR spectra were recorded from 400 to 4000 cm−1 on an Avatar-360 spectrophotometer using KBr pellets. Variable-temperature magnetic susceptibilities were measured with a MPMS- 7SQUID magnetometer at a magnetic field of 2000 G. Diamagnetic corrections were made with Pascal’s constants for all constituent atoms.

2.2. Synthesis of [M2(μ-NITpBA)4(H2O)2] (M = Zn 1 and Cu 2)

2.2.1. [Zn2(μ-NITpBA)4(H2O)2] 1

NITpBAH (0.4 mmol, 0.1076 g) was dissolved in 4 mL 0.2 M NaOH. The complex 1 was synthesized by the addition of NITpBA and ZnCl2 (0.2 mmol, 0.0275 g) to 30 mL of methanol-water. The mixture was stirred for 2 h and then filtered. The resulting blue filtrate was kept at room temperature for slow evaporation. After a few days, dark blue crystals of compound 1 suitable for X-ray analysis were obtained. Anal. Found: C, 53.12; H, 5.30; N, 8.61% Cacl. for C56 H68 N8 O18 Zn2 (1): C, 52.83; H, 5.39; N, 8.81%. IR (KBr disk): 1612 cm1 (), 1413 cm1 (), 1355 cm1 (nNO).

2.2.2. [Cu2(μ-NITpBA)4(H2O)2] 2

The complex 2 was prepared in a procedure similar to complex 1 except that ZnCl2 was replaced by CuCl2 Dark blue crystals were obtained expectedly. Anal. Found: C52.53; H, 5.16; N, 8.74% Cacl. for C56 H68 N8 O18 Cu2 (2): C, 52.98; H, 5.40; N, 8.83%. IR (KBr disk): 1610 cm1 (), 1407 cm1 (), 1350 cm1 (nNO).

2.2.3. X-Ray Data Collection and Structure Determination

X-ray diffraction intensities were collected on a Bruker Smart CCD diffractometer equipped with a graphitemonochromated Mo Κα radiation (= 0.71073 Å) by using a ω - φ scan technique at room temperature. Absor ption correction were applied using SADABS program [12]. The structures were solved by direct methods with SHELXS-97 program [13] and refined with SHELXS- 97[14] by full matrix least-squares technique on F2. All the non-hydrogen atoms were refined with anisotropic temperature para-meters. Hydrogen atoms of organic ligands were fixed in ideal positions. The relevant parameters of the crystal structures for complex 1 and 2 are listed in Table 1, and the selected bond lengths and bond angles are given in Tables 2 and 3, respectively.

Table 1. Crystal data and structure refinement for the two complexes 1 and 2.

Table 2. Selected bond distances (Å) and angles (˚) for the complex 1.

Symmetry codes: #1: x + 1, y, z + 2.

Table 3. Selected bond distances (Å) and angles (˚) for the complex 2.

Symmetry codes: #1: x, y + 2, z.

3. RESULTS AND DISCUSSION

3.1. Description of Crystal Structures

Crystal analysis show that compounds 1 and 2 are iso structural. They crystallize in the monoclinic system, P21/c (No.14) space group, which are different from that lecture [10] (triclinic system, space group P1). The asymmetric unit consists of one-half of a dimeric metal ion bridged by O-carboxyl from four nitronyl nitroxide. The two halves are related to each other through a center of inversion located in the middle of the M-M axis. The coordination geometry of Zn (II) and Cu (II) lies at the center of the distorted octahedral geometry formed by five oxygen atoms, which come from four equivalent nitroxide ligand, one water molecule, and the M-M distances of the neighboring metal atoms is [Zn1-Zn1(A) 2.9672 Å and Cu1-Cu1(A) 2.6457Å], which is rather short and may be regarded as the normal M-M bonding range[15,16]. Their molecular structures are depicted in Figures 1 and 2, respectively.

