The effect of CO 2 injection on initial strength increase and hardening of cement-fibre mix in a cement bonded particle board (CBPB) production was evaluated. Different cement contents, formation pressure and types of fibres were considered. The initial strength increase with CO 2 injection is so much faster than this caused by conventional hydration that the produced samples do not need additional curing before they can be stored. Similar strength and stiffness values as in conventional products on the market are gained with lower cement content for similar types of fibres. Visual inspection of board surfaces aged for 13 years in a harsh exterior environment as well as comparison of strength and stiffness values for these boards when new and after ageing, give s a very satisfying result. The combined effect of the above discussed gains results in markedly increased productivity at lower cost and lower environmental impacts than is possible in traditional CBPB production.
Cement bonded particle boards (CBPB) are traditionally made of wood fibres, cement and water, usually with some additives to speed up the bonding process, in traditional production caused by hydration of cement. CBPB boards so far, due i.e. to economic reasons are only used to a very limited extent, compared to common boards with organic binder (plywood, OSB). However, the CBPB boards have very interesting properties regarding stiffness, fire, acoustics and resistance to termites and microorganisms.
There are mainly two different methods in use to produce CBPB; the Hatscheck process and the Elmendorf process. Initially, asbestos fibres were used whereas now these comprise cellulose fibres; fibre length up to 4 mm (commonly less than 3 mm), diameter typically around 40 µm.
The Hatscheck Process
A drum rotates in a water based slurry of fibres and mineral materials, including Portland cement. The drum feeds a film of slurry onto a felt while simultaneously partially pressing the water from the film, upon which the felt moves the film onto a forming roller where a sheet of desired thickness is built up by a number of turns. Subsequently, the stack of films is removed from the roller and laid out flat to form the sheet.
The Elmendorf Process
Fibres, water and then cement are thoroughly mixed, with the mix typically made with fibres amounting about 70% of the volume; with the ratio by weight: cement 60%, wood 20%, water 20%. The damp matrix is fed continuously onto a bottom (caul) plate to form a mat. The caul plates with mats are stack-pressed to yield boards of desired thickness. Under the pressure, of 1.5 - 3.0 MPa, water squeezes out of the wood particles and combines with the cement to form a paste. The stack of boards is clamped together at this pressure and moved to a curing cabinet, with controlled humidity and temperature (70˚C - 80˚C) and left there for curing for 8 - 20 hours [
The CBPB boards are of interest as these have good fire protection properties, along with better resistance to humidity fluctuations than most comparable boards on the market. The inorganic binding material (cement) gives better resistance to microorganisms than boards with organic binders [
The initial strength increase of cement bonds is traditionally acquired by hydration followed with time by additional strength gained through carbonation of the hardened cement paste. Usually carbonation, due to changes in pH of the concrete and also additional shrinkage, is considered as a deterioration mechanism in reinforced concrete but the mechanism certainly has its positive sides too as e.g. substantiated by testing.
It has been known for decades that initial hardening of the cement paste by accelerated carbonation can be achieved by the injection of CO2 into the wet paste. The initial reaction on exposure to CO2 is an accelerated hydration of the silicates to form a calcium silicate hydrate (C-S-H) like gel and calcite, while furthermore the reaction is exothermic [
Tests on cement paste, with initial hardening by CO2 injection, with or without fibres, described in the literature vary with respect to both type of specimens and methodology. In the earliest tests bulk specimens were used, made of cement paste only, and specimens are placed in a chamber fed with predefined CO2 pressure and concentration [
Agopyan [
Initial hardening by CO2 exposure may result in new interesting development techniques in the production of CBPB boards. For the accelerated carbonation, CO2 in a much higher concentration than this in the atmosphere is needed, and the resulting CO2 sequestration is of interest in itself [
In 1986 E. Schmidt, Dr. Dipl.-ing [
An EU research project with the former Icelandic Building Research Institute (IBRI), now Innovation Centre of Iceland, as project leader was ongoing in the time period 1997-2000. The aim of the project was to develop a production method for box house elements of wood-fibre and cement in one pressing operation, using fast initial carbonization to speed up the hardening process. The project resulted in a patented production method [
To the knowledge of the authors of this paper there is no full scale production line functioning any longer where initial hardening of cement bonded material by CO2 injection is used.
The properties of CBPB compared to other board materials should be of interest to the building market. Especially with the use of CO2 injection, various types of fibres, e.g. waste materials from agriculture might be used. It is therefore of great interest to develop faster, cheaper and more environmentally friendly production techniques of CBPB; with lower cement content, less energy use, as curing cabinets will not be needed, to the same extent as at the present and the possibility of using non-traditional fibres such as re-used wood or waste fibres from agriculture such as bagasse.
