Y. Kamegaya, K. Sasaki, M. Oguri, T. Asaki, H. Kobayashi and T. Mitamura, “Improved Durability of Iridium Oxide Coated Titanium Anode with Interlayers for Oxygen Evolution at High Current Densities,” Electrochimica Acta, Vol. 40, No. 7, May 1995, pp. 889-895. doi:10.1016/0013-4686(94)00339-3

has been cited by the following article:

• TITLE: An Investigation on the Electrochemical Characteristics of Ta2O5-IrO2 Anodes for the Application of Electrolysis Process

  AUTHORS: Joo-Yul Lee, Dae-Keun Kang, KyuHwan Lee, DoYon Chang

  KEYWORDS: Ta2O5-IrO2 Anode; Chloride Oxidation; Oxygen Evolution; Accelerated Life Test; Corrosion Resistance

  JOURNAL NAME: Materials Sciences and Applications, Vol.2 No.4, March 22, 2011

  ABSTRACT: The electrochemical characteristics of Ta2O5-IrO2 electrodes prepared from different chemical compositions and coating methods were observed by using cyclic voltammetry, potentiostatic polarization, galvanostatic polarization and scanning electron microscopy. The efficiency for chloride oxidation and oxygen evolution processes was not only influenced by the chemical composition but also by the surface morphology of the oxide electrode which was susceptible to the ratio of the two components and the coating method. Ta2O5(50)-IrO2(50) electrodes revealed the highest catalytic activity for the chloride ion oxidation and oxygen evolution reaction because they had the largest effective surface area. The durability of the oxide electrodes in the accelerated life tests was improved as the thickness of the oxide layer increased and the ratio of [IrO2] to [Ta2O5] approached 80/20.