Difficulties in the Use of Ground Bacterial Cellulose (BC) as Reinforcement of Polylactid Acid (PLA) Using Melt-Mixing and Extrusion Technologies ()
1. Introduction
Cellulose is the most abundant material in the world. About 1.5 trillion tons of cellulose grows every year [1-3]. The different sources are wood, straw, cotton or other plant based materials. Cellulose from these sources is widely used in different industries, such as the paper industry, the chemical industry (plastics like cellulose acetate), the textile industry (e.g. viscose fibers) [1] or even in the food industry (to improve texture and reduce energy) [4]. A very interesting field is the use of cellulose fibers to reinforce plastic materials like natural fiber reinforced polypropylene, which has been used in the automotive industry for many years, for example to produce lightweight and stiff door panels [5,6]. Next to plants cellulose can furthermore be microbial synthesized [1,7]. In that case the aerobic metabolic process is carried out by bacteria (in our case: Gluconacetobacter xylinum) at the interface between a nutrient medium and air. Bacterial cellulose fibers have dimensions in nanometerscale (diameter 50 - 250 nm; length of some µm) and build a fibrous network. Therefore, BC is mostly used in medical applications such as scaffolds or blood vessels or in cosmetic applications [1,8-10]. Its perfect mechanical properties (E-Modul: 15 - 35 GPa, tensile strength: 200 - 300 MPa) [1] and high aspect ratio makes BC suitable as reinforcing material. Different academic studies have already pointed out the potential of BC as a nano-scale and renewable reinforcing material. Using a transparent matrix material, good fiber adhesion and a homogenous dispersion of BC without agglomeration resulted in an optically transparent composite [11]. In other investigations BC was used to modify the surface of natural fibers like sisal [12]. Gea et al. tried to produce in-situ poly (vinyl alcohol) composites by adding a PVA solution directly to the growing medium. The addition of PVA to a BC network results in a decrease of the Young’s modulus but in an improved transparency [13]. BC in acrylic composites results in an improvement of the storage modulus, but Tg of the resin was hardly influenced. SEM also showed a strong interfacial adhesion between BC and acrylic resin [14]. BC is mostly used in a so-called “never-dried” state and in some cases also as dissolution to produce a composite. In our research we used dry pieces of BC and ground them into small particles; those can be added to thermoplastic matrices like PLA during industrial relevant processes like extrusion or compounding.
2. Materials and Methods
2.1. Materials
BC in lyophilized form was provided by the Forschungszentrum für Medizintechnik und Biotechnologie GmbH, Germany (fzmb). PLA (Ingeo® 3051D from NatureWorks LLC; D-content = 4 wt%) was supplied by Resinex, Germany.
2.2. Biocomposite Preparation
As a first step, the BC was ground twice in a cutting mill (SM 100 from Retsch, Germany) with a bottom sieve with trapezoid holes (final size 1.5 mm). The milled BC was dried at 105˚C for two hours before processing.
To provide stable feed and avoid segregation during extrusion PLA was ground under influence of liquid nitrogen. PLA was dried at 50˚C for four hours before processing.
For preparing compounds of PLA and BC as well as for the neat PLA a Haake PolyLab OS combined with Rheomex OS (Thermo Scientific) with 5 heating zones and a single-orificed nozzle was used.
Neat PLA was also prepared by extrusion at a temperature of 190˚C for all heating zones and a speed of 50 min–1 to ensure that all samples have the same thermal history. The melt strand was cooled down in a water bath and finally cut in a pelletizer with a cut length of 1 mm.
For preparing the PLA/BC-compounds both materials were dry pre-mixed in defined ratios, 5, 10 and 20 wt% respectively, and finally mixed by extrusion like the neat PLA with the same parameters, expect for the compound with 20 wt% BC which was compounded at a speed of 40 min–1.
After drying (at 50˚C till 0.5% moisture) the granules were pressed between two steel plates at 190˚C and a pressure of 750 N/cm2 for two minutes and then cooled for 10 min at constant pressure. The thickness of the plates was adjusted using a spacing frame with a thickness of 2 mm. The samples are named PLA for neat PLA and PLA/BC X/Y for a PLA composite with Y wt% BC (e.g. PLA/BC 95/5 for a PLA composite with 5 wt% BC).
For every material version one part was annealed additionally at 90˚C for two hours in a heating oven. The annealed samples are marked with a t (e.g. PLA/C 95/5- t).
2.3. Bio-Composite Characterization
2.3.1. DSC
Thermal properties (Tg, Tm, χc) were investigated by differential scanning calorimetry with a DSC822 from Mettler Toledo, under a nitrogen atmosphere. The first heating was from 20˚C to 200˚C, after cooling the material was heated in a second step to 350˚C. The heating and cooling rate was 10 K/min.
The crystallinity of PLA and PLA/BC composites was determined by
(1)
where χc is the crystallinity, w the weight fraction of PLLA in the composite, ΔHm is the melting enthalpy and ΔHc is the enthalphy of cold cristallization from DSC measurements and is the melting enthalpy for 100% PLLA [15].
2.3.2. Tensile Tests
Tensile test were carried out according to DIN EN ISO 527 using a Universal Testing Instrument 4466 from Instron with a 10 kN load cell. For measuring the Emodulus the test speed was 1 mm/min, elsewise 5 mm/min. The thickness of the specimen was 2 ± 0.1 mm, the width 20 ± 1 mm. The gauge length was 100 mm, while the extensometer length was 50 mm.
