Cold expansion is an efficient way to improve the fatigue life of an open hole. In this paper, three finite element models have been established to crack growth from an expanded hole is simulated. Expansion and its degree influence are studied using a numerical analysis. Stress intensity factors are determined and used to evaluate the fatigue life. The residual stress field is evaluated using a nonlinear analysis and superposed with the applied stress field in order to estimate fatigue crack growth. Experimental test is conducted under constant loading. The results of this investigation indicate expansion and its degree are a benefit of fatigue life and a good agreement was observed between FEM simulations and experimental results.

The fatigue life improvement of cold expanded fasten holes is attributed to the presence of compressive residual stress induced by cold expansion. The fatigue fracture of fastener holes accounts for 50% - 90% of structural fracture of aircrafts.

Over the last 40 years, because of its simple realization and remarkable enhancement of the fatigue life of holes (usually 3 - 5 times than that of holes without cold expansion), the cold expansion process has been widely used to improve the fatigue life of components with fastener holes [

The cold-expansion, which is developed by the Fatigue Technology Inc. (FTI, 1994), is obtained by using increased pressure to plasticize an annular zone around the hole. The pressure on the surrounding material is realized by interference generated between the drilled plate and the pressuring element, i.e. the mandrel. When the mandrel is removed and the superficial pressure on the hole is erased, a residual stress field is created due to the action of the elastic deformed material on that under plastic condition [

Cold expansion can be achieved in several different ways. A common feature of most methods is to insert an oversized object from one side of the holed plate and remove it from the other side. The main differences in methods relate to the shape of the oversized object and whether a sleeve is used in the hole during cold expansion [2-12]. Compressive residual stress around a hole is very beneficial at resisting fatigue because it reduces the resultant stress at the critical edge of the hole location when the plate undergoes a tensile load [

The experimental part of this work is subdivided into three steps: Tension test, fatigue test and the introduction of residual stresses by cold expansion.

Aluminium alloy 6082-T6 from 8.0 mm thickness was used in this investigation (

Tensile specimens were machined with the dimensions and geometry as specified by the ASTM B557-06 designation. The quasi-static tension test was performed with a head speed displacement of 0.02 mm∙s^{−1}. Tensile strain of specimens was measured with an Instron^{®} extensometer model 2620-601.

The mechanical properties and chemical compositions of this material were presented in Tables 1 and 2, respectively.

Specimens were cut from aluminum alloy plates of 8mm thick plate, with the axis parallel to the rolling direction of the plate. The SENT (Single Edge Notch Tension) specimen configuration used for the experiments is similar to the suggestion in the ASTM E647-95 [E647-95]. The dimensions of the specimen are shown in

A slit of 1mm in width and 15mm in length was machined on one lateral side of the specimen. A pre-crack from the slit tip was introduced by cyclic loading and the total length of the slit and the pre crack was (a_{0} + r where r = d/2). A hole was drilled at the pre-crack tip. The hole was firstly drilled conventionally and then carefully enlarged by a boring bar to a desired radius.

The cold working expansion process was realized by forcing a hard steel ball of 6 mm inside a predrilled hole(the initial diameters of the hole are: 5.9, 5.8 and 5.75 mm, see

The degree of expansion is calculated as follows [

There are 3 DCE applied: 17%, 34% and 43%. Fatigue tests were conducted using a constant amplitude loading. Load ratio, , is 0.57, where σ_{max} and σ_{min} are the maximal and minimal loading. Hydraulic machine INSTRON 8501 was used at a frequency of 30 Hz. During fatigue testing, a video camera with a scale of 0.1 mm was used to determine the crack initiation and propagation in the entry and exit faces of the specimen.

