Catalyzed Trisodium Citrate as a Medium for Heavy Metals Treatment in Green-Lipped Mussels (Perna viridis) ()
1. Introduction
The green-lipped mussel, Perna viridis (Family: Mytilidae) is a local seafood delicacy. This bivalve is a filter feeder which feeds on phytoplankton, small zooplankton and other organic materials. This natural habitat may accumulate heavy metals over the years which enter the water and food cycles through a variety of chemical and geochemical processes [1-5]. Even low heavy metals content will possess toxic effect for human when intake is excessive [6].
Chelating agent is capable of forming a complex ring-like structure when comes in contact with a metal ion [7]. Studies have reported the application of chelating agents on heavy metals removal from human by deferasirox in chelation therapy, deferroxamine (DFO) and deferiprone (DFP) on fish, potassium butyl dithiophosphate (PBD) on wastewater, 1,3-benzenediamidoethanethiolate (BDET2−) on groundwater, citric acid on solid waste, oxalic and acetic acid on soil and sodium citrate on sediment [8-14]. Upon the catalyst application, studies have shown the enhancement toward the removal of polycyclic hydrocarbons (PAHs) in waste incinerator, the production of hydrogen from the supercritical water gasification (SCWG) and naphthenic acid removal in the acid solution model chemical reaction [15-17].
Biomonitoring the Perna viridis species have increased the awareness for health effect toward heavy metals contimination. Even though depuration process had been carried out to naturally purify transition metal contamination from the bivalves, only removed small amount of heavy metals while requires long time for process such as Hg (23.3%) in 20 days and Zn (40%), Pb (18.5%) and Cu (63.3%) in 24 days [18]. Hence, no commercially viable industrial technology was currently developed for the removal of the toxic elements. The purpose of the study is to remove heavy metals (As, Hg, Pb, Cd and Ni) from contaminated Perna viridis using trisoidum citrate with the addition of Ru/Mn (25:75)- Al2O3 catalyst. The result should compliment with the permissible limit set by the Malaysian Food Regulations (1985) and Commission Regulation of EU (2006).
2. Materials and Methods
2.1. Apparatus
As, Pb, Cd and Ni metals were analyzed through Inductive Coupled Plasma Mass Spectrometry, ICP-MS (Perkin Elmer ELAN 6100) while Hg determination was done by Mercury-Hydride Atomic Absorption Spectrometer, MHS-AAS (Perkin Elmer AAnalyst 400). The prepared catalyst was characterized using Nitrogen Absorption (Quantachrome Autosorb-1), Field Emission Scanning Electron Microscopy, X-ray Diffraction (Bruker AXS D8 Automatic Powder Diffractometer), and Energy Dispersive X-Ray (JEOL JSM-6701F). A pH meter (Hanna Instrument) was used to verify the pH of the citrate salt to achieve the desired pH.
2.2. Materials
All reagents used in the study were analytical grade and were used without any purification. All the solutions were prepared using deionized water obtained from the NANO pure water system. Samples were digested using HNO3 (Sigma Adrich, 65%). All the plastic and glassware were cleaned by soaking in diluted HNO3 (10%) and rinsed with distilled water prior to use. The element standard solutions used for calibration were produced by diluting a stock solution of 29 elements standard 3 (10 mg/L) supplied by Merck, Germany. The chelating agent used was trisodium citrate dihydrate, C6H5Na3O7∙2H2O (Sigma Adrich) while for the catalyst, the chemicals were Manganese (II) chloride (MERCK Eurolab), Ruthenium (III) chloride (MERCK Eurolab) and Aluminium Oxide (Sigma Adrich).
2.3. Catalyst Preparation
The catalyst was prepared by dissolved RuCl3 and MnCl2∙2H2O with 25:75 ratios in triply distilled water (2 mL). Then Al2O3 beds were 3 times impregnated in the catalyst solution for 15 minutes each. The catalyst was then washed with triply distilled water until no color changing of AgNO3 reagent. Later, it was aged at 80˚C for 24 hours before further calcined at 1000˚C for another 5 hours. All analysis was done in three series of replicates and the Perna viridis was rinsed with deionized water before the metals analysis.
2.4. Sampling
Perna viridis of average sizes of 9.0 cm - 11.5 cm and sea water samples were collected from each 4 sampling site along Pantai Lido-Pendas coastal area (Figure 1) from October 2010 to March 2011. These mussel samples were brought back to the laboratory and were stored at −10˚C until treatment while the sea water samples were preserved with 65% HNO3 (5mL/L) for metal analysis.
