Relative Dielectric Permittivity Variations during Compaction as a Mean of Compaction Quality Control: Case Study on Laterite Samples from Senegal ()
1. Introduction
The context of rarefaction of high-quality building materials and the concern to reduce the costs of geotechnical infrastructure are constraints on the critical distances of search for laterites used as borrow materials in Senegal [1] . As a result, materials available within the optimum radius for use in road, dyke or embankment construction may require stabilization or improvement [2] . Compaction to improve their mechanical properties is almost always necessary [3] . To ensure proper in situ implementation and to check compliance between parameters determined from laboratory measurements and on-site implementation, compaction parameters must be controlled using different quality control procedures. There are several approaches to measuring in situ compaction. The available methods include the sand cone test, the membrane densitometer test or the gamma densimeter [4] . However, most common methods, such as the membrane densitometer, the compacted sand method, in addition to being tedious to implement, use an invasive and destructive process. Another major difficulty rises from the spatial limitation of the obtained results, which do not allow to account for heterogeneity in the implementation of materials [5] . The difficulties and limitations encountered in the use of direct methods for in situ compaction quality control have motivated our investigations of the possibility of using indirect methods, such as the geophysical radar method in compaction quality control. The radar provides information on the dielectric properties of materials [6] .
Several studies have established relationships between dielectric and geotechnical properties ( [7] - [12] ). Also, unlike in situ compaction assessment direct methods, the dielectric properties of materials are easy and quick to determine ( [13] [14] [15] ). As a result, the measurement of in situ dielectric properties should make it possible to deduce compaction parameters in order to facilitate and optimize quality control.
The purpose of this study is to search, in the context of laterite materials commonly used in construction, to determine the existing relationship between the dielectric properties measured by radar method and the electrical properties calculated from the compaction parameters. Establishing such a relationship is of high importance to improve the implementation and effectiveness of in situ compaction quality control of geotechnical infrastructures.
2. Material and Method
On laterite soil samples from the quarry of Diack, in the region of Thies in Senegal, we studied the variation of dry density
as a function of the mass water content w. To proceed, the material is compacted at different water contents, in accordance with the modified Proctor test NF P 94-093 [16] .
First, the mass water content w is determined by the relation:
(1)
With
the mass of the wet sample and
the mass of the dried sample.
The dried density
is determined, taking into account the actual volume of the used mold with the relation:
(2)
with
the wet density of the sample.
with
the specific density of the wet material
and
, the specific density of water.
The volumetric water content
is given by the relation:
with
the dried density of the sample,
the specific density of water et w the mass water content.
At each stage of compaction, the porosity
of the material is determined by the relation:
At the same time, at each stage of compaction, with a given water content and dried density, the dielectric permittivity was measured using the Ground Penetrating Radar (GPR) method or Radar [17] .
The principle of GPR is based on the emission and reception of electromagnetic waves passing through the investigated material. Waves are sent as impulses in the time domain [18] .
The propagation of radar waves in a medium depends on the dielectric properties, and more on the permittivity of the material. The velocity v of radar waves through a medium is given by the relation:
(3)
With
corresponding to the radar wave velocity through the air.
is the relative permittivity of the material and corresponds to the ratio of effective permittivity
and air permittivity
taken as reference.
The device used for permittivity measurements by radar method includes a GSSI SIR 3000 acquisition unit connected to a 1.6 GHz GSSI central frequency antenna (Figure 1).
Radar data acquisition for permittivity determination was carried out using a specially designed device (see Figure 2), facilitating the passage of the monostatic radar antenna, mounted on a cart model 319, over the compacted sample still in the mold.
The determination of the permittivity of laterite soil samples by the GPR method is based on the two-way travel time method [19] . In our case, this method consists of pointing the travel time of the radar wave, between the top and the base of the mold, clearly visible on the radar profile and marked by reflections due to the permittivity contrast between the air and the surface of the sample on the one hand, and between the base of the sample and the mold support on the other hand. From the travel time, the speed v of the radar signal is written.
Figure 1. SIR3000 radar acquisition system with 1.6 GHz antenna and accessories.
Figure 2. Data acquisition device, showing the laterite soil sample in the Proctor mold and the 1.6 GHz antenna.
