Z. L. Wang, X. J. Li, J. Q. Zhu, F. Mo, C. F. Zhao and L. H. Wang, “Dynamic Consolidation of W-Cu Nanocomposites from W-CuO Powder Mixture,” Materials Science and Engineering, Vol. 527, No. 21-22, 2010, pp. 6098-6101. doi:10.1016/j.msea.2010.05.077

has been cited by the following article:

• TITLE: Microstructure Evolution of W-Cu Alloy Wire

  AUTHORS: Fei Shao, Wenge Chen, Hui Zhang, Bingjun Ding

  KEYWORDS: Hot-Swaging; Microstructure; W-Cu Alloy; Wire

  JOURNAL NAME: Materials Sciences and Applications, Vol.3 No.3, March 23, 2012

  ABSTRACT: Microstructure of W-Cu alloy wire before and after hot-swaging was studied in this paper. Results show that a homogeneous microstructure of the W-Cu alloy wire was formed after hot-swaging treatment, and the tungsten particles were embedded in copper phases to form a networking structure; the W-Cu alloy wire has a microstructure of body-centered-cubic tungsten particles and face-centered-cubic copper phase, and did not change after hot-swaging. The intermediate phases have not been found during the process, but the size of the tungsten particles in the copper matrix becomes smaller. After hot-swaging, the treated W-Cu alloy wire has a relative density of 105.1%, and a conductivity of 47.2% IACS, the tensile and bending strength can be as large as 644 and 1600 MPa, respectively.