In 2010 research on the use of fast carbonation in CBPB production was reintroduced at the Innovation Centre of Iceland in cooperation with SPECA (Iceland), with the main aim of testing fibres from agricultural waste; wheat- and barley straw to produce boards.
The aim of this paper is i.e. to describe tests on CBPB with wood fibres, comparison of CO2 injected CBPB with traditional CBPB, and then test results from small laboratory CBPB specimens with wheat fibres and CO2 injection.
In the EU research project noted earlier [
In factory production a feeder is used to form the mat on a moving caul plate, as mentioned earlier. The method results in a felt of a stable quality and it is known from experience of fibre board production that this is very important for the quality of the product. In the laboratory tests there was no access to a feeder so that a box forming the specimens was hand fed through a screen. The relevant result is thus not of the same quality as from a factory feeder. In the research project the effect of this had to be evaluated, and therefore results from measurements on specimens taken from factory production were compared with those from a laboratory production, using exactly the same material mix.
Test specimens in the research were of four types: 1) small scale specimens with traditional wood fibres, made in a laboratory simulating traditional CBPB production, 2) specimens taken from factory made CBPB boards in Europe, 3) small scale specimens with different fibre types made in the laboratory with initial CO2 hardening and finally, 4) specimens from full scale cement fibre box elements with initial CO2 hardening produced at an early stage of the aforementioned research project in Germany, and later with the factory products using CO2 produced in Iceland. In all cases the mixing of materials and production was in accordance with the Elmendorf process, not the wet slurry method of Hatscheck.
The main part of the research was aimed at evaluating the effect of fast initial hardening with CO2 injection. The method used is similar to this described by Simatupang et al. [
Cement and material mix:
Cement used was standard Type I Portland cement. The basic material mix is cement/fibre (bone dry) ratio of 2.8, the water/cement ratio 0.28 and with some additional, yet limited water in the fibres. For plain wood fibres, the total water content then results in a water/cement ratio of 0.32.
All mixes were without any additives commonly used in CBPB production.
Fibre type and size:
The wood fibres used in the testing project were in the initial stage imported spruce fibres from a big CBPB producer in Europe, but after full scale production started, the fibres were produced in Iceland from reused freight pallets. For comparison, fibres from barley and wheat stems were also used. The stems are dried to make the material more brittle makes it possible to hack the stems in a high speed mixer to produce the fibres. The method is simplistic but it was difficult to get even product, the particle size being dependent on i.e. the amount hacked each time and the time the mixer is on―a refinement of the fibre forming process will be needed.
The production of wood fibres for CBPB production is an industry, using well-defined fibres, and is well proven over time. While evaluating new type of fibres it is natural to compare these with the traditional fibres. In the test production of boards, the fibres used were traditional wood fibres (for comparison) along with fibres from different plants. For the sake of comparison between fibre types the three dimensions; thickness, width and length can be compared,
Type of fibres | Diameter (mm) | Typical length of dominant particle size (mm) | Longest fibres (mm) |
---|---|---|---|
Wood | 0.6 - 2.2 | 6 - 10 | 19 |
Barley straw (Iceland) | 0.2 - 2.2 | 10 - 12 | 86 |
that is a few times the thickness, the sizes perpendicular to length often change noticeably (the uniformity of these fibres is less than for the wood fibres).
The particle distribution is measured by quadratic mesh sieves that are vibrated to get the fibres through; the larger dimension of thickness or width will be determining for the measured distribution but the smaller dimension will be more typical measured perpendicular to the plane due to the effect of production pressure.
Laboratory specimens’ production:
The specimen produced in the laboratory were of the size of 42 × 48 cm with aimed at thickness usually 12 mm, while actual thickness varied somewhat pending on type of fibres, material mix and formation pressure.
The mixing of materials was done in a Hobart mixer by adding water to the fibres, and allowed to mix for 2 min. to get an even moisture distribution. Cement was then added in small amounts into the mix with the mixer going all the time. The material matrix was handfed onto a plate and then pressed.
The traditional CBPB production is simulated by keeping the formation pressure of 1.5 MPa for 12 hours and the stack is enclosed in polyethylene film all the time so as not to lose moisture from the board by evaporation. The stack is also insulated and the hydration heat and additional energy used to keep the temperature at 60˚C or close to this. After the 12 hours the specimen was put in a curing cabinet at 20˚C and 50% RH.
