X. Yang and Z. Wang, “Synthesis of Biphasic Ceramics of Hydroxyapatite and β-Tricalcium Phosphate with Controlled Phase Content and Porosity,” Journal of Materials Chemistry, Vol. 8, No. 10, 1998, pp. 2233-2237. doi:10.1039/a802067a

has been cited by the following article:

• TITLE: Synthesis of Biphasic Calcium Phosphate by Hydrothermal Route and Conversion to Porous Sintered Scaffold

  AUTHORS: Sunarso  , Ahmad Fauzi Mohd Noor, Shah Rizal Kasim, Radzali Othman, Ika Dewi Ana, Kunio Ishikawa

  KEYWORDS: Biphasic; Calcium Phosphate; β-TCP; Hydroxyapatite; Hydrothermal; Porous

  JOURNAL NAME: Journal of Biomaterials and Nanobiotechnology, Vol.4 No.3, July 10, 2013

  ABSTRACT: Biphasic calcium phosphate (BCP) consisting of hydroxyapatite (HA) and β-tricalcium phosphate (β-TCP) was successfully synthesized by new hydrothermal route using β-TCP as precursor. The X-ray diffraction analysis of as-synthesized powder indicated that β-TCP had been transformed into HA phase and amount of HA formed gradually increased with prolonged time. The results revealed that the recent technique may be able to control the composition of the obtained BCP which would influence the bioresorbability. Porous body of BCP was prepared by impregnation of polymeric sponge template with the slurry of the powder followed by sintering. The X-ray diffraction of porous product revealed that the composition of β-TCP increased after sintering indicating that HA had been decomposed. Porous BCP obtained from the recent technique possessed both macro and micropores structure which are useful for rapid tissue formation. Besides, the recent porous fabrication technique yielded porous BCP which preserved the sponge template morphology, enabling it to fabricate porous material with controlled pores structure.