Imaz, N., Diez, J.A., Pellicer, E., Sort, J., Grande, H. and Garcia-Lecina, E. (2017) Thermal Treatment Effect on the Mechanical, Tribological and Corrosion Properties of Ni-W Alloy Obtained by Direct and Pulse Plating Electrodeposition. Transactions of the Institute of Metal Finishing, 95, 31-38.
https://doi.org/10.1080/00202967.2017.1260885

has been cited by the following article:

• TITLE: The Hardness and Corrosion Properties of Trivalent Chromium Hard Chromium

  AUTHORS: Jiazhu Li, Yanjing Li, Xiaohua Tian, Ling Zou, Xing Zhao, Sanfeng Wang, Shenggang Wang

  KEYWORDS: Corrosion Resistance, Nanometer Materials, Hard Chromium, Trivalent Chromium

  JOURNAL NAME: Materials Sciences and Applications, Vol.8 No.13, December 11, 2017

  ABSTRACT: The formulation of hard chromium plating from trivalent chromium electrolyte and its related process have been intensively studied in this work. Through optimized conditions, the coating hardness can achieve more than HV0.1900 without any treatment and HV0.11700 after heat treatment for five minutes at 300°C, and the thickness of hard chromium coating was about 100 μm. The hard chromium coatings show good adhesion on the carbon steel and low alloy structural steel. The corrosion resistance of hard chromium coatings was enhanced by the adding nanometer materials into trivalent chromium plating coatings. More than 120 hours salt spray corrosion resistance can be achieved with 40 to 50 microns thickness of trivalent chromium plating coatings.