F. Czerwinski, H. Li, M. Megret, J. A. Szpunar, D. G. Clark and U. Erb, “The Evolution of Texture and Grain Size During Annealing of Nanocrystalline Ni-45% Fe Electrodeposits,” Scripta Materialia, Vol. 37, No. 12, 1997, pp. 1967-1972. doi:10.1016/S1359-6462(97)00390-4

has been cited by the following article:

• TITLE: Thermal Stability of Ni-Fe Alloy Foils Continuously Electrodeposited in a Fluorborate Bath

  AUTHORS: Wei-Su Chang, Yang Wei, Jun-Ming Guo, Feng-Jiao He

  KEYWORDS: Iron-Nickel Alloys; XRD; Electrodeposition; Fluorborate

  JOURNAL NAME: Open Journal of Metal, Vol.2 No.1, March 30, 2012

  ABSTRACT: Nanocrystalline Ni-Fe alloy foils were fabricated by using a continuous electrodeposition system, and then they were annealed at different temperatures ranging from room temperature to 650 ℃. A ductile-brittle-ductile evolution of these alloy foils was observed along with the increase of annealing temperature, and was affected by iron content. The first and second transformation took place at below 300 ℃ and over 500 ℃, respectively. Iron improved thermal stability of nanocrystalline Ni-Fe alloys. The XRD data indicated that for Ni100-xFex (x > 55) alloys bcc to fcc phase transformed at 300 ℃ and completely at 500℃.