The removal efficiency of heavy metals from offshore muds is enhanced in the presence of generated chlorine gas (Cl 2). The tests showed a high removal efficiency of heavy metals at the anode end of cores after 24 hours of EK application. In the initial tests, high electrokinetic flow potential was achieved; however, high levels of chlorine gas were produced in the high-salinity environments. The process was improved by controlling and maintaining a certain fraction of the chlorine gas (Cl 2) in place. The pH was controlled by the chlorine gas maintained in-situ and transported from the anode to cathode. The transports of four heavy metals were evaluated in this study. The chlorine gas can have two impacts on the transport of metals in the system. One is to oxidize the metal ions to a higher oxidation state and the second is to form chloride complexes, which have higher mobility in the system. Determination of oxidation state and the subsequent metal chloride complex are left for future research.
Electroremediationof heavy metals from muds have been studied by Haroun (2009) [
D.C current, which is determined by voltage gradient, was employed using electrokinetic technology. H+ was produced at the anode (1) and OH– at the cathode (2).
These two equations are fundamental reactions at the electrodes occurring in the electrokinetic cell.
The chlorine gas (Cl2) was produced at the anode, together with O2 in the presence of saline water:
The electrokinetic velocity of a fluid of certain viscosity and dielectric constant through a surface-charged porous medium with zeta or electrokinetic potential (ζ), under an electric potential gradient E, is given by the Helmholtz-Smoluchowski (H-S) equation as follows:
where ve = electrokinetic velocity, Qe= electrokinetic flow rate, A = cross-sectional area, D = dielectric constant, , E = potential difference, and viscosity of the fluid.
The ζ potential in Equation (4) has been shown to vary with the pH and ionic concentrations of the pore fluid, as well as the electric field. Therefore, it is not constant during electrokinetic transport in clay medium (Probstein and Hicks, 1993) [
The apparatus consists of two chambers with the anode and cathode electrodes, D.C power supply, solution tanks, volumetric cylinders with gas measurement devices, peristaltic pumps, pressure measurement devices, and digital pH measurement device (
The pH was continuously maintained at a value less than 10 at the cathode end. By maintaining the pH at less than 10, the process efficiency improved and scaling at the cathode was minimized. The saline water was flushed through the anode chamber by a peristaltic pump. The pH in the anode chamber was measured continuously and remained at less than about 2.5. Throughout the test the chlorine gas was produced at the anode.
In a closed system, the Cl2 gas was not allowed to escape with resulting increase in pressure, whereas in the open system the Cl2 gas was allowed to escape.
The samples were collected from two different contaminated areas in Abu Dhabi, UAE: 1) offshore muds adjacent to refinery—industrial area and 2) offshore muds in Port area.
Mud samples were sieved using a 1-mm sieve and then compressed in a cylinder 3.81 cm in diameter and 30 cm long for seven days under an applied pressure of 30 psi.
Two samples 30 cm in length were treated continuously with D.C current for 24 hours: sample (1) using open system and (2) using closed system. Two other samples were treated for 40 hours (sample No. 3, open system, and sample No. 4, closed system) with two 8- hour interruptions (total treatment time = 24 hours). Concentrations of As, Cr, Cs, and Zn were determined initially and after EK treatment (ICP-MS).
The experimental results are presented in Figures 2 through 17. Figures 2 through 11 show the results of 24 hour treatment, whereas Figures 12 through 17 show the results after EK treatment applied for 40 hours with two 8-hour interruptions (actual treatment time = 24 hours). Application of potential gradient of 3.5 V/cm in the open system resulted in an increased removal efficiency when compared to application of 3.5 V/cm in the closed system. Higher removal efficiency was obtained by taking advantage of Cl2 gas generated at the anode and transported to the cathode in a closed system. Reduced power consumption with higher volumes of produced water was achieved in the closed system.
Figures 12 through 17 displayed results of a second set of tests to illustrate the effect of chlorine gas on removal efficiency.
The continuous application of D.C in closed system gave better results than interrupted application of D.C. Final pH at the cathode was reduced with the aid of transported Cl2 gas.
In the case of tests involving Cl2 gas, in a closed system with a potential gradient of 3.5 V/cm, removal efficiency was higher than in the open system with 3.5 V/cm electric potential. Higher removal efficiency was obtained by using the Cl2 gas generated at the anode and transported to the cathode in a closed system. Reduced power consumption with higher volumes of produced water was achieved in the closed system.
In this study, the continuous application of D.C in closed system gave better results than interrupted application of D.C. Final pH at the cathode was reduced by Cl2 gas. The chlorine gas possibly can have two impacts on the transport of metals in the system. One is to oxidize the metal ions to a higher oxidation state and the second is to form chloride complexes which have higher mobility in the system. In conclusion, it appears that presence of Cl2 gas improves the efficiency of remediation.
The authors gratefully acknowledge the support of The Petroleum Institute, Abu Dhabi, U.A.E., University of Southern California, CA, USA, Lehigh University, PA, USA, and Electropetroleum Inc., PA, USA.