X. H. Wang, Z. D. Zou, S. Y. Qu and S. L. Song, “Microstruc-ture and Wear Properties of Fe-Based Hardfacing Coating Reinforced by TiC Particles,” Journal of Materials Processing Technology, Vol. 168, No. 1, 2005, pp. 89-94. doi:10.1016/j.jmatprotec.2004.11.001

has been cited by the following article:

• TITLE: Microstructure and Properties of Fe-Based Coating on Column Surface Formed by High Frequency Induction Cladding

  AUTHORS: Huilong Yang, Yufu Sun, Jingjie Shen, Sumeng Hu, Qing Zhao, Xiangcai Jia, Jingchao Zhang

  KEYWORDS: High Frequency Induction Cladding; Fe-Based Coating; Microstructure; Wear Resisitance

  JOURNAL NAME: Journal of Surface Engineered Materials and Advanced Technology, Vol.2 No.1, January 12, 2012

  ABSTRACT: The Fe-based coating was produced on the surface of the column substrate with a Al2O3 cylindrical sleeve by high frequency induction cladding, microstructure of the coating was investigated with scanning electron microscope (SEM), the crystal structure was characterized by X-ray diffractometer (XRD), the microhardness and wear resisitance of the coating were evaluated. The results show that a metallurgical bond between coating and substrate was obtained during the rapid solidification, the phases of the coating were composed of austenite and the eutectic of γ-Fe + (Cr, Fe)7(C, B)3. Compared with the substrate, the microhardness and wear resistance of the coating improved apparently, solid-solution strengthening and second-phase particle hardening led to these results.