Engineered Cementitious Composite (ECC) is a cement based material with ultra-high ductility and strength in tension. This material is a kind of highperformance fiber-reinforced cementitious composite materials (HPFRCCs) reinforced with short fibers and characterized by tight multiple cracking. These characteristics of ECC make it applicable to increase the capacity and the ductility of structural elements so that structural design is economic and sustainable. This paper presents an extended evaluation of Improved Engineered Cementitious Composites (IECC) for the use in the strengthening of masonry in filled reinforced concrete frames. IECC is a mixture of cement, fly ash, water, sand, quartz powder and poly-vinyl alcohol fibers with a better quality of tensile strain rather than common ECC. Two types of fine sand and quartz powder used in this study as filler to improve ECC behavior. Also, to show the effect of fly ash on IECC properties, five different mixtures were considered with various fly ash ratios. Different mixtures of IECC using fine aggregates produced in Iran were selected to find out how the aggregates and fly ash would affect IECC performance. The results show that the optimized mixture has the best characteristics including tensile strength and strain. Also, three-dimensional diagrams were used to compare the properties of different mixtures of IECC more effectively and to represent the influence of the range of fly ash ratios so that it can be opted based on design objectives such as ECC properties, costs and structural parameters and demands. These diagrams show the behavior of IECC which its fly ash content ratio in the binder is 50% to 67%.

ECC has very high ductile behavior in tensile loads and is known as a special kind of HPFRCC that invented at the University of Michigan in the early 1990s for the first time [

Thus, ECC can be used in many structures to extend service life, reduce the maintenance and repair cost. Recently, ECC is highly used in decks [

In normal concrete, aggregates play a key role in mechanical properties of hardened concrete. However, they cause poor fiber dispersion in fiber reinforced concrete [

The high quantity of cement in ECC makes easy control in fiber dispersion and better strain-hardening behavior. To obtain strain hardening in this material, matrix fracture toughness has to be limited so that multiple cracking could occur before reaching the maximum fiber bridging stress [

Based on previous studies, ECC has better performance than traditional cement concrete mixes. However, nearly all of the past works were performed on

ECC material consist of very fine sand which is not supplied by the common size of aggregates. This kind of sand includes more than 90% passing the No. 100 sieve size [

Although, there are few studies on the influence of Fly Ash (FA) on characteristics of ECC such as the bonding interface between fiber and matrix, the tensile properties and strength, there are some special studies carried out and focused on testing different FA contents and evaluating these properties. Tensile test of PVA-ECC with the FA/C (fly ash and cement ratio) between 0 to 1.5, the results showed that ECC strain capacity increased with the increase of FA/C [

In this study by the use of fine and medium aggregates in ECC, two types of aggregate size gradation are evaluated. The results showed that ECC made with fine aggregates exhibit the better and desired tensile properties or ductile behavior. Two kinds of fine sand and quartz powder were used to show the effect of aggregate size on fiber dispersion and uniaxial tensile behavior of ECC. To show the effect of cement content on the behavior of ECC, five mixtures with different ratios of the matrix which have a different volume of fly ash, were produced.

This paper presents multiple evaluations of the improved engineered cementitious composite using locally sourced materials for use of retrofit in masonry infilled reinforced concrete frames. IECC is a mixture of cement, fly ash, water, sand, quartz powder and poly-vinyl alcohol fibers with the high quality of tensile strain. In standard mix design of ECC, fly ash is commonly used. Since fly ash is expensive and not produced in Iran, using another material which contains pozzolanic properties is proposed. For this reason, five mixtures were considered for different ratio of fly ash in ECC to show the effect of this material on tensile behavior and optimize this content ratio. The purpose of evaluating IECC was to determine if IECC would be suitable for use as a masonry infill overlay. In total, 6 different laboratory mixes were evaluated using 36 uniaxial tensile tests. The results show that one mixture has the best behavior in tension.

The laboratory experiment includes the development and evaluation of different ECC mix by investigation of the effect of fly ash on ECC behavior to find the best ECC and know as IECC. Also, to show the effect of sands on tensile strength and strain of ECC, two kinds of sands were used for standard material. Mix proportions were selected based on the findings from previous research on ECC [

The ECC material used in this study utilized cement, fly ash, fine sand, quartz powder, water, and superplasticizer to improve the fresh properties of the mixture and PVA fibers. All types of materials are common except fine sand and quartz powder.

One of the most important factors of producing of each material is an expenditure. The fine sand and quartz powder used in this study as filler were instead of the typically used sand to improve ECC behavior. Two different sands and quartz powder sources were selected in Iran.