(4)
t is the two-way travel time, and d is the length of the wave ray inside the mold. In our conditions,
.
If we pose equations 3 = 4, we can deduce the relative permittivity
with the relation:
(5)
The picking of radar signal travel time inside the sample was performed on each profile under Reflex2DQuick software [20] .
In order to determine the experimental dielectric properties from the compaction data for comparison with the permittivity obtained by radar measurements, we used the Topp law [9] and the Lichteneker-Rother model [7] .
Topp’s law is an empirical law linking volumetric water to relative permittivity
. It was derived from the correlation of water content measurements and dielectric constants on various laboratory samples [9] . Topp’s law states that:
(6)
is the relative permittivity and
is the volumetric water content.
Topp’s law is valid for frequencies ranging from 10 MHz to 1 GHz and water contents from 5% to 17% [21] . However, it is inappropriate for clayey and organic matter rich soils. At higher frequencies and near-water saturation (40%), Topp’s law may overestimate relative permittivity [22] .
Other authors ( [10] [23] ) have suggested empirical relationships that also allow volumetric water content to be recovered from relative permittivity. They are expressed as follows:
(7)
(8)
The Lichteneker-Rother model also referred to as Complex Refractive Index Model—CRIM [7] is a volumetric model in which the material is considered as a medium consisting essentially of solid grains of the same nature, voids and water. The CRIM model is valid for medium with low salinity and low dielectric loss. It allows to connect the permittivity to the porosity and the water content by the relation:
(9)
is volumetric water content
and
is the porosity. We consider the relative permittivity of water
.
As stated by Knoll [24] and Robinson et al., [25] , we can assume for the solid particles fraction of the sample a permittivity
The main steps of the approach used in this study, including the compaction of the laterite soil material, the determination of the compaction parameters, the determination of the relative permittivity using both empirical and physical laws and by the radar method, are summarized in the diagram below (Figure 3).
3. Results and Discussion
The compaction parameters, determined during the modified Proctor test, namely the mass water content w, the wet density
, the dried density
, the volumetric water content
and the porosity
, are shown in the table below (Table 1).
The Proctor curve, corresponding to the variation of the dried density as a function of the mass water content, is shown in Figure 4 below.
The Proctor curve (Figure 4) shows that the optimum water content
and the optimum dried density
are respectively 16.8% and 1.83 g/cm3.
Figure 5 shows the radar facies corresponding to the tested sample and the
Figure 3. Flow diagram of the steps of the experimental approach of this study.
Table 1. Evolution of compaction parameters during the modified Proctor test.
Figure 4. Proctor curve of the laterite soil sample.
limits of the mold. In the following steps, only the part of the profile around the mold is shown. The radar profiles obtained at each stage of compaction for each water content and corresponding dried density are shown in Figure 6.
The dielectric permittivity’s determined from the Topp law, the CRIM model and the radar method are summarized in the table below (Table 2).
Figure 5. Overview of a radar profile showing the radar facies corresponding to the tested sample and the limits of the mold (see annotations).
Figure 6. Radar profiles obtained at the various stages of the compaction.
Table 2. Summary of the obtained relative dielectric permittivity (dimensionless).
is the permittivity from Topp law,
is the permittivity from CRIM law and
is the permittivity determined from radar method.
Several correlations were performed to understand the relationship between the various parameters determined during compaction (Table 1) and the obtained relative permittivity (Table 2).
In a first step, we correlated the density and mass water contents with the different permittivities (Figure 7). In a second step, wet and dried densities were correlated with permittivities (Figure 8). Finally, the porosity is correlated with the permittivities (Figure 9).
The correlation between permittivity and water content (Figure 7) shows that the permittivity of the sample increases linearly with the water content. This increase is valid for all three types of permittivity. The correlation coefficients are between 95% and 97% for the mass water content, and between 98% and 99% for the volumetric water content with a 99% confidence interval verified for a number of samples n = 4.
The linearity of the relation can be explained by the fact that, when the water content increases, the air previously contained in the voids of the material is gradually replaced by water. Thus, the permittivity of the material evolves towards the permittivity of the water which corresponds to the maximum permittivity (
). Moreover, in the presence of water, the polarization capacity of the medium increases due to the polarity of the water molecules, resulting in dielectric loss [26] . The better correlation with the volumetric water content compared to the mass water content is due to the fact that, the mass water content only takes into account the free water that can be removed by drying in the oven [27] .