For specimen intended for CO2 injection from one side the material matrix is fed onto a perforated plate to allow injection of CO2 into the matrix. When injected from both sides a similar plate was placed on top of the matrix before placing the stack into the loading apparatus,
Bending test of specimen:
Determination of bending strength and stiffness is made according to EN 310 [
The bending stiffness is determined from the load-deflection curve from load and deflection at loads 0.1 Fmax and 0.4 Fmax.
From each board, made in the laboratory or from full scale production, five specimen of a certain size were acquired to fulfil the standard requirements, the thickness of boards, and specimen, varied between 12 and 20 mm.
The specimen and products discussed in this part of the paper are all made from either virgin spruce fibres or recycled wood products from freight pallets.
Small scale specimens were produced in the laboratory simulating the traditional CBPB production as described earlier, the specimen were stored for seven days in a curing cabinet at 20˚C, 50% RH before testing. Additionally, test specimens were cut from full size boards produced in a CBPB factory in Germany. The test results from bending tests of these two types of test specimen are shown in
The results show that the results from the small scale production of test pieces were consistent in themselves but much lower than the results from the full scale production. For comparison with the traditional CBPB market, it should be noted that boards on the European market from two big producers have a stated bending strength of 12 MPa. Based on the evaluated strength and stiffness difference of test pieces from small and large scale production the small scale production was considered valuable in evaluating the effect of different production methods and material mixes, keeping in mind that the full scale products would
No of tests | Density (kg/m3) | Bending strength MOR (MPa) | Bending stiffness MOE (MPa) | |
---|---|---|---|---|
Small laboratory specimens | 24 | 1333.4 | 5.1 (0.78) | 1754 (374.5) |
Full scale specimens | 8 | 1393.6 | 11.7 (1.1) | 5225 (427.1) |
be considerably stronger. The higher strength in a full scale production using initial hardening by CO2 was later in the project proven to be the case. Based on this, further tests on small scale test pieces with initial CO2 hardening were made to evaluate the effect of ageing, amount of cement and types of fibres.
Small scale laboratory specimens ere produced with initial hardening by CO2 injection from both sides. The matrix mix is the same as in traditional CBPB tested, the cement content about 800 kg/m3. The test results are shown in
By comparing values in
Small scale specimen with different cement content and initial hardening by CO2 from both sides were tested, a total of 24 test pieces for each type of mix. Water content is somewhat higher than in the tests already described; 15% of dry weight of fibres + 0.30 w/c ratio. Formation pressure was either 1.5 MPa or 2.5 MPa, and tests done after curing of specimens for respectively 1 and 10 weeks.
Conditioning (days) | No of tests | Bending strength MOR (MPa) | Bending stiffness MOE (MPa) |
---|---|---|---|
1 | 45 | 4.54 (1.07) | 1849 (587) |
7 | 33 | 5.01 (0.88) | 2141 (524) |
28 | 33 | 6.21 (1.46) | 2693 (576) |
The test results may be summarized as follows:
1) Bending strength (and also density and stiffness, not shown on figure) of specimens increases significantly with increased cement content given the same formation pressure.
2) Increased formation pressure makes denser and somewhat stronger products.
3) Bending strength increases significantly with age from 1 week to 10 weeks.
Generally, the variability in results from the small scale specimen is considerable and so quite a number of test pieces are required to get reliable results. Measured moisture adsorption on a very limited number of pieces indicates that equilibrium moisture of the CO2 hardened pieces is considerably lower than for the factory produced CBPB boards and that the first mentioned pieces also have smaller dimensional changes due to moisture changes. This can be explained by the findings of Fan et al. [
Limited test series with only eight specimens of each type were used to compare strength results of pieces produced with CO2 injection from both sides with pieces injected from one side only. The results indicate that specimen produced with single sided injection are as good as these produced with double sided injection.
