Sjölander, E. and Seifeddine, S. (2010) The Heat Treatment of Al-Si-Cu-Mg Casting Alloys. Journal of Materials Processing Technology, 210, 1249-1259.
https://doi.org/10.1016/j.jmatprotec.2010.03.020

has been cited by the following article:

• TITLE: Effect of Mg Addition on the Structure and Properties of Al-4.5 Cu-3.4 Fe In-Situ Cast Composite

  AUTHORS: Nurul Afsar Chowdhury, Md. Arifur Rahman Khan, Sajib Aninda Dhar

  KEYWORDS: Metal Matrix Composites (MMCs), Intermetallic Compounds, Al-Cu-Fe Alloy, In-Situ Composite, Mg Addition

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.8 No.3, March 13, 2020

  ABSTRACT: Ternary Al-4.5 (wt%) Cu-3.4 (wt%) Fe in-situ composite was prepared at 1100°C by conventional casting method. However, this particular alloy contains larger needle-shaped intermetallics of Al3Fe phase. These exert adverse effect on the mechanical properties of the alloys. The larger shape and uneven orientation of the intermetallic were found to be responsible for the degradation of properties. The main purpose of this study was to modify the geometry of those needles by adding magnesium (Mg) as a fourth material. A series of alloys were prepared by adding 4, 6, 8, 10, wt% Mg in Al-4.5 (wt%) Cu-3.4 (wt%) Fe alloy. Microstructures were observed by optical microscopy. Mechanical properties like ultimate tensile strength, % elongation, % area reduction, hardness and wear test were determined. The study revealed that Mg transformed the needles of Al3Fe into globular shape which gave the alloys better mechanical properties.