Three finite element analysis was used to simulate the

crack growth in SENT specimen using the commercial code ANSYS. This computer program has the capabilities to simulate, step by step, the rigid ball displacement in the hole axis direction through the plate thickness, thus permitting to establish the variability of the stress field not only in the plane of the plate, but also through the specimen thickness. A two-step nonlinear analysis was performed, in order to simulate the effect of cold expansion of the crack growth numerically, in the first step, The simulation of cold expansion was carried out by changing the position of the rigid ball on the Z-direction, the rigid ball was pushed through the hole and removed from the other side by applying displacement increments on the top nodes of the rigid ball. This phase represents the storing of the residual stress field near the hole. After this operation, there is a relaxation of the tensile strain due to the deformability of the plate under the loading action of cold expansion, on attaining equilibrium and in the second step; this plate was subjected to remote longitudinal stresses to simulate the process of loading during the fatigue testing. Fracture mechanics aims to determine the effect of any cracks on the mechanical behavior of structures. Contributing to this field, we analyzed the influence of residual stresses induced by the cold expansion on the crack growth in 6082-T6 Aluminum alloy.

Superposition techniques are often used when assessing the effects of a known residual stress field on fatigue crack propagation. To estimate crack growth from the equation, some authors [15-18] compute a stress intensity factor which is associated with the initial pre-existing residual stress field (K_{res}). This factor it then superposed upon the stress intensity factor that results from external loading (K_{app}) to give the total resultant stress intensity factor for the maximum and minimum loads:

The stress intensity range is then calculated using:

According to these authors, the stress intensity range is independent on residual stresses and only stress ratio (R) is affected.

Total stress induces a displacement of crack face. Given this displacement value and assuming the fracture mode one, ANSYS calculates the total stress intensity factor with the Irwin theory [

where G is shear modulus, is equal to (3-4n) if plane strain is assumed and to in plane stress, n is Poisson’s ratio, v displacements in local cartesian coordinate system as shown in

According to the Equations (3) and (4), Stress intensity

range is calculated as follows:

Crack growth depends also on the load ratio [20-22]. This effect is introduced by Equation (5). In our case we take a value of load ratio that minimize the effect of crack opening and allows us to use Paris law to evaluate crack growth rate.

Many authors use the superposition technique [23,24]. This use has been criticized by some researchers because it doesn’t take in consideration residual stress relaxation during crack propagation [25-28]. In the present work, this effect won’t be taken in count.

Macro files were implemented to simulate crack propagation, using Paris law, under residual stresses influence; this is not possible to do directly in this simulation tool. Calculation procedure is represented on

a_{final} represents the final value of crack length at witch calculation will be stopped.

As shown in this figure, we used an Ansys command to calculate J-integral. This method has the advantage of keeping the same mesh of the specimen during crack propagation. Stress Intensity Factors, assuming fracture mode one, are calculated using the Equations (12) and (13).

With:

(DCE): DCE = 1.7%, 3.4% and 4.3% applied to the 6 mm hole diameter.

A first observation from the reading of

It is now that the cold expansion process produces a uniform negative residual stress throughout the depth of a hole.

The effect of expansion and the increase of DCE is illustrated in

Five degrees of expansion are applied to a hole of diameter 6 mm. DCE equal to zero correspond to a hole without expansion (fatigue plane). The initial number of cycles, corresponding to the initiation of the crack, is taken equal to 1E5 cycles. This is not true because expansion has also an effect on initiation phase, this result

were confirmed by other researchers [29,30].

The expansion improves fatigue life due to the existence of residual stresses on the side of the hole. This field of stresses tends to decrease the crack growth rate as shown in

The aim of this study is to analyze the effect. By finite element method, we investigated the effect of cold expansion process on the crack growth in aluminum alloy, from experimental and numerical results, we can deduce the following conclusions.

The ability of cold expansion to produce beneficial compressive residual stresses around fastener holes was

numerically investigated in this work. The stress superposition technique was applied to plot stress intensity factors by the finite element in ANSYS. This analysis tool was implemented in order to plot SIF (Stress Intensity Factors) during the crack propagation.

Expansion process was simulated with a nonlinear analysis. Residual stresses were superposed to the applied stress field and the resulting stress intensity factors were calculated for each crack length. Crack propagation phase was considered only as the linear behavior of the studied aluminum alloy.

Simulation results are in good agreement with the experiment’s data. This confrontation demonstrates the benefit that has expansion and its degree DE on crack propagation.

Other works are conducted to see the effect of residual stresses on K_{min}, K_{max} and ΔK separately. The redistribution of the residual stress field during the initiation and the propagation of the crack and the numerical determination of the optimal value of the expansion degree are also under study.