Test results on specimen with CO2 injection from small scale elements were compared with results from specimens from full scale element factory production. The matrix mix is exactly the same in both types of elements; wood fibres (bone dry) 275 kg/m3, water 245 kg/m3, cement Type I 770 kg/m3, CO2 80 kg/m3 and formation pressure 2.5 MPa. The small and full scale specimen compared were of exactly the same mix and the production methodology as similar as possible (only the feeding of matrix differs).The results are in
Agricultural materials such as wheat and barley stems are available in abundance worldwide. Thus it is of interest if such fibres can be used in CBPB. A few specimens were produced in the laboratory and tested after seven days curing in the same way as already described for other small scale specimen. The cement content was 900 kg/m3, one sided CO2 injection used and formation pressure 1.5 MPa. The test results are shown in
A full scale factory production was operated for some years in Iceland as mentioned earlier, using the same mix as already described for the full scale test elements. Throw away elements from this production period, specimens that were
Type | No. of tests | Density (kg/m3) | Bending strength MOR (MPa) | Bending stiffness MOE (MPa) |
---|---|---|---|---|
Small scalelab. specimen | 33 | 1235 | 6.2 (1.5) | 2693 (576) |
Full scale specimen | 40 | 1461 (99) | 15.8 (2.1) | 8417 (1396) |
Type | No. of tests | Age (days) | Density (kg/m3) | Bending strength MOR (MPa) | Bending stiffness MOE (MPa) |
---|---|---|---|---|---|
Barley stem fibres | 4 4 | 6 13 | 1415 (18) 1447 (4) | 4.9 (0.85) 6.5 (0.40) | 2407 (129) 2832 (228) |
not approved in the quality control inspection, still exist in an unprotected stack outdoors at the factory site. There also stands an extension building to the production hall; built in 2003 from CBPB box elements. The walls are unprotected by any surface treatment. The climate is moist and windy with frequent freeze-thaw periods; the yearly precipitation is 600 - 800 mm, humidity all year round about 80% RH and number of annual freeze-thaw cycles ranges 45 - 55. A visual inspection shows a slight surface roughening at spots on the surface of wall-elements,
The moisture content in some elements along with the factory wall element was measured with a capacitive moisture meter for comparison. Moisture in the wall elements was similar to the driest unused elements. Pieces were cut from five of the stacked box elements,
The research project gave many interesting results regarding initial hardening following CO2 injection into the newly pressed CBPB with traditional wood fibres compared to similar production without CO2 injection, and furthermore that other types of fibres can be used in this context.
Small scale laboratory production yields less strength and stiffness properties than products from a full scale production. This difference is mainly due to uneven feeding (by hand) of the matrix in a small scale production. The small specimens show a greater variability in properties than does a full scale production. The difference makes for a fairly exact estimate of which results may be expected in full size production somewhat uncertain.
Measured dimensional changes due to moisture changes in CBPB produced with CO2 injection are considerably lower than in traditional CBPB.
The initial hardening with CO2 injection does not need any extra energy for heating of the boards, and also less cement use than is needed in traditional
Number of test-pieces | Thickness (mm) | Material density, dry (kg/m3) | Material moisture (on site), of dry weight (%) | Bending strength MOR (MPa) | Bending stiffness MOE (MPa) | |
---|---|---|---|---|---|---|
Elements aged 7 days | 40 | 15.8 (2.1) | 8417 (1396.3) | |||
Elements after 13 years weathering | 25 | |||||
Span of measured values | 25.9 - 33.0 | 1400 - 1530 | 12.0 - 18.4 | 14.8 - 19.1 | 5880 - 7906 | |
Average value and standard deviation | 28.1 (2.95) | 1473 (57) | 15.9 (3,3) | 16.6 (1.7) | 7440 (975) |
CBPB production. To reach the same strength as traditional CBPB boards on the market show, the cement content can be lower still.
Barley fibres need higher cement content than is the case for wood fibres, but this fulfilled, they can be used in CBPB production, pending CO2 injection.
The product is highly resistant to termites and microorganisms (mildew) and with good weathering properties.
The use of initial hardening by CO2 injection should be of interest in the production of CBPB;
The method gives higher initial strength with lower cement content than in traditional production and no need for energy use for curing of boards. The production is obviously environmentally friendly inasmuch that this/it binds CO2 and does not need external energy for heat treatment. In other words, it should be of great interest in the context of minimizing global warming effects.
Shorter production time as the boards, after formation pressure and CO2 injection of 3 - 4 minutes, are strong enough to be stored without additional curing.
Formation pressure of 1.5 MPa can be used for production with initial hardening by CO2, in traditional CBPB production formation pressure as high as 3 MPa is often needed.
Increased productivity as the traditional curing of CBPB will not be necessary. The potential for increased productivity in a CO2 based production as compared with a traditional production is estimated as high as 5 - 10 times.
Initial hardening by injection of CO2 from one side without using intermediate vacuum operations and with open edges of boards makes it possible to change existing production lines at a very limited cost.
Surface structuring of boards (embossment) can easily be done in a single sided CO2 injection production line.
Marteinsson, B. and Gudmundsson, E. (2018) Cement Bonded Particle Boards with Different Types of Natural Fibres―Using Carbon Dioxide Injection for Increased Initial Bonding. Open Journal of Composite Materials, 8, 29-43. https://doi.org/10.4236/ojcm.2018.81003