Figure 1. The sampling location from Pantai Lido-Pendas coastal area marked by (*).
2.5. Heavy Metals Removal
Treatment for the heavy metals removal in Perna viridis was conducted using trisodium citrate in the presence of Ru/Mn (25:75)-Al2O3 catalyst. The samples were put in sack and were soaked in the beaker (250 mL) that contains the chelating agents with stirring for 5 hour under the optimum treatment condition at 500 µg/g of dosage, at temperature of 35˚C ± 1˚C, at pH 6 - 7, for 5 hours of duration and in the presence of compressed air (flow rate 895.50 mL/min).
2.6. Metal Analysis
All prepared samples were digested using 65% of HNO3 (APHA 30 30 E). The digestion was done through partial reflux until clear solutions were obtained. After the digestion process, the samples were allowed to cool and filtered through a Whatman Grade 2 filter Paper and then diluted to 50 mL with deionized water. The prepared samples were then analysed for As, Pb, Cd and Ni using ICP-MS while MHS-AAS for Hg. The concentrations are presented in µg/g. To check for contamination and performance of the instrument, procedural blank and standard were analysed once for every ten samples.
3. Results
3.1. Heavy Metal Concentrations in Perna viridis
The initial concentrations of heavy metals (µg/g) in the Perna viridis from 4 sampling points are presented in Table 1. 5 batches of sampling were done from October 2010 to March 2011. For this study, the average of initial concentration for 5 samples (represent 5 sampling times) was used to calculate the percentage of heavy metals removed after the treatment. From Table 1, the averages of the studied heavy metals were above and exceed the permissible limit by Malaysian Food Regulations (1985) and Commission Regulation of EU (2006).
Table 1. Initial heavy metals concentration in Perna viridis with the permissible limit stated by Malaysia and EU.
3.2. Catalytic Treatment
The preliminary study on the catalytic treatment was done to identify the effect of Ru/Mn (25:75)-Al2O3 catalyst towards metals chelation of trisodium citrate. The heavy metals concentration with and without the presence of catalyst were determined. The results are illustrated in Figure 2. The result showed that with the presence of Ru/Mn (25:75)-Al2O3 catalyst, the percentage removal of the heavy metals increases up to 20% compared to none Ru/Mn (25:75)-Al2O3 catalyst in trisodium citrate medium. Hence, the catalyst was optimized to get the optimum catalytic activity.
3.3. Optimization of Catalyst
The calcination temperature of Ru/Mn(25:75)-Al2O3 catalyst were varied at 900˚C, 1000˚C and 1100˚C for 5 hours. The catalytic treatment activities are summarized in Figure 3. The result shows that calcination temperatures for 1000˚C gave higher catalytic activity for the catalyst on As, Pb and Hg when compared with calcination temperature at 900˚C and 1100˚C. Whereby, Cd and Ni followed the order 900˚C > 1000˚C > 1100˚C and 1100˚C > 1000˚C > 900˚C respectively. The percentage removal achieved at 1000˚C was As: 62.66%, Pb: 85.19%, Cd: 77.10%, Ni: 60.20% and Hg: 96.96%.
The optimization for the loading of the catalyst, Ru/Mn (25:75)-Al2O3 was varied by 1:1 (2.5 g catalyst in 250 mL sodium citrate) and 1:0.5 (1.25 g catalyst in 250 mL sodium citrate) ratios. The ratio used was based on volume of citrate salt to the weight of the catalyst. The result is illustrated in Figure 4.
Figure 4 clearly shows that the presence of catalyst even in a small quantity may enhance the removal rate of the heavy metal in Perna viridis. From the result, the dosage of the catalyst at 1.25 g was selected as both dosage of Ru/Mn(25:75)-Al2O3 in trisodium citrate did not gave much different in percentage removal of the heavy metals and only differed below 10%.
Figure 2. Percentage removal of heavy metals in Perna viridis in the presence of Ru/Mn (25:75)-Al2O3 catalyst at 900˚C calcination temperature in trisodium citrate (500 µL/L) medium with pH 7, at 35˚C ± 1˚C and for 5 hours.
Figure 3. Percentage removal of heavy metals removal for catalyzed trisodium citrate with Ru/Mn (25-75)-Al2O3 catalyst (1.25 g) at various calcination temperatures for 5 hours.
4. Characterization of Potential Catalyst
In this study, the characterization techniques of potential catalysts used were carried out by Nitrogen Absorption (NA), Electron Microscopy (FESEM), X-Ray Diffraction Analysis (XRD) and Field Emission Scanning Energy Dispersion X-Ray (EDX).
