J. A. Platt, A. Guzman, A. Zuccari, D. W. Thornburg, B. F. Rhodes, Y. Ossida, D. W. Thornburg, B. F. Rhodes, Y. Ossida and B. K. Moore, “Corrosion Behavior of 2205 Duplex Stainless Steel,” American Journal of Orthodontics and Dentofacial Orthopetics, Vol. 112, 1997, pp. 69-79.

has been cited by the following article:

• TITLE: Atmospheric Corrosion Studies of Ductile Iron and Austenitic Stainless Steel in an Extreme Marine Environment

  AUTHORS: Olasupo Ogundare, Babaniyi Babatope, Adelana Razaq Adetunji, Samuel Olugbenga Oloruntoba Olusunle

  KEYWORDS: Atmospheric Corrosion; Ductile IronL Austenitic Stainless Steel; Sodium Chloride And Microstructure

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.11 No.9, September 25, 2012

  ABSTRACT: This paper presents the corrosion characteristics and the accompanying changes in the microstructure of unalloyed duc-tile iron (DI) and austenitic stainless steel (ASS) in table salt medium representing an upper limit in an extreme marine environment. The individual corrosion rates of DI and ASS was evaluated for the maximum time period of 1200 hr. Using the immersion test technique, the corrosion rate of DI was evaluated and found to be four-orders of magnitude greater than that of ASS. The corrosion product morphologies of the DI showed that the nodular matrix was gradually covered up as immersion time progressed while the corrosion channels and volume of pits that initially formed in ASS respectively deepened and increased with increased exposure time. This work is important as a reference point for the quantification of the corrosion effectiveness of alloying DI. The microstructures of the corroded samples showed corro-sion initiation and gradual accumulation of corrosion products.