Study on Various Compositions of Polyvinyl Alcohol and Starch Blends by Cross-Linking with Glyoxal ()
1. Introduction
Starch is a relatively inexpensive and renewable product that can be obtained from multiple plant sources and that has been extensively used as wet end additive, coating binder, sizing agent, adhesive, and textile size [1] [2] . However, its bonding capacity is not strong enough to glue wood [3] [4] [5] [6] [7] . A few studies have been conducted on the potential of utilizing starch as wood adhesive. Recent studies have focused on formaldehyde-free wood adhesives, which are obtained through the reaction between a cross-linker and a blend of starch with other polymers, such as starch/polyvinyl alcohol [8] , starch/tannin [9] [10] [11] and starch/isocyanates [12] . However, such wood adhesives cannot be used at room temperature because the required curing temperature is usually over 100˚C [13] . Many efforts have been exerted to develop starch-based polymers as alternatives of petroleum-based polymers [14] [15] [16] .
Polyvinyl alcohol (PVA) is water soluble polymers, strong, durable and biodegradable. It possesses high crystalline structure [17] . Physical and chemical properties of PVA depend on the synthetics condition and degree of hydrolysis of the polymer [18] [19] [20] [21] [22] . To improve the properties, researchers have blended starch with other biodegradable polymers such as methyl cellulose and hydroxyl propylmethyl cellulose, polyhydroxyalkanoates poly lactic acid (PLA) and PVA. PVA contains secondary hydroxyl group that easily forms hydrogen bonds with starch. There is a wide variety of crosslinking agents for PVA, such as maleic acid, formaldehyde, and glyoxal [23] .
PVA crosslinked with dialdehydes is one of the most commonly used techniques. It is well known that hydroxyl groups from PVA react with aldehydes via formation of acetal bonds. When dialdehyde is used, such as glyoxal or glyoxal, crosslinking reactions of PVA can be conducted under mild conditions [24] [25] [26] . Dialdehydes are the multifunctional reagents that cross-link starch by reacting with the hydroxyl groups of starch and intro-duce intermolecular bridges between the polysaccharides chains.
In this paper, the effects of various factors such as increasing starch content, increasing amount of glyoxal, on the performance properties like tensile strength, pencil hardness and thermal properties were studied.
2. Experimental
2.1. Materials
PVA (containing 86.5% to 89% degree of hydrolysis) were obtained from Kuraray Cooperative Limited, India. Maize starch containing 25% - 30% of amylose content was obtained from Sanstar Ltd. Glyoxal (∼40% content in water) was purchased from Sigma-Aldrich. Deionized water was used as the solvent in all experiments. Maize starch was dried to remove moisture.
2.2. Preparation Method
First, Maize starch and PVA blends were mixed in water and poured into a kettle. Second, the kettle was closed and was sealed to make it air tight. Third, the seal tight kettle was heated to 60˚C temperature while mixing the sample at 175 rpm. The cross-linker was later added as per the amount given in Table 1. Subsequently, the temperature was raised to 90˚C - 95˚C keeping the constant stirring 2 hrs. After completion of cross-linking the solution was brought to room temperature for further analysis.
2.3. Casting of Films
A bar applicator was used for casting films of 1000 µm. The films were then kept
Table 1. Preparation of various adhesive compositions with glyoxal.
at room temperature for curing for 24 hrs.
Formulation 1:
For formulation 1, the PVA/S blend was kept constant at 25/5 with composition of glyoxal varied from 0 to 1.5 (Table 1).
Formulation 2:
For formulation 1, the PVA/S blend was kept constant at 20/10 with composition of glyoxal varied from 0 to 1.5 (Table 1).
3. Characterization and Testing
3.1. Viscosity
A Brookfield DV1 Viscometer was used to measure the viscosities of the formulations 1 and 2. All readings were taken at 30˚C.
3.2. Fourier Transform Infra-Red Spectroscopy (FTIR)
Infrared spectra of crosslinked PVA and starch blends were measured on a PerkinElmer FTIR spectrum 100 instrument. Thin films were made from crosslinked blends prior to analysis.
3.3. Differential Scanning Calorimetry (DSC)
A Perkin Elmer instrument Q100 DSC has been used for estimating the glass transition temperature (Tg).
3.4. Pencil Hardness Test
Testing method employed to calculate pencil hardness was ASTM D 3363.
3.5. Ultimate Stress of Films
ATinus Olsen 5ST instrument was used for determining the ultimate stress of the films.
3.6. Tensile Strength
A Tinus Olsen H25KT instrument has been used for calculating the tensile strength. Two pieces of steamed beech wood were taken for determining the tensile strength. The adhesive was applied on one end (2.5 cm × 2.5 cm) of the two pieces and was held together for 2 and 24 hrs at room temperature. The cured wood samples were then tested using a controlled speed of 10 mm/min to obtain the tensile strength values.