4.1. NA
The surface area and pore diameter of Ru/Mn(25:75)- Al2O3 catalyst were presented in Table 2. The results followed the order of 1000˚C > 1100˚C > 900˚C of calcination temperature.
At 1000˚C, the catalyst achieved the highest surface area (9.576 m2∙g−1) and highest average pore diameter (84.887 nm) compared to other calcination temperature. In general, bigger pore size creates bigger surface area of the catalyst, hence giving more active sites. However, higher calcination temperature leads to sintering effect and cause migration of particles size to grain in which the particles size increases and surface area decreases while low calcination temperature was unable to create high pore size on the surface of the catalyst which lead to low surface area. Even though the N2 adsorption-desorption isotherms analysis recognized that the catalyst to be Type IV and mesopores at all temperature, but the hysteresis loop as shown in Figure 5 indicates the narrower pore size of the catalyst at 1000˚C calcinations temperature.
It was proven as it gave higher uptake of nitrogen at high relative pressure and formation of the hysteresis loop at high relative pressure compared to calcination temperature at 900˚C and 1100˚C. Thus, high catalytic activity achieved at 1000˚C calcination temperature was due to the higher surface area with bigger and narrower pore size.
Figure 4. The percentage removal of heavy metals for different dosage of Ru/Mn (25:75)-Al2O3 catalyst calcined at 1000˚C in the trisodium citrate (500 µL/L) at neutral pH (pH 6 - 7), temperature of 30˚C - 35˚C with stirring for 5 hours.
Table 2. Surface area (SBET) and BJH desorption average pore diameter, d (nm) of Ru/Mn (25:75)-Al2O catalysts calcined at 900˚C, 1000˚C and 1100˚C for 5 hours.
(a)(b)(c)
Figure 5. Isotherm plots of Ru/Mn (25:75)-Al2O3 catalyst calcined at (a) 900˚C (b) 1000˚C and (c) 1100˚C for 5 hours.
4.2. XRD
Figure 6 shows the XRD pattern of Ru/Mn (25:75)- Al2O3 catalyst. All calcination temperature showed the presence of Al2O3 support in rhombohedral phase with RuO2 tetragonal phase and Mn2O3 hexagonal phase as the active site species. At 900˚C, Al2O3 (rhombohedral)
Figure 6. XRD Diffractograms of Ru/Mn (25:75)-Al2O3 catalysts calcined at (a) 900˚C (b) 1000˚C (b) and (c) 1100˚C for 5 hours.
was revealed at 2θ = 35.131˚ (I100), 43.329˚ (I96), 57.410˚ (I91), 25.550˚ (I68), 68.089 (I52), 52.475 (I47), 37.323˚ (I46) and 66.398 (I35); RuO2 (tetragonal) at 2θ = 28.076˚ (I100) and 54.965˚ (I39) while Mn2O3 (hexagonal) at 2θ = 36.466˚ (I100) and 61.872˚ (I39). For 1000˚C, Al2O3 (rhombohedral) was found at 2θ values of 35.126˚ (I100), 42.323˚ (I96), 57.462˚ (I91) 25.548˚ (I68), 68.217 (I52), 52.519 (I47), 37.776 (I46), 66.483 (I35) and 76.869 (I15); RuO2 (tetragonal) at 2θ = 28.076˚ (I100) and 54.454˚ (I39) while Mn2O3 (hexagonal) at 2θ = 36.316˚ (I100) and 61.211˚ (I50). Whereby, at 1100˚C, Al2O3 (rhombohedral) was determined at 2θ = 35.162˚ (I100), 43.350˚ (I96), 57.514˚ (I91) 25.574˚ (I68), 68.187(I52), 52.5459 (I47), 37.780 (I46), 66.493 (I35) and 76.901 (I15); RuO2 (tetragonal) at 2θ = 28.041˚ (I100) and 54.966˚ (I39) while Mn2O3 (hexagonal) at 2θ = 36.451˚ (I100) and 61.921˚ (I50).
The result revealed the amorphous state for the catalyst at 900˚C compared to crystalline state at 1000˚C and 1100˚C. The high peak intensity of RuO2 tetragonal at 1100˚C compared to 1000˚C calcination temperature will increased the crystallinity and may also decreased the surface area as indicated by NA analysis. Therefore, high catalytic activity at 1000˚C calcination temperature was mainly due the presence of crystalline phase at high surface area.