In complex 1, the C1-O1 and C1-O2 bonds from the same carboxylate group are equal to 1.246 and 1.249 Å, respectively, whereas the distance of C15-O5 and C15- O6 are of 1.244 and 1.254 Å, respectively. The Ph-COO bonds of 1.5093 Å are close to that reported in the literature [11]. The C-C bond lengths of the phenyl rings show no alternation and are located in the aromatic region ranging from 1.361 to 1.394 Å. The Zn-Owater distance of 1.964 Å is shorter than that of Zn-O whose oxygen atoms are from Ph-COO. Four oxygen atoms from Ph-COO of the nitroxide ligand compose the equatorial plane. The O5-Zn1-O6A angle in the equatorial plane is 158.99˚, and the O1-Zn1-O2A angle is equal to 158.59˚. The O1W-Zn1-Zn1A angle in the axial position is 171.23˚. The Zn (II) center is displaced by 0.324 Å from the basal O4-plane toward the axial oxygen atom from H2O. The fragment O4-N2-C8-N1-O3 is non-planar, and it forms a dihedral angle of 65.1˚ with the plane of the phenyl ring (C6-C5-C4). Conversely, the fragment O8- N4-C22-N3-O7 is nearly planar and forms a dihedral angle of 35.1˚ with the plane of the phenyl ring (C19- C18-C20). The IR spectrum shows the N-O stretching vibration of the NITpBA at 1355 cm−1 as well as the antisymmetric and the symmetric stretching mode of the caroxyl group at 1612 and 1413 cm1, respectively, in accordance with a bidentatebridging mode [10,17,18].

In complex 2, the Cu1-Cu1A distance is 2.6457 Å, which is a typical value for dimeric copper (II) carboxylate adducts [19,20]. The Cu-Owater distance of 2.121 Å is longer than that of Cu-O whose oxygen atoms come from Ph-COO. The Cu (II) core is displaced by 0.205 Å from the basal O4-plane toward the axial oxygen atom of the solvent. Mean deviation from base O4-plan

Figure 1. View of the moiety of the complex 1 [Zn2(NITpBA)4(H2O)2]. All hydrogen atoms are omitted for clarity.

Figure 2. View of the moiety of the complex 2 [Cu2(NITpBA)4(H2O)2]. All hydrogen atoms are omitted for clarity.

is 0.0009 Å. The fragment O4-N2-C8-N1-O3 is nonplanar, where the mean deviation from the plane is 0.0676 Å, and forms a dihedral angle of 86.1˚ with the plane of the phenyl ring (C4-C5-C6). The fragment O8-N4-C22-N3-O7 is nearly planar, and the plane for ms a dihedral angle of 36.4˚ with the phenyl ring (C19-C18-C20). The product shows IR absorptions at 13 50, 1407 and 1610 cm1, respectively.

3.2. Magnetic Properties

We have then examined the temperature dependences of

χMT and χM for complex 1 and 2 in order to analyze the exchange coupling in this six-spin system. Temperature dependences of the molar magnetic susceptibility for two complexes were measured in a temperature range of 2 K to 300 K at a magnetic field of 2000 G. The results are given in Figures 3 and 4, respectively.

For complex 1, the χMT at room temperature has a value of 1.535 emu∙K∙mol1, which is close to the expected value for uncoupled spins of S = 4/2 (1.5 emu∙ K∙mol−1) for two zinc centers and four nitronyl nitroxide radical-ligands. It was regarded as a tetra-radical system to evaluate the exchange coupling constants. The χMT value decreases slowly and reaches 1.43 emu∙K∙mol−1 at 100 K as the temperature is lowered, and subsequently decreases rapidly during further lowering of temperature. Based on the structural results, it undergoes a major magnetic interaction in the present system, in which the exchange interaction of NITpBA radicals through Zn (II) core exists [21]. The result indicates that a weak antiferromagnetic exchange interaction is predominant, which is agreement with literatures [22,23].

Figure 3. Temperature dependece of χM (○) and χMT () vs T for the complex 1

Figure 4. Temperature dependece of χM (○) and χMT () vs T for the complex 2

For complex 2, the χMT value at room temperature is 2.14 emu∙K∙mol1, which is significantly lower than that of the expected value for six uncoupled spins of S = 1/2 (2.25 emu∙K∙mol1) for two copper centers and four nitronyl nitroxide. The result indicates that a strong antiferromagnetic exchange interaction is predominant. The result is in accord with those reported [10,24].