4. Results and Discussion
The hydroxyl groups of PVA and starch react with glyoxal via formation of acetal bonds hence crosslinking could take place [25] . Since, the glyoxal at 90˚C reacts with the hydroxyl groups, forming a between two inter-molecular chains for intra-molecular chains. The medium required for this reaction to occur is acidic, which is inherent in the solution. The cross-linking mechanism of PVA/S with glyoxal is given below in Figure 1. The results obtained by carrying out various tests are given in Table 2 (Formulation 1) and Table 3 (Formulation 2)
4.1. Viscosity
The glyoxal acts as a cross-linker for PVA/S, which has led to subsequent viscosity
Figure 1. Crosslinking of mechanism of PVA/S with glyoxal.
Table 2. Results obtained by carrying out various tests for Formulation 1.
Table 3. Results obtained by carrying out various tests for Formulation 2.
Figure 2. Viscosity at increasing concentration of glyoxal given by (a) Formulation 1 and (b) Formulation 2.
change as shown in Figure 2.
The effect of cross-linking between the hydroxyl groups of PVA/S is evident in Figure 2. The glyoxal has reacted with the hydroxyl groups and thus forming a cross-link. This cross-link increases the chain length of the PVA and S, thus the increase in viscosity. Since, the longer chain length increases the chances of entanglement, it has led to increase in viscosity as evident in Figure 2. Although, while comparing the formulation 1 and formulation 2 values, we get a much greater viscosity in formulation 2. This is due to presence of hydrolyzed starch which has contributed to increase in viscosity.
4.2. Fourier Transform Infra-Red Spectroscopy (FTIR)
As, the concentration of cross-linker is increased, there is a movement of curve towards the lower wave number. This is observed since the cross-linker reduces the distance between chains by bridging between them, this bridging leads to lower H-bonding in the adhesive. The effect of decreased H-bonding can be seen in Figure 3 as the curve shifts towards lower wavenumber. Additionally, the increase in starch content also contributes to decrease in H-bonding (shown in Figure 3).
4.3. Differential Scanning Calorimetry (DSC)
The glyoxal acts as a cross-linker for PVA/S, which has led to subsequent glass transition temperature change as shown in Figure 4.
Figure 3. FTIR curves for (a) Formulation 1 and (b) Formulation 2.
The effect of cross-linking between the hydroxyl groups of PVA/S is evident in Figure 4. The glyoxal has reacted with the hydroxyl groups and thus forming a cross-link. This cross-link increases the chain length of the PVA and S, thus the increase in glass transition temperature. As evident from the FTIR curves, there is a decrease in H-bonding of the adhesive with subsequent increase in cross-linker. The similar trend is observed for Tg, there is an increase in Tg with increase in concentration of cross-linker. In comparing formulation 1 and formulation 2, there is slightly higher Tg for formulation 2 due to hydrolysis of starch.
4.4. Pencil Hardness of Film
Pencil hardness is a property dependent on the flexibility of the polymeric chains. The flexible chains of PVA are replaced partially by starch (which contains large 6 membered rings). The presence of rings in starch has contributed to increase in hardness of the formulations 2. Better cohesion in blends has also contributed to increase in hardness (as seen in Table 4). Both the formulations show a large difference in hardness with and without cross-linker. The cross-linking has clearly enhanced the hardness of the blends.
4.5. Tensile Shear Strength
The glyoxal acts as a cross-linker for PVA/S, which has led to subsequent tensile strength change as shown in Figure 5.
Table 4. Values of pencil hardness by cross-linking with glyoxal.
Figure 4. Glass transition temperature (Tg) at increasing concentration of glyoxal given by (a) Formulation 1 and (b) Formulation 2.
As seen in the previous sections, there is an increase in viscosity, glass transition temperature and pencil hardness of the blends. The tensile strength shows a similar trend as there is decrease in free volume between the chains, there is an increase in number of hydroxyl groups at the surface, as the hydroxyl groups become abundant on the surface there is an increase in tensile strength. Since, more cross-linker causes this decrease in free volume more rapidly, the tensile strength is increased subsequently (Figure 5(a) and Figure 5(b)). The cohesion between chains has also increased which further reduces the chances of tensile failure.
4.6. Ultimate Stress of Films
The cross-linking of glyoxal has decreased the mobility of the polymer chains. This has led to increase in stress bearing capacity of the chains. Thereby, increasing the stress required to break the blends. Also while comparing the formulation 1 and formulation 2, the larger number of six membered ring in starch help in increasing the stress (as seen from Table 5).
5. Conclusion
The cross-linking of PVA/S blends has efficiently increased thermal and mechanical properties. There is an increase in cohesion and decrease in H-bonding which has contributed majorly to increase in viscosity. Mechanical properties such as tensile strength, ultimate stress and pencil hardness have also shown
Table 5. Values of ultimate stress by cross-linking with glyoxal.
Figure 5. Tensile shear strength with increasing concentration of glyoxal after 2 hrs and 24 hrs of (a) Formulation 1 and (b) Formulation 2.
enhancing effect due to cross-linking. There is a shift in the glass transition temperature which supports the cross-linking mechanism. FTIR proves the presence of H-bonding which has effected its various thermal and mechanical properties. The presence of more starch content is found to increase the cross-linking due to easy accessibility for cross-linker to attack hydroxyl groups. Additionally, an increase in ratio of starch to PVA in a blend with constant concentration of glyoxal resulted in increase in the mechanical and thermal properties.