K. Kishida, Y. Takahama and H. Inui, “Deformation Twinning in Single Crystals of a D019 Compound with an Off-Stoichiometric Composition (Ti-36.5 at.%Al),” Acta Materialia, Vol. 52, No. 16, 2004, pp. 4941-4952. doi:10.1016/j.actamat.2004.06.051

has been cited by the following article:

• TITLE: Structure Transformations in the Polycrystalline (Ti,Nb)3Al Alloy under Shock-Wave Loading

  AUTHORS: Nataliya V. Kazantseva, Evgenii V. Shorokhov

  KEYWORDS: Ti3Al, Phase Transformation, Shock Waves

  JOURNAL NAME: Journal of Modern Physics, Vol.2 No.10, October 19, 2011

  ABSTRACT: Structure transformations in the two-phase (Ti, Nb)3Al alloy, induced by shock-wave loading, were studied. The samples were subjected to an impact of a steel plate. The maximum pressure on the samples’ surfaces was 100 GPa, while the maximum temperature was 573 K. The β0→α2 phase transformation occurred during strong deformations. High temperature rectilinear dislocations (such types of dislocations usually could arise at 1073 K) with the c-component, which occasionally formed slip bands, were located at the α2-phase grains after the shock. The deformation α2-phase twins were not observed.