4. CONCLUSION

Two new binuclear complexes formulae of [M2(μ- NITpBA)4(H2O)2] (M = Zn 1 and Cu 2) [where NITpBA =2-(4-carboxyl-phenyl)-4,4,5,5-tetramethyl-4,5-dihydro- 1H-imidazol-1-oxyl-3-oxide)] were synthesized and structurally characterized. The simple procedure of the NITpBAH with metal chloride yielded dimeric complexes 1 and 2. The temperature dependences of the magnetic susceptibility show dominant itram-olecular antiferromagnetic exchange interaction in complexes 1 and 2. According to the result of the complex 1, it demonstrates that the magnitude of the intramolecular magnetic exchange has little relationship with the crystal system and space group.

5. ACKNOWLEDGEMENTS

This work was supported by the National Natural Science Foundation of China (No. 21071006), the Natural Science Foundation of Henan Province (No. 102102 210457) and the Natural Science Foundation of the Henan Higher Education Institutions of China (No. 2010 B150001).

APPENDIX A. SUPPLEMENTARY DATA

Detailed crystallographic data in CIF format for the title complex are available from Cambridge Crystallographic Data Center (CCDC ID: 876210 and 876209). CIF deposits may now be made using our new online service: https://www.ccdc.cam.ac.uk/services/structure_deposit.

NOTES

Conflicts of Interest

The authors declare no conflicts of interest.