The correlation of permittivity with density (Figure 8) gives a bell-shaped curve. At low relative permittivity, the density increases with the permittivity until we reach the optimal density
. Beyond, the density decreases with the permittivity. This curve allows us to determine the permittivity at the optimum which is respectively 13.39, 17.77 et 18.77 for
,
and
.
Even if the optimum permittivity varies according to the method of determination, the shape of the curve remains substantially the same, with a left or right
Figure 7. Correlation between the permittivity obtained by different methods (Topp formula, CRIM model and GPR) with the mass water content and volumetric water content.
Figure 8. Correlation between the permittivity obtained by different methods (Topp formula, CRIM model and GPR) with the wet density and the dried density.
Figure 9. Correlation between the permittivity obtained by different methods (Topp formula, CRIM model and GPR) with the porosity.
offset. Also, the shape of the permittivity/density curve, identical to that of the Proctor curve (dry density as a function of mass water content) means that, like the water content, permittivity could indeed serve as an indicator of compaction. This is substantiated by the linear correlation between permittivity and water content (see Figure 7).
The correlation of the porosity with the permittivity (Figure 9) shows an inverted bell-shaped curve, with a minimal porosity corresponding to the optimal permittivity. The decrease in porosity at the optimum is related to grain tightening. Beyond the optimum, the increase in porosity can be explained by the cracking and breaking of grains related to compaction energy ( [28] [29] ).
The various correlations show that, even if the value of the permittivity varies from one determination method to another, the shape of the curve remains unchanged. The maximum permittivities are obtained with the CRIM model, followed by the Topp law and the GPR method.
These differences in permittivity are explained by the fact that, these different methods evaluate permittivity by focusing on different parameters. The very high values observed with the CRIM model could be explained by the fact that this model considers the sample as a composite material with a solid fraction consisting of the grains, a liquid fraction consisting of water and a gaseous fraction filling the voids of the medium. It considers that the solid phase consists of grains of the same mineralogic nature, which is not the case for laterite. Indeed, many studies have shown that, apart from the iron oxide rich gravelly, laterite may contain a more or less large clay fraction or other weathering minerals or parent rock residues [30] .
The permittivity obtained from Topp model could have been influenced by the frequency of the antenna, which is 1.6 GHz while the model was established from measurements with a frequency band of 10 MHz to 1 GHz. This confirms the decrease in permittivity with the decreasing frequency suggested by several authors ( [31] [32] [33] ). In addition, the metallic walls of the Proctor mold may cause interference due to the total reflection of radar waves on metallic objects [34] .
Nevertheless, despite the lower permittivities obtained by GPR measurements compared to the those obtained from the Topp formula and the CRIM model, the similar shape of the curves ensures the reproducibility of the permittivity/compaction properties relation. In addition, the curves show that the optimal permittivity can be used to identify the optimum dry density, corresponding to an optimum water content and an optimum porosity.
By regression, it is possible to establish the law linking the permeability, measured by GPR method to the dry density.
The relationship between permittivity and dry density is expressed as:
4. Conclusions
The study of the relationship between the dielectric permittivity according to the Topp formula, the CRIM model and the geophysical radar method made it possible to understand its relationship with the compaction parameters. Due to the good correlation between water content and permittivity, the trend of the compaction curve can be reproduced by the curve of the dry density variation as a function of the permittivity, which makes it possible to determine a permittivity at the optimum Proctor.
Even if the value of the permittivity changes depending on the method of determination, the fact remains that, for the different methods, it remains possible to determine the optimal permittivity linked to the optimal density.
The resemblance of the gaits allows seeing the correspondence between the permittivity and the optimal dry density used in the quality control of compaction.
During the in-situ quality control of compaction, investigations using radar method should make it possible to evaluate the optimal permittivity as a proxy for monitoring the optimal compaction.
In order to generalize the use of this procedure in the compaction quality control, it should be necessary to carry out a parametric study on various laterite samples at various frequencies with various water content. It should also be necessary to tighten the water content steps to improve the accuracy on the Proctor curve and its equivalence with the Proctor curve from GPR method.