As mentioned, The ECC material used in this particular study utilized cement, fly ash, fine sand, quartz powder, water, and Hydroxy Propyl Methyl Cellulose (HPMC) as superplasticizer to enhance the fresh properties of the mixture and

Diameter (µm) | Length (mm) | Tensile strength (MPa) | Young’s modulus (GPa) | Elongation (%) | Density (g/cm^{3}) |
---|---|---|---|---|---|

39 | 8 | 1600 | 42.8 | 6 | 1.3 |

2% of PVA fibers in volume. The weight proportions of the ECC matrix ingredients are given in

In practice, dry ingredients consist of cement, fly ash, sand, quartz powder and superplasticizer were first mixed using a type of laboratory mixer for about 1 min. Then water was added and mixed about 4 min. At this time, obtained mortar showed adequate flowability and viscosity visually investigated and needed for the good workability and uniform fiber distribution. Finally, PVA fibers were added gradually and mixed for 3 min.

To determine the applicability of using IECC as a masonry infill overlay, the material was subjected to performance tests to determine tensile strength and strain.

To confirm the tensile strain-hardening behavior of this ECC and compare with the common ECC, the dog-bone specimens with 500 mm long, 90 mm wide and 50 mm thick shown in the next section, at the age of 7 days were used in the uniaxial tensile test. The strain of the dog-bone specimen was obtained by taking the average reading of extensometer, attached to the specimen. Mixing process and slump test of the specimens is shown in

Cement | Fly ash | Fine sand | Quartz powder | Water | Superplastisizer |
---|---|---|---|---|---|

1 | 2 | 0.35 | 0.35 | 0.75 | 0.012 |

pairs of steel plates, which were connected to the loading device. Then, an extensometer was attached on both sides of the specimen to measure the specimen deformation and consider eccentricities. The tests were conducted under displacement control with a loading rate of 0.015 mm/s [

The tensile strengths of each mix were measured at 7 days after mixing. The specimen size and results of uniaxial tensile tests in stress-strain curves are presented in

ECC type | Tensile yield strength (MPa) | Tensile strength (MPa) | Ultimate tensile strain |
---|---|---|---|

Type 1 | 2.4 ± 0.1 | 3.16 ± 0.25 | 3.92 ± 0.6 |

Type 2 | 2.3 ± 0.15 | 2.84 ± 0.63 | 4.15 ± 0.64 |

strength, ultimate strength and ultimate strain. The definition of tensile yield strength is shown in

To show the effect of fly ash ratio on ECC behavior, 5 different ratios were considered. For each mixture, three tests were done. The ratio of fly ash to cement material is illustrated in

Mix name | Cement ratio | Fly ash ratio |
---|---|---|

F0.5 | 1 | 0.5 |

F1 | 1 | 1 |

F1.5 | 1 | 1.5 |

F2 | 1 | 2 |

F2.5 | 1 | 2.5 |

the binder was fix and the total amount of cement and fly ash is not variable whereas their ratio is changing. Figures 9-12 show the tensile stress-strain curves.

The tensile properties of the ECC were evaluated at 14 days after mixing. The reported tensile strengths are the maximum value for testing. The reported tensile strains are the values where the tensile load experiences a large drop just before the sample breaks into two. Since the behavior of ECC with type 2 is better than type 1, the best mixture is tested using type 2 material. As seen, the best behavior of ECC tested with different fly ash ratios with type 2 material is F1.5 Mixture (with 1:1.5 cement to fly ash ratio). This mixture can be known as IECC due to high tensile strength and strain which are 3.5 MPa and 6% respectively. To compare standard ECC and IECC which have an average tensile strength of 3.16 MPa and 3.92 MPa and tensile strain 3.92% and 6% respectively.

To compare tensile strength and strain of all ECC mixtures,

ECC mixture | Tensile yield strength (MPa) | Tensile strength (MPa) | Ultimate tensile strain (%) |
---|---|---|---|

Standard type 1 (S1) | 2.4 ± 0.1 | 3.16 ± 0.25 | 3.92 ± 0.6 |

Standard type 2 (S2) | 2.3 ± 0.15 | 2.84 ± 0.63 | 4.15 ± 0.64 |

F0.5 | 3.25 ± 0.1 | 3.65 ± 0.1 | 3.35 ± 0.4 |

F1 | 2.95 ± 0.05 | 3.6 ± 0.08 | 3.7 ± 0.3 |

F1.5 | 2.65 ± 0.1 | 3.4 ± 0.14 | 6.1 ± 0.13 |

F2.5 | 1.9 ± 0.12 | 2.2 ± 0.13 | 2.7 ± 0.62 |

mean and median values of results in bar charts and connect line respectively. Also, the interval of each mixture can be seen to consider standard deviation calculated in

As it can be seen, the best mixture in tensile yield strength and tensile strength is F0.5 which has C:FA ratio of 1:0.5. The mean values of these strengths for this mix are 3.15 MPa and 3.7 MPa respectively with 0.1 standard deviation. The lowest mean values of strengths (1.9 MPa and 2.2 MPa) belong to F2.5 with C:FA = 1:2.5 ratio.

