Ma, X.X., Zhao, X.G., Zhang, F., Shi, J.Y., Zhang, J. and Liang, W. (2007) Oxidation Kinetics of the Pack Siliconized TiAl-Based Alloy and Microstructure Evolution of the Coating. Intermetallics, 15, 1-8.
https://doi.org/10.1016/j.intermet.2005.11.038

has been cited by the following article:

• TITLE: Investigation of the Boriding Process of the Ti-Al Intermetallic Alloy GE48-2-2 Taking into Account the Probability of the Influence of the Substrate Modification

  AUTHORS: Dimitrios I. Zagkliveris, Georgios K. Triantafyllidis

  KEYWORDS: Titanium Aluminide, Boriding, Titanium Boride, Substrate Modification, Phase Analysis, X-Ray Diffraction

  JOURNAL NAME: Materials Sciences and Applications, Vol.9 No.11, October 26, 2018

  ABSTRACT: Boriding of the Ti-Al intermetallic GE48-2-2 at 1273 K for 10 hours was performed. In order to ensure that no any serious alteration occurred in the substrate, it was previously examined with X-Ray Diffractometry (XRD), after it has undergone an annealing process at the temperature of boronizing. Subsequently, we examined the coating with XRD and Scanning Electron Microscopy, in order to characterize its structure and morphology. A dense TiΒ2 layer, 10 - 15 μm thick, was formed, but also Cr2B3 and NbN, BN and some Ti-Al phases were detected. Efforts were undertaken to focus on influence of the substrate modification, towards the quality of the coating.