The aim of this study is to search for a substitute for the natural coarse aggregate in various regions of the world, such as Amazon-Brazil, where this type of material is lacking. The asphalt binder AC 50/70 is mixed with an aggregate obtained from the sinterization of a calcined clay (SACC) as a possible alternative to coarse aggregate material for the construction of asphalt pavements in tropical zones. The dynamic modulus | E*| of this mixture was measured under strain control mode and in tension control mode. The results are compared with those obtained from AC 50/70 mixed with pebbles, which is currently used as the coarse aggregate in this region. For pavements that work at high temperatures, such as 40 ℃, and low frequencies, the mixture with SACC appears to be a viable alternative to coarse aggregate material for the construction of asphalt pavements in tropical zones.
In all regions of the world, there have been increased efforts to identify new materials for use in road construction that obey the economic and environmental conditions based on the natural resources and new technologies of each country. In this context, lightweight aggregates from expanded clay have been studied as substitutes for natural aggregates in the construction of asphalt pavements [
In the Amazon region in northern Brazil, the construction of pavements is a great challenge for civil engineering due to the lack of coarse aggregate. The natural sources of aggregate materials are distant from the urban areas. The predominant geological formations consist of claystone, siltstone, and sandstone. Since the Tertiary period, these rocks have undergone intense lateritic weathering, resulting in a thick layer of residual soil on which the Amazon rainforest spreads. The rock material is located at a great depth from the surface such that its exploitation as a source of aggregate material for civil construction is notably expensive. The transportation of those materials from the distant surface deposits to the urban areas should generally be conducted via the river network that crosses the region. The scarcity of this material, associated with the poor navigability of the rivers for six months each year (the dry season) and the great distances involved in its transportation, makes its cost prohibitive to the civil construction industry. In the absence of the traditionally used granular materials, the pavements in this region are often constructed using pebbles collected from the edges and the bottom of the local rivers. However, the continued large-scale exploitation of these materials could cause serious environmental problems in the very near future with a strong impact on the Amazon rainforest. The sintered aggregate of calcined clay (SACC) may represent a viable alternative to coarse aggregate material for the construction of pavements in the Amazon region.
For the above reasons, we studied the Dynamic Modulus |E*| of asphalt binder AC 50/70 mixed with an aggregate obtained from the sinterization of a calcined clay under cyclic loading [
The materials studied under cyclic loading are composed of a mixture of asphalt concrete AC50/70 and the coarse aggregates SACC and pebbles. The latter is what is currently largely used in the asphalt mixtures of pavements, the exploitation of which is responsible for the deterioration of the Amazon rivers beds. In this study, pebbles are used only as a comparison to SACC, which is studied as an alternative for the serious environmental problems created by the exploitation of pebbles.
1) Aggregates
The SACC was obtained from typical clay soil of Amazon-Brazil. The SACC was characterized according to the Brazilian Association of Technical Standards (ABNT) using NBR-7181 for the grain size, NBR-6459 for the liquid limit and NBR-7180 for the plastic limit. The calcination potentiality of the raw clay to form aggregates was obtained following the instructions of the Federal National Department of Transport Infrastructure (DNIT) of Brazil (ME222, ME223 and ME225). To produce aggregates from raw clay, massive bricks, with dimensions of 60 mm × 110 mm × 200 mm and two longitudinal holes, were crushed into grain-sized portions.
The two coarse materials were evaluated according to the instructions of the American Society for Testing and Materials (ASTM). The grain size and the Los Angeles abrasion value follow ASTM-C136 and ASTM- C131, respectively. The apparent specific gravity (Gsa), bulk specific gravity (Gsb), bulk specific gravity in the condition saturated surface dry (Gsbssd) and absorption were obtained via adherence to ASTM-C127. The coarse materials were also characterized in relation to the Rodded Unit Weight (Wur) and Loose Unit Weight (Wul) following the American Association of State Highway and Officials (AASHTO).
Three fine aggregates were used to constitute the asphalt mixtures: two sands, obtained from the local supplier, with different grain sizes, and the powder resulting from the procedure of brick grinding. They were characterized by ASTM-C136 (grain size), ASTM-C128 (Gsa, Gsbssd and absorption) and Rodded Unit Weight (AASHTO).
The grain-size distributions for the natural soil (NSOIL), which was used to produce the sintered aggregate of calcined clay, are shown in
The mineralogy of the natural soil used to obtain the sintered aggregate consists of kaolinite, goethite, hematite, illite and quartz. The characterizations of the coarse aggregate and the sand are shown in
2) Binder and filler
The petroleum asphalt cement AC 50/70 was used as the binder, and rheological analysis, performed according to the Superior Performance Asphalt Pavements, classified it as PG64 + 2. The Portland cement, the filler in the composition of the asphalt mixtures, exhibits 3.15/cm3 of apparent specific gravity and a 0.075 mm sieve passing percentage of 100% according to DNIT-ME085 and DNIT-ME367, respectively.
The mechanical behavior of asphalt mixtures depends largely on temperature, varying from elastic to nonlinear viscoelastic, as well as on rate of application of the load or strain. These characteristics are derived primarily from the asphalt binder. In this study, we perform the Dynamic Modulus |E*| under both constant tension and constant strain regimes. This propriety was obtained for two types of AC 50/70 mixtures: with SACC, as an alternative coarse material, and with pebbles, which is a conventional coarse aggregate used in civil engineering and taken as the reference material for SACC.