2.3.3. DMTA
Dynamic-mechanical analysis were carried out with a Dynamic Analyzer RDA II and Orchestrator Software, Rheosource Series II (Rheometric Scientific) using temperature sweep and torque mode. The specimens had a thickness between 2.0 to 2.3 mm and a width between 10.7 and 11.3 mm. The measuring length was (25.3 ± 0.4) mm. The dynamic storage and loss moduli were determined at a constant angular frequency of 6.28 rad/s as a function of temperature from –50˚C to 140˚C, a heating rate of 2 K/min and a deformation of 0.1%.
2.3.4. Microscopy
For microscopic investigations a microscope from ZEISS (Axiotech 100 HD) with a CCD camera (AVT Horn) was used. Ground BC was separated on a glass slide and examined at a magnification of 2.5.
For determining the size of the milled BC the software Axiovision (ZEISS) was used and a minimum of 400 particles were measured. As the ground BC particles did not show any regular shapes, it is difficult to define its length and width. Thus, we decided to measure the particle surface area to define the particle size.
Scanning electron microscopy (SEM) investigations were performed using a cross beam basis system (Auriga, ZEISS). Prior to SEM the samples were coated with Au.
3. Results and Discussion
3.1. Measuring Particle Size of Ground BC
There is a broad distribution of particle size of the ground BC as shown in Figure 1. As already mentioned and as it can be seen in Figure 1, the BC-particels have a complex shape making it difficult to determine length and width. Therefore, the surface area was determined also to compare with BC ground with other sieve size (not shown). The statistical analysis of the particle size results in an arithmetic average of 94,650 µm2 with a coefficient of variation of 93.2% that can be seen in the broad distribution. 50% of the particles have a smaller surface than 71,348 µm2, but because of the fibrous network and the folding of the particles the effective surface in the composite will be higher.
Surprisingly, there are no fibrils around the particles. The same was seen at SEM investigations (Figure 2). However, the fibrous network, for which BC is wellknown, can be observed at higher magnification, but only on the surface; deeper regions are impervious.
3.2. Influence of BC and Annealing on Thermal Properties
The DSC curves show that BC has an influence on the thermal properties of PLA, especially on its crystallization behavior (Figure 3). For the untreated sample no exothermic peak (cold crystallization) occurred at neat PLA but a significant exothermic peak for the composites PLA/BC 95/5 and PLA/BC 80/20 was noted. The exothermic peak appears at 123.20˚C for 5 wt% BC and at 117.06˚C for 20 wt% BC (see also Table 1). This means, BC particles act as a nucleating agent as it was also observed by other research groups using microfibrillated cellulose [16]. DSC curves of annealed PLA and PLA/BC composites do not show any exothermic peak. Thus, crystallization might be completed. Furthermore, BC does not influence significantly the glass transition temperature (Tg) or melting temperature (Tm) for the not annealed samples. After annealing only neat PLA shows a Tg. Comparing the Tg of untreated and annealed PLA shows an increase of 5 K for PLA-t. Furthermore the BC
Figure 1. Size distribution of ground BC.
Figure 2. Scanning electron micrographs of ground BC.
Figure 3. DSC plots of PLA and PLA/BC-composites: left: without annealing; right: with annealing.
Table 1. Thermal properties of annealed and untreated PLA and PLA/BC composites.
content influences the crystallinity of PLA. The incorporation of BC does not increase the crystallinity (χc). Improvements can be reached with heat treatment. Comparing not annealed and annealed samples with the same content of BC shows a significant improvement of χc in the annealed samples. This also indicates that BC particles act as a nucleating agent [16].
3.3. Influence of BC and Annealing on Tensile Properties
All samples show brittle failure behavior (Figure 4) and the elongation at break (εB) decreases with increasing BC-content (Table 2). Furthermore, εB of the annealed samples has also a lower value compared to untreated samples. The tests show a decrease of the tensile strength (σ) with increasing content of BC for both the untreated and annealed PLA/BC composites. This behavior is also known for natural fiber/polypropylene composites [17,18] and indicates a missing stress transfer between the BC and the matrix. At low fiber loadings the reinforcement acts more as an imperfection and leads to local stress peaks [18]. Except for PLA/BC 80/20 the tensile strength of untreated and annealed samples is on the same level, while for PLA/BC 80/20-t it is surprisingly significantly lower. As expected, the tensile stiffness (E-Modulus) increases with rising BC-content. As annealing leads to an increasing crystallinity it also improves the tensile modulus.
As Figure 5 shows the BC particles are uniformly dispersed in the PLA-matrix. With higher magnification SEM-pictures of the fracture surface show a weak fibermatrix-interface with gaps between the BC-particles and the matrix (Figure 4). Using a suitable coupling agent like maleic anhydride-grafted-PLA may improve the interface and consequently the mechanical strength and stiffness as it was already intensively shown for PP/ natural fiber composites [19,20].
Furthermore because of the contrariness of hydrophilic cellulose and more hydrophobic PLA the small interfibrillar spaces between single BC fibrils are not penetrated with the matrix. Hence, the high aspect ratio of the
(a)(b)
Figure 4. Stress-strain curves of (a): PLA/BC-composites and (b): annealed PLA/BC-composite.
Table 2. Tensile properties of annealed and untreated PLA and PLA/BC composites.
BC fibrils is not exploited. Only the surface of the BC particles interacts with the matrix. This leads to low mechanical improvements compared to other natural fiber composites or composites with nano-sized reinforcement.
3.4. Influence of BC and Annealing on Dynamic Mechanical Properties
Figure 6 shows that the incorporation of BC leads to a slight increase of the storage modulus (G’). For annealed