Abdul Raheem K. Abid Ali and Zuheir T. Khulief Al-Tai, “The Effect of Iron Addition on the Dry Sliding Wear and Corrosion Behavior of Cu Al Ni Shape Memory Alloy,” Engineering and Technology Journal, Vol. 28, No. 24, 2010, pp. 6888-6902.

has been cited by the following article:

• TITLE: Corrosion Behavior of Cu-Zn-Ni Shape Memory Alloys

  AUTHORS: S. Sathish, U. S. Mallik, T. N. Raju

  KEYWORDS: Shape Memory Alloys; Shape Memory Effect; Corrosion

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.1 No.2, March 28, 2013

  ABSTRACT: Four shape memory alloys of Cu-Zn-Ni, in the range of 35-55 wt% of Cu, 43-60 wt% Zn and 2-9 wt% Ni, were prepared by ingot metallurgy route in an induction furnace under an inert atmosphere. The shape memory effect was tested by bend test. The alloys were further tested for its corrosion behavior in fresh water, Hank’s solution and sea water. From the results it was observed that the alloys exhibit high corrosion resistance in fresh water when compared to Hank’s solution and sea water. And it was also observed that the alloys exhibit better corrosion resistance in Hank’s solution than in sea water.