1) Samples
Following the Superpave system for the granulometric compositions of asphalt mixtures, the Nominal Maximum Sizes (NMS) adopted was 19.00 mm. The percentages of mineral components of the mixtures were defined according to the Bailey method [
In
The air voids (Va) and voids filled with asphalt (VFA) were determined by compacting the mixtures according to the Marshall method of dosage. Based on these parameters, and following the method of DNIT, the content of the composite was determined; the volumetric parameters are shown in
Tests | SACC | Pebble | Method |
---|---|---|---|
Bulk specific gravity, Gsb (g/cm3) | 1.855 | 2.626 | ASTM C-127 |
Bulk Specific Gravity in the condition saturated surface dry, Gsbssd (g/cm3) | 2.133 | 2.636 | |
Apparent Specific Gravity, Gsa (g/cm3) | 2.571 | 2.643 | |
Absorption (%) | 15.0 | 0.0 | |
Loose Unit Weight, Wul (kg/m3) | 1062.0 | 1894.6 | AASHTO T-19 |
Rodded Unit Weight, Wur (kg/m3) | 1126.35 | 1906.32 | |
Los Angeles abrasion (%) | 70.0 | 37.0 | ASTM C-131 |
Sample | MAO | COA | SCCA-P | Method |
---|---|---|---|---|
Gsb (g/cm3) | 2.632 | 2.627 | 1.790 | ASTM C 128 |
Gsbssd (g/cm3) | 2.692 | 2.706 | 2.167 | |
Absorption (%) | 0.00 | 0.00 | 18.96 | |
Wur (kg/m3) | 1675.9 | 1782.20 | 1375.71 | AASHTO T-19 |
Components | SCCA mixture | Pebble mixture |
---|---|---|
SCCA (%) | 74.25 | - |
Pebble (%) | - | 67.2 |
SCCA-P Sand (%) | 14.03 | - |
COA Sand (%) | 10.32 | - |
MAO sand (%) | - | 29.7 |
Portland cement (%) | 1.40 | 3.10 |
Parameters | SACC | Pebble |
---|---|---|
Content of AC (%) | 9.4 | 4.5 |
Bulk specific gravity, Gmb (%) | 1.778 | 2.288 |
Maximum specific gravity, Gmm (g/cm3) | 1.842 | 2.383 |
Air voids, Va (%) | 3.5 | 4.0 |
Voids in mineral aggregates, VMA (%) | 15.98 | 18.78 |
Voids filled with asphalt, VFA (%) | 78.1 | 78.7 |
short-termaging effect, before compaction, the mixtures remained in an oven at 10˚C above the temperature of compaction for two hours. Based on the guidelines of DNIT, its preparation and compaction temperatures were determined.
To perform the dynamic module test, the samples were prepared with 100 mm diameters and 200 mm heights. The samples were subjected to pulses of sinusoidal loads, under strain control mode (by applying axial tension- compression loading) and under tension control mode, at temperatures of −5˚C, 10˚C, 25˚C and 35˚C and load application frequencies of 0.01, 0.05, 0.10,0.50, 1.00, 5.00, 10.00 and 25.00 Hz. To prevent sample damage, the axial deformation did not exceed the value of 75 µε. The tests were performed using a Universal Testing Machine UTM-14, made by IPC Co. Ltd. of Australia. The deformations in the samples were monitored with micros LVDTs (Linear Variable Differential Transducers). Such devices were bonded at four diametrically opposed points of the samples at distances of 25 mm to150 mm from each face.
The Dynamic Modulus (E∗) of AC 50/70 mixtures with SACC and pebbles was obtained under both the strain control mode and tension control mode. In
Taking a reference temperature T0 in a double logarithmic scale, log(αT) is the amount of shift necessary to form a unique curve from different temperatures, known as a master curve. In the present study, the reference temperature T0 is taken as 10˚C. The results present in
where
dimensionless shape parameters. The parameters ωc, k and me are estimated using a minimum squared error fitting procedure. This function presents a spectrum that increases monotonically from zero, at ωR = 0, until its saturation at
In
The comparison between the Dynamic Modulus of the mixtures of AC 50/70 with SACC and with pebbles is shown in
that, in such zones and where sedimentary soil is more plentiful, with the lack of granular material, the sintered aggregate of calcined clay (SACC) can be a good alternative to natural granular aggregate for concrete asphalt mixtures.
We investigated the application of the sintered aggregate of calcined clay (SACC) in mixtures of concrete asphalt for road pavement. We consider CA 50/70 as the binder, and SACC and pebbles as the coarse material. The Dynamic Modulus |E*| of the mixtures was measured under cyclic loading. For high temperatures and low frequencies, the mixture with SACC appears stronger than the mixture with pebbles. This temperature condition is observed in tropical zones around the world. For such regions, where there is a lack of natural granular material, the sintered aggregate of calcined clay can be a good option for use as the coarse material in mixtures of concrete asphalt for road pavement.
The authors acknowledge the National Council for Scientific and Technological Development (CNPq) and the Foundation for Research Support of the State of Amazonas (FAPEAM) for their financial support.
Cleudinei Lopesda Silva,Hidembergue Ordozgoithda Frota,Consuelo Alvesda Frota, (2015) Sintered Calcined Clay as an Alternative Coarse Aggregate for Asphalt Pavement Construction. Open Journal of Civil Engineering,05,281-288. doi: 10.4236/ojce.2015.53028