References

[1] Caneschi, A., Gatteschi, D., Sessoli, R. and Rey, P. (1989) Toward molecular magnets: The metal-radical approach. Accounts of Chemical Research, 22, 392-398. doi:10.1021/ar00167a004
[2] Boskovic, C., Pink, M., Huffman, J.C., Hendrickson, D.N. and Christou, G. (2001) Single-molecule magnets:? Ligand-induced core distortion and multiple Jahn-Teller isomerism in [Mn12O12(O2CMe)8(O2PPh2) 8(H2O)4]. Journal of the American Chemical Society, 123, 9914-9915. doi:10.1021/ja016341+
[3] Aubin, S.M.J., Sun, Z., Eppley, H.J., Rumberger, E.M., Guzei, I.A., Folting, K., Gantzel, P.K., Rheingold, A.L., Christou, G. and Hendrickson, D.N. (2001) Single-molecule magnets:? Jahn-Teller isomerism and the origin of two magnetization relaxation processes in Mn12 complexes. Inorganic Chemistry, 40, 2127-2146. doi:10.1021/ic000911+
[4] Kahn, O. (1993) Molecular magnetism. VCH, Weinheim.
[5] Inoue, K. and Iwamura, H. (1993) Magnetic properties of the crystals of p-(1-oxyl-3-oxido-4,4,5,5-tetramethyl-2-imidazolin-2-yl)benzoic acid and its alkali metal salts. Chemical Physics Letters, 207, 551-554. doi:10.1016/0009-2614(93)89046-K
[6] Ballester, G., Coronado, E., Galán-Mascarós, J.R., Giménez-Saiz, C., Nuez, A. and Romero, F.M. (2001) A new approach for the synthesis of magnetic materials based on nitroxide free radicals and inorganic coordination polymers. Polyhedron, 20, 1659-1662.
[7] Schi?dt, N.C., Fabrizi de Biani, F., Caneschi, A. and Gatteschi, D. (1996) Structure and magnetism of nickel (II) and manganese (II) complexes of a nitronyl nitroxide carboxylic acid. Inorganica Chimica Acta, 248, 139-146. doi:10.1016/0020-1693(95)04996-7
[8] Zhao, Q.H., Li, L.C., Jiang, Z.H., Liao, D.Z., Yan, S.P. and Fang, R.B. (2004) Synthesis and structure of a novel one-dimensional chain compound formed by copper (II) and nitronyl nitroxide radical. Journal of Chemical Crystallography, 34, 191-193. doi:10.1023/B:JOCC.0000021563.00957.85
[9] Del Sesto, R.E., Arif, A.M. and Miller, J.S. (2000) Copper (II) benzoate nitroxide dimers and chains: Structure and magnetic studies. Inorganic Chemistry, 39, 4894-4902. doi:10.1021/ic0007106
[10] Schatzschneider, U., Weyhermüller, T. and Rentschler, E. (2002) Copper complexes with mono nd bidentatebridging nitronyl nitroxide-substituted benzoate ligands. Inorganica Chimica Acta, 337, 122-130. doi:10.1016/S0020-1693(02)01103-9
[11] B?tz, C., Amann, P., Deiseroth, H.J. and Dulog, L. (1994) Die oxidation zweier neuer 1,3-dihydroxyimidazolidinedarstellung und Struktur von Nitronylnitroxid-Radikalen. Liebigs Annalen der Chemie, 7, 739-740. doi:10.1002/jlac.199419940715
[12] Sheldrick, G.M. (1997) SHELXS97, program for the solution of crystal structure. University of G?ttingen, G?ttingen.
[13] Sheldrick, G.M. (1997) SHELXS97, program for the refinement of crystal structure. University of G?ttingen, G?ttingen.
[14] Sheldrick, G.M. (1996) SADABS. University of G?ttingen, G?ttingen.
[15] Ohmura, T., Mori, W., Takei, T., Ikeda, T. and Maeda, A. (2005) Structure and magnetic behaviour of mononuclear and dinuclear Cu (II)/Zn (II) monocarboxylate-pyridine derivatives studied by crystal engineering. Materials Science-Poland, 23, 729-732.
[16] Chui, S.S.Y.S., Lo, M.F., Chammant, J.P.H., Orpen, A.G. and Williams, I.D. (1999) A chemically functionalizable nanoporous material [Cu3(TMA)2(H2O)3]n. Science, 283, 1148-1150. doi:10.1126/science.283.5405.1148
[17] Deacon, G.B. and Phillips, R.J. (1980) Relationships between the carbon-oxygen stretching frequencies of carboxylato complexes and the type of carboxylate coordination. Coordination Chemistry Reviews, 33, 227-250. doi:10.1016/S0010-8545(00)80455-5
[18] Alcock, N.W., Tracy, V.M. and Waddington, T.C. (1976) Acetates and acetato-complexes. Part 2. Spectroscopic studies. Journal of the Chemical Society, Dalton Transactions, 21, 2243-2245. doi:10.1039/dt9760002243
[19] Lewis, J., Lin, Y., Royston, L. and Thompson, R. (1965) The chemistry of polynuclear compounds. Part III. Magnetic properties of some carboxylic acid derivatives of copper (II). Journal of the Chemical Society, 17, 6464-6477. doi:10.1039/jr9650006464
[20] Lippard, S.J. and Doedens, R.J. (2007) Structure and metal-metal interactions in copper (II) carboxylate complexes. Progress in Inorganic Chemistry, 21, 209-231.
[21] Castro, I., Sletten, J., Calatayud, M.L., JuIve, M., Cano, J., Lloret, F. and Caneschi, A. (1995) Synthesis and magnetic properties of a tetranuclear copper (II) complex with a mu.-1,2,3,4-squarato coordination mode. Crystal structure of u-1,2,3,4-squarato)tetrakis [(tris(2-aminoethyl)amine)copper (II)] perchlorate. Inorganic Chemistry, 34, 4903-4909. doi:10.1021/ic00123a027
[22] Gao, D.Z., Zhao, W.W., Chen, Y.W. and Sun, Y.Q. (2009) Synthesis, crystal structure and magnetic behavior of a new Zn (II) nitronyl nitroxide complex [Zn(NIT3Py)2Cl2]. Chinese Journal of Inorganic Chemistry, 25, 738-741.
[23] Wang, S.P., Gao, D.Z., Liao, D.Z., Jiang. Z.H. and Yan, S.P. (2006) Two novel diamagnetic-metal coordination polymers of nitronyl nitroxide radical incorporating isophthalate bridges. Transition Metal Chemistry, 31, 214-219. doi:10.1007/s11243-005-6396-x
[24] Chen, J., Liao, D.Z., Jiang, Z.H. and Yan, S.P. (2005) A new heterospin complex from oxamide-bridged Cu (II) binuclear units and carboxyl-phenyl-substituted nitronyl nitroxide. Inorganic Chemistry Communications, 8, 564- 567. doi:10.1016/j.inoche.2005.02.015

Copyright © 2024 by authors and Scientific Research Publishing Inc.

Creative Commons License

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.