4.3. FESEM
The morphology of Ru/Mn(25:75)-Al2O3 catalysts were shown by FESEM micrographs in Figure 7. All the images show the formation of aggregation and agglomeration. Through FESEM mapping pattern in Figure 8, both Ru and Al species were identified to be in cluster pattern at 900˚C calcinations temperature while only Ru species was clustered for 1000˚C and 1100˚C calcinations temperature.
High catalytic activity for the catalyst at 1000˚C calcinations temperature was determined to be inhomogeneous nano particle sizes which vary from 41.4 nm to
(a)(b)(c)
Figure 7. FESEM micrographs of Ru/Mn (25:75)-Al2O3 catalyst calcined at (a) 900˚C, (b) 1000˚C and (c) 1100˚C for 5 hours (Magnification: 50,000×, Scale bar: 1 cm = 100 nm).
85.1 nm. Besides, the particles were shown to project out from the catalyst surface with high aggregation and was parallel with Ru mapping profile which shown to be more clustered at 1000˚C compared to 1100˚C. This morphology will increase the surface area of the catalyst and it was in agreement with the result obtained through NA analysis. Whereby, the surface area was lower at 900˚C as the particles with large number of square shape and uniform small spherical at diameter varies from 74.5 nm to 122.0 nm were more flatten on the catalyst surface. Meanwhile at 1100˚C, a capsule like shape and inhomogeneous small spherical shape with diameter sizes varied from 34.4 nm to 103.6 nm were presented. The particles were projected out from the catalyst surface but tend to more agglomerated which also lower the surface area.
(a)(b)(c)
Figure 8. FESEM Mapping pattern for Ru/Mn (25:75)- Al2O3 catalyst calcined at (a) 900˚C (b) 1000˚C and (c) 1100˚C for 5 hours. (Magnification: 20,000x, Scale bar: 1 cm = 2.0 µm).
4.4. EDX
The elements composition of Ru/Mn (25:75)-Al2O3 catalyst was shown in Table 3. The result showed the presence of Al, O, Mn and Ru elements on the catalyst at all studied calcination temperature. Al and O elements were attributed to the presence of Al2O3 as the catalyst support while both Mn and Ru elements exhibited as the active species of the catalyst which appeared as individual phases as Mn2O3 and RuO2 respectively as determined in XRD analysis. The percentage weight of Mn in the catalyst shows inversely proportional to the calcination temperature while the percentage weight of Ru in the catalyst followed the order of 1000˚C > 900˚C > 1100˚C of calcination temperature. Thus, indicates the high Ru aggregation formation as shown in the Ru mapping profile in FESEM analysis. High percentage of Mn at 900°C on the catalyst not affected the catalytic activity as it act only as a base for Ru active species on the Al2O3 support.
5. Proposed Mechanisms of the Catalytic Activity
The catalytic activity can be explained with the postulated reaction mechanism shown in Figure 9.
The reaction begins when trisodium citrate solution was been adsorbed on the surface of Ru/Mn (25:75)- Al2O3 catalyst (1). Then, the bonding between sodium, hydrogen and oxygen in the compound will be dissociated to form anion and cation (2). At the transition state, citrate ion will bond to the metal ion from the mussel while the sodium ion will bond with OH− from water molecule (3). Later, the production of metal citrate compound and NaOH will be released into the solution leaving the catalyst alone (4). The catalyst will then proceed their catalytic activity with adsorbing new trisodium citrate compound on their surface. Thus, a cyclic catalytic chelation proceeds again.
Figure 9. Proposed catalytic chelation cycle for the removal of metal ion from Perna viridis.
Table 3. EDX analysis of Ru/Mn (25:75)-Al2O3 catalyst calcined at 900˚C, 1000˚C and 1100˚C for 5 hours.
6. Conclusion
The obtained results proved that the catalytic treatment gave higher percentage removal of heavy metals in Perna viridis compared to treatment using only chelating agent. The Ru/Mn(25:75)-Al2O3 catalyst calcined at 1000˚C, was found to be the best catalyst to enhance the removal of heavy metals in Perna viridis. This catalyst possesses crystalline phase, surface area of 9.576 m2∙g−1 with average pore diameter of 84.887 nm, the isotherm of Type IV with hysteresis loop indicating the presence of mesopores, nano particle sizes which vary from 41.4 nm to 85.1 nm and high percentage composition of Ru and Mn on the catalyst with 4.15% and 9.09% respectively. Furthermore, the presence of RuO2 aggregation species on the catalyst surface suggested as active sites of the catalyst.
7. Acknowledgements
We thank Universiti Teknologi Malaysia for the financial support through Research University Grant (Vot No. 02J34).
NOTES