To compare the ultimate tensile strain parameter, it should be known that the most important factor of the ductile behavior of ECC is having multiple cracks and higher ultimate tensile strain represented in the uniaxial tensile stress-strain curve. To obtain the high-ductile behavior of ECC, this parameter must be greater than ordinary HPFRCC. To achieve the high ductile behavior and multiple cracks in ECC ultimate tensile strain was compared to 6 mixtures based on

Also, it should be noticed that variation of results and standard deviation in strength parameters is less than strain. Based on

By comparing the mean and median value of figures, it can be found that there is no significant difference between them. Although mean is not a robust statistic tool since it cannot be applied to all distributions, it is easily the most widely used statistic tool to derive the central tendency. The reason for this matter is due to getting unduly impacted by values in the sample that is too small to too large. On the other hand, it is difficult to use median in theoretical studies and generally, there is no easy mathematical formula to calculate the median. Therefore, in this case these two statistical parameters are compared to show the central tendency of their distribution. As seen, mean and median values are nearly the same in all figures. So, it means that in this case the mean is a good representative of the central tendency of the samples.

To show the effect of the other C:FA ratios in tensile strength and strain of ECC, a contour plot between tensile strength and ultimate tensile strain is shown for different mixtures in

done using the distance-based method to predict the strength and strain of ECC. This method is simple and famous which is mostly used for the interpolation. It is based on the gradual change of trend surface in proximity concept [

Z * ( u ) = ∑ i = 1 n λ i Z ( u i ) (1)

where u is the estimation location, u_{i}, i = 1, 2, ・・・, n, are the locations of the sample points within the search neighborhood, Z*(u) is the inverse distance estimate at the estimation location, n is the number of sample points, λ_{i}, i = 1, 2, ・・・, n, are the weights assigned to each sample point, and Z(u_{i}), i = 1, 2, ・・・, n, are the conditioning data at sample points. The weights are determined as:

λ i = ( 1 d i p ) ∑ i = 1 n ( 1 d i p ) , ( i = 1 , 2 , ⋯ , n ) (2)

where d_{i} are the Euclidian distances between estimation location and sample points, and exponent p is the power or distance exponent value. It should be mentioned that the sum of the inverse distance weights is equal to 1 as follows:

∑ i = 1 n λ i = 1 (3)

The most common value applied for the power p is 2. However, any value for p can be chosen. If p increases, the interpolated value by inverse distance will be assigned the value of the nearest sample point and become the same as estimate produced by polygonal method [

As known, the distance method works well in a wide range of circumstances. It is a conservative method because it always provides estimates of the third factor within the range of the data. In this approach, distance power is 2 and mesh number of interpolating surface is 30 × 30 in each direction to obtain a higher quality of results.

As seen in

The purpose of this study was to evaluate the performance of ECC made with locally sourced materials. Two different fine sand and quartz powders and five different mix proportions of fly ash were used to develop IECC mix. The performance of IECC was compared to that of a typical ECC mix used for masonry infill overlays in RC frames. The objective was to determine if IECC could replace the ECC as the material for these overlays.

Based on the findings from this study, the following observations can be made:

・ Using fine materials show lower strength and higher strain that must be considered in all designs.

・ In fine aggregates, yield strength and tensile strength were decreased 5% and 10% respectively. However, the ultimate strain was increased 5%.

・ The best ratio of fly ash in the binder is 1 to 1.5 for the cement to fly ash ratio which has 3.5 MPa tensile strength and 6% tensile strain so that IECC can be known with 60% in the binder.

・ The Central tendency of the samples was observed in all ECC mixtures.

・ It is concluded that in FA/C ratio between 1 - 2, ECC has high ductility. However, tensile strength can be higher than 3 MPa in the ratio between 1 - 1.5 and lower than 3 MPa in the ratio between 1.5 - 2. Thus, IECC will be obtained if fly ash content is between 50% to 67% of the binder.

The authors are grateful to International Institute of Earthquake Engineering and Technology (IIEES) for the supports in this research especially in experimental studies.

Nateghi-A, F., Ahmadi, M.H. and Dehghani, A. (2018) Experimental Study on Improved Engineered Cementitious Composite Using Local Material. Materials Sciences and Applications, 9, 315-329. https://doi.org/10.4236/msa.2018.93021